Submicrometre scale single-crystalline gold plates of nanometre thickness: synthesis through a nucleobase process and growth mechanism

Synthesis of submicrometre scale single-crystalline gold plates of nanometre thickness in the presence of nucleobase guanine through chemical reduction of HAuCl4 was investigated. The elemental composition of the as-prepared gold nanoplates was estimated using energy-dispersive x-ray spectroscopy. The as-prepared gold plates were composed of essentially (111) lattice planes, as revealed by both x-ray diffraction (XRD) and transmission electron microscopy (TEM) results. It was found that the molar ratio of HAuCl4 to guanine played a very important role in the formation of gold nanoplates. Gold nanoplates could be produced at a molar ratio of [HAuCl4]/[guanine] = 50: 1 while only smaller gold spherical nanoparticles were obtained at molar ratios of [HAuCl4]/[guanine] <= 20:1. A possible growth mechanism of the as-prepared gold nanoplates is proposed and discussed. The results and conclusion presented in this work may be valuable for our further understanding of the roles of precursor ligands in the control of nanoparticles aggregation states and the preparation of shape-controlled nanoparticles.

Highly uniform and monodisperse beta-NaYF4 : Ln(3+) (Ln = Eu, Tb, Yb/Er, and Yb/Tm) hexagonal microprism crystals: Hydrothermal synthesis and luminescent properties

beta-NaYF4:Ln(3+) (Ln = Eu, Tb, Yb/Er, and Yb/Tm) hexagonal microprisms with remarkably uniform morphology and size have been synthesized via a facile hydrothermal route. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), and photoluminescence (PL) spectra as well as kinetic decays were used to characterize the samples. It is found that sodium citrate as a shape modifier introduced into the reaction system plays a critical role in the shape evolution of the final products. Furthermore, the shape and size of the products can be further manipulated by adjusting the molar ratio of citrate/RE3+ (RE represents the total amount of Y3+ and the doped rare earth elements such as Eu3+, Tb3+, Yb3+/Er3+, or Yb3+/Tm3+). Under the excitation of 397 nm ultraviolet light, NaYF4:xEu(3+) (x = 1.5, 5%) shows the emission lines of Eu3+ corresponding to D-5(0-3) -> F-7(J) (J = 0-4) transitions from 400 to 700 nm (whole visible spectral region) with different intensity, resulting in yellow and red down-conversion (DC) light emissions, respectively.

Monodisperse and core-shell-structured SiO2@YBO3 : Eu3+ spherical particles: Synthesis and characterization

Y0.9Eu0.1BO3 phosphor layers were deposited on monodisperse SiO2 particles of different sizes (300, 570, 900, and 1200 nm) via a sol-gel process, resulting in the formation of core-shell-structured SiO2@Y0.9Eu0.1BO3 particles. X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), photoluminescence (PL), and cathodoluminescence (CL) spectra as well as lifetimes were employed to characterize the resulting composite particles. The results of XRD, FE-SEM, and TEM indicate that the 800 degrees C annealed sample consists of crystalline YBO3 shells and amorphous SiO2 cores, in spherical shape with a narrow size distribution. Under UV (240 nm) and VUV (172 nm) light or electron beam (1-6 kV) excitation, these particles show the characteristic D-5(0)-F-7(1-4) orange-red emission lines of Eu3+ with a quantum yield ranging from 36% (one-layer Y0.9Eu0.1BO3 on SiO2) to 54% (four-layer Y0.9Eu0.1BO3 on SiO2).

Biofunctionalization of CeF3 : Tb3+ nanoparticles

CeF3: Tb3+ nanoparticles (short pillar-like morphology with an average length and width of 11 and 5 nm, respectively) were successfully prepared by a polyol process using diethyleneglycol (DEG) as solvent. After being functionalized with a SiO2-NH2 layer, these CeF3: Tb3+ nanoparticles can be conjugated with biotin molecules (activated by thionyl chloride) and further with avidin. The as-formed CeF3: Tb3+ nanoparticles, CeF3: Tb3+ nanoparticles functionalized with amino groups, biotin conjugated amino-functionalized CeF3: Tb3+ nanoparticles and biotinylated CeF3: Tb3+ nanoparticles bonded with avidin were characterized by x-ray diffraction (XRD), transmission electron microscopy (TEM), Fourier transform infrared (FT-IR), UV/vis absorption spectra and luminescence spectra, respectively. The biofunctionalization of the CeF3: Tb3+ nanoparticles has less effect on their luminescence properties, i.e. they still show strong green emission (from Tb3+, with D-5(4) - F-7(5) at 543 nm as the most prominent group), indicative of the great potential for these CeF3: Tb3+ nanoparticles to be used as biological fluorescence probes.

