Morphology evolutions of organically modified montmorillonite/polyamide 12 nanocomposites

Organically modified montmorillonites (OMMTs) by octadecylammonium chloride with two adsorption levels were dispersed in polyamide 12 (PA12) matrices with two molecular weights for different melt mixing times in order to investigate morphology evolutions and factors influencing fabrication of PA12 nanocomposites. Different adsorption levels of the modifier in the OMMTs provide different environments for diffusion of polymer chains and different attractions between MMT layers. Wide-angle X-ray diffraction (WAXD), transmission electron microscope (TEM) and gas permeability were used to characterize morphologies of the nanocomposites. Both OMMTs can be exfoliated in the PA12 matrix with higher molecular weight, but only OMMT with lower adsorption level can be exfoliated in the PA12 matrix with lower molecular weight. It was attributed to the differences in the levels of shear stress and molecular diffusion in the nanocomposites. The exfoliation of OMMT platelets results from a combination of molecular diffusion and shear. After intercalation of PA12 into interlayer of OMMT in the initial period of mixing, further dispersion of OMMTs in PA12 matrices is controlled by a slippage process of MMT layers during fabricating PA12 nanocomposites with exfoliated structure.

Chemical effects of cationic surfactant and anionic surfactant used in organically modified montmorillonites on degradation and fire retardancy of polyamide 12 nanocomposites

Three kinds of organically modified Na+-montmorillonites (OMMTs), including two kinds of octadecylammonium modified montmorillonite with different contents of octadecylammonium and a kind of sodium dodecylsulfonate (SDSo) modified montmorillonite, were used to prepare polyamide 12 (PA12)/OMMT nanocomposites. Effects of the modifiers on degradation and fire retardancy of PA12/OMMT nanocomposites were investigated. Acid sites formed in cationic surfactant modified MMT via Hoffman decomposition could accelerate degradation of PA12 at high temperature. However, catalytic effect of the acid sites on carbonization of the degradation products promoted char barrier formation, which reduced heat release rate (HRR). Higher content of cationic surfactant in OMMT is beneficial to fire retardancy of PA12 nanocomposites and the dispersion states of OMMT have assistant effects. In contrast, Na+-montmorillonite (Na-MMT) and anionic surfactant modified MMT (a-MMT) could not form acid sites on the MMT layers; in this case, fire retardancy of PA12/Na-MMT appears to have no improvement and PA12/a-MMT appears to have limited improvement.

Crystal structures of EtEDTB center dot 1.4C(2)H(5)OH center dot 5H(2)O and H4EtEDTB(ClO4)(4)center dot C2H5OH (EtEDTB=N, N, N ', N '-tetrakis[2-(1-ethylbenzimidazolyl)methyl]-1,2-ethanediamine)

The crystal structures of EtEDTB.1.4C(2)H(5)OH.5H(2)O 1 and H4EtEDTB(ClO4)(4).C2H5OH 2 (EtEDTB = N, N,N',N'-tetrakis[2-(1-ethylbenzimidazolyl)methyl]-1,2-ethanediamine) have been determined by single-crystal X-ray diffraction method. Compound 1 crystallizes in the space group P(1) over bar with a = 11.489(2), b = 11.866(3), c = 12.002(3) Angstrom, alpha = 97.47(2), beta = 114.564(13), gamma = 114.11(2)degrees, V = 1266.6(5) Angstrom(3), Z = 1, M-r = 847.48, D-c = 1.111 g/cm(3), F(000) = 456 and mu(MoKalpha) = 0.076 mm(-1). A total of 5207 reflections were measured for 1, of which 4323 were independent. The structure of 1 was solved by direct methods and refined by full-matrix least-squares technique to the final R = 0.0706 and wR = 0.1802 for 1318 observed reflections with I > 2sigma(I). In the structure of 1, centrosymmetric EtEDTB molecules are linked by hydrogen bonds through water and ethanol to form 2-dimensional network. Compound 2 crystallizes in the space group C2/c with a = 24.260(5), b = 13.040(3), c = 17.680(4) Angstrom, beta = 97.50(3)degrees, V = 5545.2(2) Angstrom(3), Z = 4, M-r = 1140.80, D-c = 1.366 g/cm(3), F(000) = 2384 and mu(MoKalpha) = 0.289 mm(-1).

