CYCLIC VOLTAMMETRIC AND SPECTROELECTROCHEMICAL STUDIES OF COPPER IN ALKALINE-SOLUTION

The behaviour of the electroplated copper film electrode on tin oxide/glass or glassy carbon surface was studied in potassium hydroxide medium by cyclic voltammetry and in situ transmission spectroelectrochemistry. The results indicate that the electroplated copper film electrode is similar to a copper electrode and cyclic voltammetry with this electrode affords more resolution. The anodic peaks were found to correspond successively to the adsorption of oxygen, the formation of a surface layer of Cu2O, the formation of a surface layer of Cu(OH)2 or CuO and formation of a thick multilayer film of CuO. This is the first time it has been proposed that a surface layer of Cu(OH)2 or CuO is formed from the oxidation of the surface layer of Cu2O. Similarly, a clear interpretation is presented that the cathodic peaks correspond successively to the reduction of CuO to Cu2O, the reductions of Cu2O to Cu and the soluble Cu(II) species to Cu. On the other hand, a shoulder peak related to the chemical transformation of Cu(OH)2 to CuO was first observed.

DIRECT ELECTRON-TRANSFER REACTION OF HEMEPROTEINS PROMOTED BY METHYLENE-BLUE MODIFIED ELECTRODE

The heterogeneous electron transfer reaction of hemeproteins including hemoglobin, myoglobin and cytochrome C at Pt mesh electrode adsorbed methylene blue has been investigated. Thin-layer spectroelectrochemical technique was used for observing the electron transfer processes of three kinds of proteins, and the corresponding electrode rate constants were measured.

FLOW-INJECTION ANALYSIS OF MYOGLOBIN AND HEMOGLOBIN AT TOLUIDINE BLUE CHEMICALLY MODIFIED ELECTRODE

Electrodeposition of the phenothiazine mediator titrant toluidine blue onto a glassy carbon substrate at an appropriate potential was used to construct a toluidine blue chemically modified electrode (CME) exhibiting electrocatalytic reduction for myoglobin and hemoglobin. The CME catalyzed the hemoprotein electroreduction at the reduction potential of the mediator molecule. When the CME as used as a detector for flow injection analysis at a constant applied potential of -0.30 V vs. a saturated calomel electrode, it gave detection limits of 20 and 50 ng (1.2 and 0.78 pmol) injected myoglobin and hemoglobin, respectively, with a dynamic linear concentration range over 2 orders of magnitude. After a brief equilibration period, the CME retained nearly 90% of its initial myoglobin response over 8 hours of continuous exposure to the flow-through system.

Formation of nano-crystalline corrosion products on Zn-Al alloy coating exposed to seawater

Hot dip Zn-Al alloy coating performs better than hot dip galvanized coating and 55% Al-Zn-Si coating as well with regard to general seawater corrosion protection. A characterization of the corrosion products on Zn-Al alloy coating immersed in dynamic aerated seawater has been performed mainly based on transmission electron microscopy (TEM) for morphological analysis and X-ray diffraction (XRD) technique for crystalline phase identification. The XRD and TEM analyses showed that the corrosion products mainly were typical nanometer Zn4CO3(OH)(6).H2O, Zn-5(OH)(8)Cl-2 and Zn6Al2CO3(OH)(16). 4H(2)O microcrystals. This probably is connected to the co-precipitation of Zn2+ and Al3+ ions caused by adsorption. Zn-Al alloy coating being suffered seawater attacks, AI(OH)(3) gel was first produced on the coating surface. Zn and Al hydroxides would co-precipitate and form double-hydroxide when the concentration of adsorbed Zn2+ ions by the newly produced gel exceeded the critical degree of supersaturation of the interphase nucleation. However, because the growth of the crystals was too low to keep in step with the nucleation, a layer of nano-crystalline corrosion products were produced on the surface of the coating finally. (C) 2001 Elsevier Science Ltd. All rights reserved.

