Surface structure and reaction performances of highly dispersed and supported bimetallic catalysts

Surface structures of Pt-Sn and Pt-Fe bimetallic catalysts have been investigated by means of Mossbauer spectroscopy, Pt-L-III -edge EXAFS and H-2-adsorption. The results showed that the second component, such as Sn or Fe, remained in the oxidative state and dispersed on the gamma-Al2O3 surface after reduction, while Pt was completely reduced to the metallic state and dispersed on either the metal oxide surface or the gamma-Al2O3 surface. By correlating the distribution of Pt species on different surfaces with the reaction and adsorption performances, it is proposed that two kinds of active Pt species existed on the surfaces of both catalysts, named M-1 sites and M-2 sites. M-1 sites are the sites in which Pr directly anchored on the gamma-Al2O3 surface, while M-2 sites are those in which Pt anchored on the metal oxide surface. M-1 sites are favorable for low temperature H-2 adsorption, and responsible for the hydrogenolysis reaction and carbon deposition, while M-2 sites which adsorb more H-2 at higher temperature, are more resistant to the deactivation due to less carbon deposition, and provide major contribution to the dehydrogenation reaction.

Partial oxidation of ethane to syngas over nickel-based catalysts modified by alkali metal oxide and rare earth metal oxide

The catalytic activity, thermal stability and carbon deposition of various modified NiO/gamma-Al2O3 and unmodified NiO/gamma-Al2O3 catalysts were investigated with a flow reactor, XRD, TG and UVRRS analysis. The activity and selectivity of the NiO/gamma-Al2O3 catalyst showed little difference from those of the modified nickel-based catalysts. However, modification with alkali metal oxide (Li, Na, K) and rare earth metal oxide (La, Ce, Y, Sm) can improve the thermal stability of the NiO/gamma-Al2O3 and enhance its ability to suppress carbon deposition during the partial oxidation of ethane (POE). The carbon deposition contains graphite-like species that were detected by UVRRS. The nickel-based catalysts modified by alkali metal oxide and rare earth metal oxide have excellent catalytic activities (C2H6 conversion of similar to 100%, CO selectivity of similar to 94%, 7x 10(4) l/(kg h), 1123 K), good thermal stability and carbon-deposition resistance.

Novel porous metal/ceramic membrane materials

During the past 22 months, the preparation and application of novel porous metal/ceramic membrane materials have been extensively explored in the area of membrane science and catalysis. Thus, new preparation methods and new application concepts in membrane catalysis have been developed.

Sol-gel derived oxides and mixed oxides catalysts with narrow mesoporous distribution

A novel sol-gel process for preparing oxides and mixed oxides sols from precipitation and peptization process is reported in this article. Inorganic salts are used as raw materials in this study. It is found that the amount of acid has great influence on the stability and particle diameter distribution of the precursor sols. Ultrasonic treatment is used to prepare alumina sol at room temperature. The result of Al-27 NMR shows that there exist Al-13(7+) species in the sol. By controlling the sol particles with narrow particle diameter distribution, alumina, titania and silica-alumina (SA) materials with narrow mesoporous distribution are formed by regular packing of sol particles during gelation without using any templates. The results also show that the structure and particle diameter distribution of precursor sol determine the final materials' texture.

Partial oxidation of methane over the perovskite oxides

Ba0.5Sr0.5Co0.8Fe0.2O3-delta and Ba0.5Sr0.5Co0.8Ti0.2O3-delta oxides were synthesized by a combined EDTA-citrate complexing method. The catalytic behavior of these two oxides with the perovskite structure was studied during the reaction of methane oxidation. The pre-treatment with methane has different effect on the catalytic activities of both the oxides. The methane pre-treatment has not resulted in the change of the catalytic activity of BSCFO owing to its excellent reversibility of the perovskite structure resulting from the excellent synergistic interaction between Co and Fe in the oxide. However, the substitution with Ti on Fe-site in the lattice makes the methane pre-treatment have an obvious influence on the activity of the formed BSCTO oxide.

Mixed reforming of heptane to syngas in the Ba0.5Sr0.5Co0.8Fe0.2O3 membrane reactor

Fuel cells are recognized as the most promising new power generation technology, but hydrogen supply is still a problem. In our previous work, we have developed a LiLaNiO/gamma-Al2O3 catalyst, which is excellent not only for partial oxidation of hydrocarbons, but also for steam reforming and autothermal reforming. However, the reaction needs pure oxygen or air as oxidant. We have developed a dense oxygen permeable membrane Ba0.5Sr0.5Co0.8Fe0.2O3 which has an oxygen permeation flux around 11.5 ml/cm(2) min at reaction conditions. Therefore, this work is to combine the oxygen permeable membrane with the catalyst LiLaNiO/gamma-Al2O3 in a membrane reactor for hydrogen production by mixed reforming of heptane. Under optimized reaction conditions, a heptane conversion of 100%, a CO selectivity of 91-93% and a H-2 selectivity of 95-97% have been achieved. (c) 2005 Elsevier B.V. All rights reserved.