"Green synthesis" of monodisperse Pt nanoparticles and their catalytic properties

A green synthetic strategy to prepare monodisperse Pt nanoparticles was reported. Aminodextran acted as the reductive and protective agents, and Pt nanoparticles were characterized by UV/vis spectroscopy (UV-vis), Pt nanoparticles were conveniently obtained at one step. transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FT-IR), and X-ray photoelectron spectroscopy (XPS). By changing the initial molar ratio of arninodextran to platinum precursor, Pt nanoparticles with different size were obtained. Amino groups of aminodextran could absorb on Pt nanoparticles surfaces and serve as a very good stabilizer. However, dextran without amino groups could not effectively stabilize Pt nanoparticles and aggregation of Pt nanoparticles were obtained. Catalytic activity of these Pt nanoparticles for the electron-transfer reaction between hexacyanoferrate (III) ions and thiosulfate ions was also studied, and they showed good catalytic efficiency.

Enhanced photoluminescence of Ba2GdNbO6: Eu3+/Dy3+ phosphors by Li+ doping

The Ba2GdNbO6: Eu3+/Dy3+ and Li+-doped Ba2GdNbO6: Eu3+/Dy3+ phosphors were prepared by solid-state reaction process. X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM) and photoluminescence (PL) as well as lifetimes, was utilized to characterize the resulting phosphors. Under the excitation of ultraviolet light, the Ba2GdNbO6: Eu3+/Dy3+ and Li+-doped Ba2GdNbO6: Eu3+/Dy3+ show the characteristic emissions of Eu3+ (D-5(0)-F-7(1,2,3) transitions dominated by D-5(0)-F-7(1) at 593 nm) and Dy3+ (F-4(9/2)-H-6(15/2),(13/2) transitions dominated by F-4(9/2)-H-6(15/2) at 494 nm), respectively. The incorporation of Li+ ions into the Ba2GdNbO6: Eu3+/Dy3+ phosphors has enhanced the PL intensities depending on the doping concentration of Li+, and the highest emission was obtained in Ba2Gd0.9NbO6: 0.10Eu(3+), 0.01Li(+) and Ba2Gd0.95NbO6: 0.05Dy(3+), 0.07Li(+), respectively. An energy level diagram was proposed to explain the luminescence process in the phosphors.

Spontaneous formation of two-dimensional gold networks at the air-water interface and their application in surface-enhanced Raman scattering (SERS)

Two-dimensional (2-D) gold networks were spontaneously formed at the air-water interface after HAuCl4 reacted with fructose at 90 degrees C in a sealed vessel, in a reaction in which fructose acted as both a reducing and a protecting agent. Through fine-tuning of the molar ratio of HAuCl4 to fructose, the thus-formed 2-D gold networks can be changed from a coalesced pattern to an interconnected pattern. In the coalesced pattern, some well-defined single-crystalline gold plates at the micrometer-scale could be seen, while in the interconnected pattern, many sub-micrometer particles and some irregular gold plates instead of well-defined gold plates appeared. It is also found that the 2-D gold networks in the form of an interconnected pattern can be used as substrates for surface-enhanced Raman scattering (SERS) because of the strong localized electromagnetic field produced by the gaps between the neighboring particles in the 2-D gold networks.

An effective hydrothermal route for the synthesis of multiple PDDA-protected noble-metal nanostructures

In this Article, we demonstrate an effective hydrothermal route for the synthesis of multiple PDDA-protected (PDDA = poly(diallyl dimethylammonium) chloride) noble-metal (including silver, platinum, palladium, and gold) nanostructures in the absence of any seeds and surfactants, in which PDDA, an ordinary and water-soluble polyelectrolyte, acts as both a reducing and a stabilizing agent. Under optimal experimental conditions, Ag nanocubes, Pt and Pd nanopolyhedrons, and Au nanoplates can be obtained, which were characterized by transmission electron microscopy, scanning electron microscopy, energy-dispersive spectroscopy, and X-ray diffraction. More importantly, the nanostrucfures synthesized show potential applications in surface-enhanced Raman scattering and electrocatalysis, in which Ag nanocubes and Pt nanopolyhedrons were chosen as the examples, respectively.

Self-assembly of ionic liquids-stabilized Pt nanoparticles into two-dimensional patterned nanostructures at the air-water interface

In this paper, we demonstrate the self-assembly of ionic liquids (ILs)-stabilized Pt nanoparticles into two-dimensional (2D) patterned nanostructures at the air-water interface under ambient conditions. Here, ILs are not used as solvents but as mediators by virtue of their pronounced self-organization ability in synthesis of self-assembled, highly organized hybrid Pt nanostructures. It is also found that the morphologies of the 2D patterned nanostructures are directly connected with the quantities of ILs. Due to the special structures of ILs-stabilized Pt nanoparticles, 2D patterned Pt nanostructures can be formed through the pi-pi stack interactions and hydrogen bonds. The resulting 2D patterned Pt nanostructures exhibit good electrocatalytic activity toward oxygen reduction.