The electrochemical reduction reaction of dissolved oxygen on Q235 carbon steel in alkaline solution containing chloride ions

Cyclic voltammetry, electrochemical impedance spectroscopy, and rotating disk electrode voltammetry have been used to study the effect of chloride ions on the dissolved oxygen reduction reaction (ORR) on Q235 carbon steel electrode in a 0.02 M calcium hydroxide (Ca(OH)(2)) solutions imitating the liquid phase in concrete pores. The results indicate that the cathodic process on Q235 carbon steel electrode in oxygen-saturated 0.02 M Ca(OH)(2) with different concentrations of chloride ions contain three reactions except hydrogen evolution: dissolved oxygen reduction, the reduction of Fe(III) to Fe(II), and then the reduction of Fe(II) to Fe. The peak potential of ORR shifts to the positive direction as the chloride ion concentration increases. The oxygen molecule adsorption can be inhibited by the chloride ion adsorption, and the rate of ORR decreases as the concentration of chloride ions increases. The mechanism of ORR is changed from 2e(-) and 4e(-) reactions, occurring simultaneously, to quietly 4e(-) reaction with the increasing chloride ion concentration.

Enhanced activity of an In-Fe2O3/H-ZSM-5 catalyst for NO reduction with methane

Selective reduction of NO by CH4 on an In-Fe2O3/H-ZSM-5 catalyst was investigated in the presence of excess oxygen. Compared with In/H-ZSM-5, the In-Fe2O3/H-ZSM-5 catalyst with high Fe2O3 contents showed higher activity in a wide range of reaction temperatures. It was found that the addition of Fe2O3 yielded a promotion effect on CH4 activation. The influence of water vapor on NO conversion was also investigated. The activity of the In/H-ZSM-5 catalyst has been found to be strongly inhibited by water vapor, while the In-Fe2O3/H-ZSM-5 catalyst remained fairly active in the presence of 3.3% steam. (C) 2000 Elsevier Science B.V. All rights reserved.

Phase transformation in the surface region of zirconia detected by UV Raman spectroscopy

The phase transformation of zirconia from tetragonal to monoclinic is characterized by UV Raman spectroscopy, visible Raman spectroscopy, and XRD. Electronic absorption Of ZrO2 in the UV region makes UV Raman spectroscopy more sensitive at the surface region than XRD or visible Raman spectroscopy. Zirconia changes from the tetragonal phase to the monoclinic phase with calcination temperatures elevated and monoclinic phase is always detected first by UV Raman spectroscopy for the samples calcined at lower temperatures than that by XRD and visible Raman spectroscopy. When the phase of zirconia changes from tetragonal to monoclinic, the slight changes of the phase at very beginning can be detected by UV Raman spectroscopy. UV Raman spectra clearly indicate that the phase transition takes place initially at the surface regions. It is found that the phase change from tetragonal to monoclinic is significantly retarded when amorphous Zr(OH)(4) was agglomerated to bigger particles and the particle agglomeration of amorphous zirconium hydroxide is beneficial to the stabilization of t-ZrO2 phase.

Complete hydrodechlorination of chlorobenzene and its derivatives over supported nickel catalysts under liquid phase conditions

Liquid phase hydrodechlorination of chlorobenzene was studied over Ni/active carbon (Ni/AC), Ni/gamma-Al2O3, Ni/SiO2 and Raney Ni. The complete hydrodechlorination of chlorobenzene was realized at 333-343 K on Ni/AC under hydrogen atmosphere of 1.0 MPa in the presence of alkaline hydroxide. Aryl halides, three chlorotoluenes (o-, m- and p-), three chloroanilines, three chlorobenzotrifluorides, three dichlorobenzenes and two trichlorobenzenes (1,2,3- and 1,2,4-) were also completely hydrodechlorinated under the similar conditions. Chlorobenzene derivatives having either an electron-donating group or an electron-withdrawing group decreased their reactivities with respect to the unsubstituted chlorobenzene.

Morphology transcription process from CMC micelles to inorganogel and its effect on the properties of alumina particle

In this study, a carboxymethyl cellulose (CMC)-mediated sol-gel process was developed to synthesize the alumina hydoxide whiskers. During the process, inexpensive inorganic salts were used as precursors and supercritical drying method was used to extract the water in hydrogel. The influences of CMC on the gel formation and the particle morphology were investigated. The results show that the formation of CMC-aluminium hydroxide organic-inorganic hybridgels led to a morphology transcription process from CMC micelles to aluminium hydroxide gel, as a result, the precursor with whiskerious morphology was obtained.