Structure and properties of samarium overlayer and Sm/Rh surface alloy on Rh(100)

The structure and properties of Sm overlayer and Sm/Rh surface alloy have been investigated with Auger electron spectroscopy (AES), low energy electron diffraction (LEED), X-ray photoelectron spectroscopy (XPS), and temperature programmed desorption spectroscopy (TDS). The growth of Sm on Rh(100) at room temperature (RT) appears following the Stranski-Krastanov growth mode and only the trivalent state Sm is observed from XPS results. Thermal treatment of the Sm film at 900 K leads to the formation of ordered surface alloy which shows the c(5 root2 x root2)R45 degrees and c(2 x 2) LEED patterns. Annealing the Sm film at temperature above 400 K makes the binding energy (B.E.) of Sm 3d(5/2) shift to higher energy by 0.7 eV, which indicates charge transfer from Sm to Rh(100) substrate, causing the increase of CO desorption temperature.

Structure and chemical composition of supported Pt-Sn electrocatalysts for ethanol oxidation

Carbon supported PtSn alloy and PtSnOx particles with nominal Pt:Sn ratios of 3:1 were prepared by a modified polyol method. High resolution transmission electron microscopy (HRTEM) and X-ray microchemical analysis were used to characterize the composition, size, distribution, and morphology of PtSn particles. The particles are predominantly single nanocrystals with diameters in the order of 2.0-3.0 nm. According to the XRD results, the lattice constant of Pt in the PtSn alloy is dilated due to Sn atoms penetrating into the Pt crystalline lattice. While for PtSnOx nanoparticles, the lattice constant of Pt only changed a little. HRTEM micrograph of PtSnOx clearly shows that the change of the spacing of Pt (111) plane is neglectable, meanwhile, SnO2 nanoparticles, characterized with the nominal 0.264 nm spacing of SnO2 (10 1) plane, were found in the vicinity of Pt particles. In contrast, the HRTEM micrograph of PtSn alloy shows that the spacing of Pt (111) plane extends to 0.234 nm from the original 0.226 nm. High resolution energy dispersive X-ray spectroscopy (HR-EDS) analyses show that all investigated particles in the two PtSn catalysts represent uniform Pt/Sn compositions very close to the nominal one. Cyclic voltammograms (CV) in sulfuric acid show that the hydrogen ad/desorption was inhibited on the surface of PtSn alloy compared to that on the surface of the PtSnOx catalyst. PtSnOx catalyst showed higher catalytic activity for ethanol electro-oxidation than PtSn alloy from the results of chronoamperometry (CA) analysis and the performance of direct ethanol fuel cells (DEFCs). It is deduced that the unchanged lattice parameter of Pt in the PtSnOx catalyst is favorable to ethanol adsorption and meanwhile, tin oxide in the vicinity of Pt nanoparticles could offer oxygen species conveniently to remove the CO-like species of ethanolic residues to free Pt active sites. (C) 2005 Elsevier Ltd. All rights reserved.

Structure and impedance of ZrO2 doped with SC2O3 and CeO2

Scandia and ceria doped zirconia samples, with 10 mol% SC2O3 and different content of CeO2, were synthesized and characterized. The XRD results depict that the sintered samples have a cubic phase structure. However, Raman spectra show that besides the main cubic phase, a secondary phase is also present in the sintered samples. The addition of CeO2 can raise the content of the cubic phase, but the minor metastable tetragonal phase (t'-phase) exists even at the CeO2 content as high as 10 mol%. The near-UV Raman spectra indicate that the deformed tetragonal structure predominates at the grain boundary. The addition of CeO2 can reduce the impurity at grain boundary, and no impurity can be found by near-UV Raman spectroscopy at the grain boundary of the samples with high CeO2 content. The impedance measurements show that with the increase of CeO2 content, the impedance of grain boundary decreases and the bulk impedance increases. The low impedance of grain boundary can be attributed to the formation of a clean grain boundary upon CeO2 doping, and the increase of the bulk impedance is due to the blocking effect of the large Ce(IV) ions. (c) 2005 Elsevier B.V All rights reserved.