CHARACTERIZATION, MORPHOLOGY AND THERMAL-PROPERTIES OF ETHYLENE PROPYLENE BLOCK COPOLYMERS

Characterization, morphology and thermal properties of commercial ethylene-propylene block copolymers have been studied by C-13 nuclear magnetic resonance (n.m.r.) spectroscopy, differential scanning calorimetry (d.s.c.), dynamic mechanical analysis (d.m.a.) and scanning electron microscopy (SEM). The results obtained show that there exists some ethylene-propylene random copolymer in the block copolymers extractable by n-heptane. The possibility of forming PP-b-PE diblock copolymer is questionable on the basis of the effects of residual propene and the chain-transfer reaction in the sequential copolymerization. A difference in the thermal properties between commercial ethylene-propylene block copolymers and PP/PE blends was noticed, which cannot be used to identify PP-b-PE diblock copolymer. The multiphase structure has been confirmed by d.m.a. and SEM, with ethylene-propylene random copolymer and polyethylene forming the domains in the matrix of polypropylene.

FRACTAL BEHAVIOR OF SPINODAL DECOMPOSITION IN POLYMER BLENDS

Fractal behaviour of ramified domains in the late stage of spinodal phase separation in a binary polymer blend of poly(vinyl acetate) with poly(methyl methacrylate) was investigated by optical microscopic method. In the late stage of the spinodal decomposition, the fractal dimension D is about 1.64. It implies that some anomalous properties of irregular structure probably may be explained by fractal concepts.

THE CRYSTALLIZATION BEHAVIOUR OF BLOCK COPOLYMER/HOMOPOLYMER BLENDS I. INFLUENCE OF NONSPHERICAL MICELLE ON CRYSTALLIZATION BEHAVIOUR IN DILUTE SOLID SOLUTIONS

The effect of micelle on crystallization behaviour of dilute poly(methyl methacrylate-b-tetrahydrofuran) diblock copolymer/tetrahydrofuran homopolymer, dilute poly (ethylene-b-styrene-b-ethylene) triblock copolymer/ethylene homopolymer solutions has been studied. The results show that with the structural teansitions from spherical to nonspherical micelle in the blends, great changes in the nucleation and spherulite morphologies take place.

THE MISCIBILITY AND MORPHOLOGY OF EPOXY-RESIN POLY(ETHYLENE OXIDE) BLENDS

Poly(ethylene oxide) (PEO) was found to be miscible with uncured epoxy resin, diglycidyl ether of bisphenol A (DGEBA), as shown by the existence of a single glass transition temperature (T(g)) in each blend. However, PEO with M(n) = 20 000 was judged to be immiscible with the highly amine-crosslinked epoxy resin (ER). The miscibility and morphology of the ER/PEO blends was remarkably affected by crosslinking. It was observed that phase separation in the ER/PEO blends occurred as the crosslinking progressed. This is considered to be due to the dramatic change in the chemical and physical nature of ER during the crosslinking.

BLENDS OF PHENOLPHTHALEIN POLY(ETHER ETHER KETONE) WITH PHENOXY AND EPOXY-RESIN

The properties of miscible phenolphthalein poly(ether ether ketone)/phenoxy (PEK-C/phenoxy) blends have been measured by dynamic mechanical analysis and tensile testing. The blends were found to have single glass transition temperatures (T(g)) that vary continuously with composition. The tensile moduli exhibit positive deviations from simple additivity. Marked positive deviations were also observed for tensile strength. The tensile strengths of the 90/10 and 75/25 PEK-C/phenoxy blends are higher than those of both the pure components. Embrittlement, or transition from the brittle to the ductile mode of failure, occurs in the composition range of 50-25 wt% PEK-C. These observations suggest that mixing on the segmental level has occurred and that there is enough interaction between the components to decrease its internal mobility significantly. PEK-C was also found to be miscible with the epoxy monomer, diglycidyl ether of bisphenol A (DGEBA), as shown by the existence of a single glass transition temperature (T(g)) within the whole composition range. Miscibility between PEK-C and DGEBA could be considered to be due mainly to entropy. However, PEK-C was judged to be immiscible with the diaminodiphenylmethane-curved epoxy resin (DDM-cured ER). It was observed that the PEK-C/ER blends have two T(g), which remain invariant with composition and are almost the same as those of the pure components, respectively. Scanning electron microscopy showed that the PEK-C/ER blends have a two-phase structure. The different miscibility with PEK-C between DGEBA and the DDM-cured ER is considered to be due to the dramatic change in the chemical and physical nature of ER after curing.