Preparation of novel silver-gold bimetallic nanostructures by seeding with silver nanoplates and application in surface-enhanced Raman scattering

Novel silver-gold bimetallic nanostructures were prepared by seeding with silver nanoplates in the absence of any surfactants. During the synthesis process, it was found that the frameworks of silver nanoplates were normally kept though the basal plane of silver nanoplates became rugged. The real morphology of these nanostructures depended on the molar ratio of gold ions to the seed particles. When the molar ratio of gold ions to silver atoms increased from 0.5 to 4, porous or branched silver-gold bimetallic nanostructures could be made. The growth mechanism was qualitatively discussed based on template-engaged replacement reactions and seed-mediated deposition reactions. Due to the unusual structures, they exhibited interesting optical properties. Moreover, they were shown to be an active substrate for surface-enhanced Raman scattering measurements.

Fabrication and characterization of SERS-active silver clusters on glassy carbon

In this article, a novel technique for the fabrication of surface enhanced Raman scattering (SERS) active silver clusters on glassy carbon (GC) has been proposed. It was found that silver clusters could be formed on a layer of positively charged poly(diallyldimethylammonium) (PDDA) anchored to a carbon surface by 4-aminobenzoic acid when a drop containing silver nanoparticles was deposited on it. The characteristics of the obtained silver clusters have been investigated by atomic force microscopy (AFM), SERS and an SERS-based Raman mapping technique in the form of line scanning. The AFM image shows that the silver clusters consist of several silver nanoparticles and the size of the clusters is in the range 80-100 nm. The SERS spectra of different concentrations of rhodamine 6G (R6G) on the silver clusters were obtained and compared with those from a silver colloid. The apparent enhancement factor (AEF) was estimated to be as large as 3.1 x 10(4) relative to silver colloid, which might have resulted from the presence of 'hot-spots' at the silver clusters, providing a highly localized electromagnetic field for the large enhancement of the SERS spectra of R6G. The minimum electromagnetic enhancement factor (EEF) is estimated to be 5.4 x 10(7) by comparison with the SERS spectra of R6G on the silver clusters and on the bare GC surface.

Cathodic electrochemiluminescence in aqueous solutions at bismuth electrodes

The high hydrogen evolution overpotential of a bismuth electrode makes it a powerful electrode for cathodic electro-chemiluminescence studies in aqueous solutions.

EDTA-controlled one-pot preparation of novel shaped gold microcrystals and their application in surface-enhanced Raman scattering

We report a one-pot preparation method for a series of novel shaped gold microcrystals by simply mixing HAuCl4 with disodium salt of ethylenediaminetetraacetic acid (Na(2)EDTA). Under the different reaction temperatures, spinous structures, multipod microspheres, and rough surfaced microspheres were obtained. These microcrystals exhibit high surface-enhanced Raman scattering (SERS) activity.

Template-free fabrication of hexagonal ZnO microprism with an interior space

Well-faceted hexagonal ZnO microprisms with regular interior space have been successfully prepared by a template-free hydrothermal synthetic route. The morphologies of the products depend on the experimental conditions such as the solvent, the concentration of ammonia aqueous solution, and the reaction temperature. Through manipulation of the aging time, the as-prepared ZnO can be controlled as a monodispersed hexagonal twinning solid or as hollow microprisms. Moreover, the evolution process of the hollow ZnO nanoarchitecture after reaction for 2, 6, 12, and 24 h has been investigated by field emission scanning electron microscopy (FE-SEM) and transmission electron microscopy (TEM). A possible growth mechanism has also been proposed and discussed. Furthermore, the photoluminescence (PL) measurement exhibits the unique emitting characteristic of hollow ZnO nanostructures.

Bifunctional magnetic-optical nanocomposites: Grafting lanthanide complex onto core-shell magnetic silica nanoarchitecture

Anew class of bifunctional architecture combining the useful functions of superparamagnetism and terbium complex luminescence into one material has been prepared via two main steps by a modified Stober method and the layer-by-layer (LbL) assembly technique. The obtained bifunctional nanocomposites exhibit superparamagnetic behavior, high fluorescence intensity, and color purity. The architecture has been characterized by field-emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), UV-vis absorption and emission spectroscopy, X-ray diffraction, and superconducting quantum interference device (SQUID) magnetometry.