Stable pulse-compressed acousto-optic Q-switched fiber laser

A novel acousto-optic switch operation by a simple laser-diode pumped acousto-optic, Q-switched, ytterbium-doped, double-clad fiber laser is reported. Stable compressed Q-switched sub-40 ns pulses with a beam quality factor (M-2 = 2) are achieved at the repetition rate of 1-50 kHz. Q-switched pulses of similar to 20 mu J pulse energy and 35 as pulse width are obtained at the repetition rate of 50 kHz. Finally, a reasonable explanation of the novel Q-switched operation is presented. (c) 2007 Optical Society of America.

锯齿形板条抽运结构的热效应数值比较

激光二极管抽运的全固态激光器中,除了激光介质的温度分布和热透镜效应以外,抽运、冷却结构对获得高光束质量、高功率激光输出至关重要。基于热传导方程,在相同的抽运功率和传导冷却边界条件下,对单侧面抽运锯齿形(zigzag)板条、单侧面键合锯齿形板条、部分抽运板条三种不同抽运结构的温度分布、热致应力、温度导致的折射率变化进行了详细的分析,并通过光线追迹方法,比较了光束在锯齿形面内和垂直于锯齿形面内的光程差,由光程差曲线分析了激光束的热透镜效应。对三种抽运结构的端面温度、端面变形和端面变形导致的光程差也进行了对比分

硬边非稳腔平面波导激光器的光束特性

基于衍射理论和坐标变换,采用数值模拟的方法分析了硬边非稳腔平面波导激光器的光束特性,研究了存在非均匀抽运和增益饱和时,输出激光的光束质量.在端面抽运和边缘抽运时,比较了正支和负支非稳腔的输出光束特性.结果表明：利用优化的离轴硬边非稳腔可以得到近衍射极限的输出.在相同的抽运不均匀性情况下,对于边缘抽运和端面抽运,正支非稳腔的光束质量因子M^2分别为3.9和2.3,而相同条件下负支非稳腔的M^2因子为1.8和1.7.

激光二极管阵列的窄线宽、可调谐输出

外腔反馈的激光二极管阵列(LDA)可获得窄线宽、可调谐的光谱输出。外腔由快轴准直镜、准直光学系统和闪耀光栅组成。由于阵列中各发光单元的排列弯曲导致不同波长的光原路返回,引起谱线展宽,在输出光路中加入光谱滤波器,使激光二极管阵列的线宽进一步窄化。这样,激光二极管阵列的输出光谱由自由运转时的2 nm压缩到0.12 nm,在恒定温度23 ℃时,实现了激光在806～818 nm的调谐,调谐范围达12 nm。

Passive Q-switching of short-length Tm3+-doped silica fiber lasers by polycrystalline Cr2+:ZnSe microchips

We demonstrate passive Q-switching of short-length double-clad Tm3+-doped silica fiber lasers near 2 mu m pumped by a laser diode array (LDA) at 790 nm. Polycrystalline Cr2+:ZnSe microchips with thickness from 0.3 to 1 mm are adopted as the Q-switching elements. Pulse duration of 120 ns, pulse energy over 14 mu] and repetition rate of 53 kHz are obtained from a 5-cm long fiber laser. As high as 530 kHz repetition rate is achieved from a 50-cm long fiber laser at similar to 10-W pump power. The performance of the Q-switched fiber lasers as a function of fiber length is also analyzed. (c) 2008 Elsevier B.V. All rights reserved.

Efficient excitations of radially and azimuthally polarized Nd 3+:YAG ceramic microchip laser by use of subwavelength multilayer concentric gratings composed of Nb2O5/SiO2

Cylindrical vector beams were produced from laser diode end-pumped Nd:YAG ceramic microchip laser by use of two types of subwavelength multilayer gratings as the axisymmetric-polarization output couplers respectively. The grating mirrors are composed of high- and low-refractive-index (Nb2O5/SiO2) layers alternately while each layer is shaped into triangle and concentric corrugations. For radially polarized laser output, the beam power reached 610mW with a polarization extinction ratio ( PER) of 61: 1 and a slope efficiency of 68.2%; for azimuthally polarized laser output, the beam power reached 626mW with a PER of 58: 1 and a slope efficiency of 47.6%. In both cases, the laser beams had near-diffraction limited quality. Small differences of beam power, PER and slope efficiency between radially and azimuthally polarized laser outputs were not critical, and could be minimized by further optimized adjustment to laser cavity and the reflectances of respective grating mirrors. The results manifested, by use of the photonic crystal gratings mirrors and end-pumped microchip laser configuration, CVBs can be generated efficiently with high modal symmetry and polarization purity. (C) 2008 Optical Society of America.

掺铒氟（卤）磷碲酸盐玻璃的上转换发光性能研究

研究了掺铒氟（卤）磷碲酸盐玻璃的吸收光谱和上转换荧光光谱，探讨了Er^2＋在氟（卤）磷碲酸盐玻璃中的上转换发光机理．在975nm激光二极管抽运下产生强烈的上转换红光及绿光。且红光的发光强度要远远大于绿光．以PbCl2取代PbF2后，红光的发光强度下降，而绿光却没有明显变化；以ZnCl2取代ZnF2达5mol％时，红光和绿光的发光强度均明显增大．

Infrared-to-visible upconversion emissions in Er3+ doped TeO2-based oxyhalide glasses

The fluorescence and up-conversion spectral properties of Er3+-doped TeO2-ZnO and TeO2-ZnO-PbCl2 glasses suitable for developing optical fiber amplifier and laser have been fabricate and characterized. Strong green (around 527-550 nm) and red (around 661 nm) up-conversion emissions under 977 nm laser diode excitation were investigated, corresponding to H-2(11/2), S-4(3/2), --> I-4(15/2) and F-4(9/2) --> I-4(15/2) transitions of Er3+ ions respectively, have been observed and the involved mechanisms have been explained. The dependence of up-converted fluorescence intensity versus laser power confirm that two-photons contribute to up-conversion of the green-red emissions. The novelty of this kind of optical material has been its ability in resisting devitrification, and its promising optical properties strongly encourage for their further development as the rare-earth doped optical fiber amplifiers and upconversion fiber laser systems.