Synthesis of zeolite NaA membranes with high permeance under microwave radiation on mesoporous-layer-modified macroporous substrates for gas separation

This article reported the NaA zeolite membranes with high permeance synthesized with microwave heating method under different conditions: (1) on a macroporous substrate in gel, (11) on a mesoporous/macroporous (top-mesoporous-layer-modified macroporous) substrate in gel, and (111) on a mesoporous/macroporous substrate in sol. In general, the H-2 permeance of the NaA membranes by microwave heating in gel was usually at the level of 10(-6) mol s(-1) m(-2) Pa-1, much higher than that by the conventional hydrothermal synthesis. At similar H-2/C3H8 permselectivity. On the substrate modified mesoporous top layer, the H-2 permeance of the NaA membranes by microwave heating in gel or sol was further enhanced, while maintaining comparable H-2/C3H8 permselectivity, due to the prevention of penetration of the reagent into the pores of the macroporous substrate. Meanwhile, the synthesis took less time in sol than in gel on the mesoporous/macroporous substrate. The NaA membranes synthesized in sol had larger permeance than those in gel and underwent transformation in shorter time. The permeation of C3H8 suggested that there existed unwanted intercrystalline pores or defects in the membranes. © 2005 Elsevier B.V. All rights reserved.

Development and application of oxygen permeable membrane in selective oxidation of light alkanes

In this paper, oxygen permeable membrane used in membrane reactor for selective oxidation of alkanes will be discussed in detail. The recent developments for the membrane materials will be presented, and the strategy for the selection of the membrane materials will be outlined. The main applications of oxygen permeable membrane in selective oxidation of light alkanes will be summarized, which includes partial oxidation of methane (POM) to syngas and partial oxidation of heptane (POH) to produce H-2, oxidative coupling of methane (OCM) to C-2, oxidative dehydrogenation of ethane (ODE) to ethylene and oxidative dehydrogenation of propane (ODP) to propylene. Achievements for the membrane material developments and selective oxidation of light alkanes in membrane reactor in our group are highlighted.

In situ high temperature X-ray diffraction studies of mixed ionic and electronic conducting perovskite-type membranes

Phase structure and stability of three typical mixed ionic and electronic conducting perovskite-type membranes, SrCo0.8Fe0.2O3-delta (SCF), Ba0.5Sr0.5Co0.8Fe0.2O3-delta (BSCF) and BaCo0.4Fe0.4Zr0.2O3-delta (BCFZ) were studied by in situ high temperature X-ray diffraction at temperatures from 303 to 1273 K and under different atmospheres (air, 2% O-2 in Ar and pure Ar) at 1173 K. By analyzing their lattice parameters the thermal expansion coefficients (TECs) of BSCF, SCF and BCZF are obtained to be 11.5 x 10(-6) K-1, 17.9 x 10(-6) K-1 and 10.3 x 10(-6) K-1, respectively. A relationship between phase stability and TEC was proposed: the higher is the TEC, the lower is the operation stability of the perovskite materials. (C) 2005 Elsevier B.V. All rights reserved.

Stainless-steel-net-supported zeolite NaA membrane with high permeance and high permselectivity for oxygen over nitrogen

A stainless-steel net is used to support a zeolite NaA membrane synthesized using a 'seeded-growth' method. The zeolite and stainless-steel net are tightly integrated (see Figure), showing large-scale order and high mechanical stability. High oxygen permeance and high permselectivity for O-2 over N-2 (about 7) is demonstrated.

Benzene electro-oxidation in a PEMFC for phenol and electricity cogeneration

In the present investigation, the electrochemically-assisted oxidation of benzene in a H-2-O-2 proton exchange membrane fuel cell (PEMFC) for electricity and phenol cogeneration is studied. Experiments were carried out in a PEMFC electrochemical reactor using Pd black as cathode electrocatalyst at 60 and 80 degrees C, respectively and 1 atm back pressure. Indeed, it was found that the only product detected under the examined experimental conditions was phenol. The online GC product analysis revealed that it is impossible to produce phenol when the fuel cell circuit is open (I = 0) under all the examined experimental conditions. When the fuel cell circuit was closed, however, the phenol yield was found to follow a volcano-type dependence on the cur-rent of the external circuit. It was found that the maximum phenol yield was 0.35% at 100 mA/cm(2) at 80 degrees C. At the same time, the PEMFC performance was also investigated during the phenol generation process. Furthermore, experiments with the rotating ring disc electrode (RRDE) technique showed that the intermediate oxidation product, i.e. H2O2 existed during the oxygen electro-reduction process. The cyclic voltammograms showed that benzene was strongly adsorbed on the Pd surface, leading to a degradation of the PEMFC performance. (c) 2005 Elsevier B.V. All rights reserved.