977nm抽运下掺铒碲酸盐基氧卤玻璃的光谱特性

研究了掺铒TeO2-ZnO-PbCl2碲酸盐基氧卤玻璃在977nm激光二极管抽运下的发光和上转换发光特性，结果发现除红外1．53μm^4I13.2→^4I15/2发光外(荧光半高宽高达69nm)，该玻璃还存在很强的^2H11/2→^4I15/2(527nm)，^4S3/2→^4I15/2(549nm)和^4R9/2→^4I15/2(666nm)可见上转换发光．应用Judd-Ofelt理论计算得到玻璃强度参数Ω1(t=2，4，6)分别为Ω2=5．87×10^20cm^2,Ω4=2．08×10^2-cm^2，

Spectroscopic properties of fluorophosphate glass with high Er(3+)supercript stop concentration

Fluorophosphate glass with 4 mol.% ErF3 content was prepared. The different scanning calorimetry was conducted. Raman spectrum, infrared transmission spectrum, absorption spectrum were measured. Fluorescence spectrum and lifetime of emission around 1.53 mu m were measured under 970 nm laser diode excitation. The metaphosphate content in the composition is limited, but the maximum phonon energy of glass amounts to 1290 cm- 1, and is comparatively high. The full width at half maximum is about 56 nm, and is wider than for most of the materials investigated. The measured lifetime of I-4(13/2) -> I-4(15/2) transition, contributed by the high phonon energy, inefficient interaction of Er3+ ions, and low water content, amounts to no less than 7.36 ms though the Er3+ concentration is high. This work might provide useful information for the development of compact optical devices.

Upconversion emissions in Yb3+-Tm3+-doped tellurite glasses excited at 976 nm

Intense Tm3+ blue upconversion emission has been observed in Tm3+-Yb3+ codoped oxyfluoride tellurite glass under excitation with a diode laser at 976 nm. Three emission bands centered at 475, 650 and 796 nm corresponding to the transitions (1)G(4) -> H-3(6), (1)G(4) -> H-3(4) and F-3(4) -> H-3(6), respectively, simultaneously occur. The dependence of upconversion intensities on Tm3+ ions concentration and excitation power are investigated. For fixed Yb2O3 concentrations of 5.0 mol%, the maximum upconversion intensity was obtained with Tm2O3 concentration of about 0.1 mol%. The blue upconversion luminescence lifetimes of the Tm3+ transitions (1)G(4) -> H-3(6) are measured. The results are evaluated by the possible upconversion mechanisms.

Optical amplification near 1300 nm in bismuth-doped strontium germanate glass

We demonstrate the broadband optical amplification in bismuth-doped strontium germanate glass with 808 nm and 980 nm laser diodes (LDs) as excitation sources. The net optical gain has been obtained within the wavelength region of 1272 to 1348 nm with 808 nm laser diode under 0.97 W power. The maximum gain and gain coefficients are 1.23 and 1.03 cm(-1) at 1315 nm, respectively. The signal increment at 1300 nm is 2.8 times with 980 nm LD, under 3 W power. The differential thermal analysis measurement reveals the good thermal stability of the studied glass. This glass could be suggested as a promising gain medium for broadband optical amplifiers.

Intense infrared luminescence in transparent glass-ceramics containing beta-Ga2O3 : Ni2+ nanocrystals

Transparent glass-ceramics containing beta-Ga2O3:Ni2+ nanocrystals were synthesized and characterized by X-ray diffraction, transmission electron microscopy, and electron energy loss spectroscopy. Intense broad-band luminescence centering at 1200 nm was observed when the sample was excited by a diode laser at 980 nm. The room-temperature fluorescent lifetime was 665 mu s, which is longer than the Ni2+-doped ZnAl2O4 and LiGa5O8 glass-ceramics and is also comparable to the Ni2+-doped LiGa5O8 single crystal. The intense infrared luminescence with long fluorescent lifetime may be ascribed to the high crystal field hold by Ni2+ and the moderate lattice phonon energy of beta-Ga2O3. The excellent optical properties of this novel material indicate that it might be a promising candidate for broad-band amplifiers and room-temperature tunable lasers.

Multicolor upconversion of Er3+/Tm3+/Yb3+ doped oxyfluoride glass ceramics

Er3+/Tm3+/Yb3+ tricloped oxyfluoride glass ceramics was synthesized in a general way. Under 980 nm LD pumping, intense red, green and blue upconversion was obtained. And with those primary colors, multicolor luminescence was observed in oxyfluoride glass ceramics with various dopant concentrations. The red and green upconversion is consistent with F-4(9/2) -> I-4(15/2) and H-2(11/2), S-4(3/2) -> I-4(15/2) transition of Er3+ respectively. While the blue upconversion originates from (1)G(4) -> H-3(6) transition of Tm3+. This is similar to that in Er3+/Yb3+ and/or Tm3+/Yb3+ codoped glass ceramics. However the upconversion of Tm3+ is enhanced by the energy transfer between Er3+ and Tm3+. (c) 2006 Published by Elsevier B.V.