Kinetics of atomic force microscope-based scanned probe oxidation on an octadecylated silicon(111) surface

Atomic force microscope (AFM)-based scanned probe oxidation (SPO) nanolithography has been carried out on an octadecyl-terminated Si(111) surface to create dot-array patterns under ambient conditions in contact mode. The kinetics investigations indicate that this SPO process involves three stages. Within the steadily growing stage, the height of oxide dots increases logarithmically with pulse duration and linearly with pulse voltage. The lateral size of oxide dots tends to vary in a similar way. Our experiments show that a direct-log kinetic model is more applicable than a power-of-time law model for the SPO process on an alkylated silicon in demonstrating the dependence of oxide thickness on voltage exposure time within a relatively wide range. In contrast with the SPO on the octodecysilated SiO2/silicon surface, this process can be realized by a lower voltage with a shorter exposure time, which will be of great benefit to the fabrication of integrated nanometer-sized electronic devices on silicon-based substrates. This study demonstrates that the alkylated silicon is a new promising substrate material for silicon-based nanolithography.

Scanned probe oxidation on an octadecyl-terminated silicon (111) surface with an atomic force microscope: kinetic investigations in line patterning

Scanned probe oxidation (SPO) nanolithography has been performed with an atomic force microscope (AFM) on an octadecyl-terminated silicon (111) surface to create protuberant oxide line patterns under ambient conditions in contact mode. The kinetic investigations of this SPO process indicate that the oxide line height increases linearly with applied voltage and decreases logarithmically with writing, speed. The oxide line width also tends to vary with the same law. The ambient humidity and the AFM tip state can remarkably influence this process, too. As compared with traditional octadecylsilated SiO2/Si substrate, such a substrate can guarantee the SPO with an obviously lowered voltage and a greatly increased writing speed. This study demonstrates that such alkylated silicon is a promising silicon-based substrate material for SPO nanolithography.

Direct patterning of negative nanostructures on self-assembled monolayers of 16-mercaptohexadecanoic acid on Au(111) substrate via dip-pen nanolithography

Both bare and self-assembled monolayer (SAM) protected gold substrate could be etched by allyl bromide according to atomic force microscopy (AFM), x-ray photoelectron spectroscopy (XPS) and inductively coupled plasma mass spectrometric (ICPMS) analysis results. With this allyl bromide ink material, negative nanopatterns could be fabricated directly by dip-pen nanolithography (DPN) on SAMs of 16-mercaptohexadecanoic acid (MHA) on Au(111) substrate. A tip-promoted etching mechanism was proposed where the gold-reactive ink could penetrate the MHA resist film through tip-induced defects resulting in local corrosive removal of the gold substrate. The fabrication mechanism was also confirmed by electrochemical characterization, energy dispersive spectroscopy (EDS) analysis and fabrication of positive nanopatterns via a used DPN tip.

Surface-appropriate lipophobicity - Application in isobutene oligomerization over Teflon-modified silica-supported 12-silicotungstic acid

A series of silica-supported 12-silicotungstic acid catalysts (H4SiW12O40, abbreviated as HSiW), modified with various loadings of Teflon (HSiW/SiO2-Teflon), were prepared by an impregnation method. The surface properties of the catalysts were studied by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), BET, infrared (IR) spectroscopy, NH3-TPD and the Drop Shape Analysis (DSA). SEM results combined with energy-dispersive X-ray (EDX) measurements of HSiW/SiO2-Teflon revealed that F-compound (Teflon) is effectively coated on the catalyst surface. The contact angles for water and oil of 50 wt% HSiW/SiO2 and HSiW/SiO2-Teflon indicate that HSiW/SiO2-Teflon catalyst enhances not only the surface hydrophobicity but also the surface lipophobicity by means of the addition of Teflon. Silica-supported 12-silicotungstic acid modified with Teflon exhibits higher C-8(=) selectivity and longer lifetime than that of silica-supported 12-silicotungstic acid in isobutene oligomerization. Thus, surface-appropriate lipophobicity of catalysts may be effective for decreasing the interaction between coke precursors and the catalyst surface and for removing deposited coke more easily.

Diluting thiol-derivatized oligonucleotide monolayers on Au(111) by mercaptohexanol replacement reaction

Surface replacement reaction of thiol-derivatized, single-stranded oligonucleotide (HS-ssDNA) by mercaptohexanol (MCH) is investigated in order to reduce surface density of the HS-ssDNA adsorbed to Au(111) surface. Cyclic voltammograms (CVs) and scanning tunneling microscopy (STM) are employed to assess the composition and state of these mixed monolayers. It is found that each CV of mixed self-assembled monolayers (SAMs) only shows a single reductive desorption peak, which suggests that the resulted, mixed SAMs do not form discernable phase-separated domains. The peak potential gradually shifts to negative direction and the peak area increases step by step over the whole replacement process. By analyzing these peak areas, it is concluded that two MCH molecules will replace one HS-ssDNA molecule and relative coverage can also be estimated as a function of exposing time. The possible mechanism of the replacement reaction is also proposed. The DNA surface density exponentially reduces with the exposing time increasing, in other words, the replacement reaction is very fast in the first several hours and then gradually slows down. Moreover, the morphological change in the process is also followed by STM.

Reactive blending of modified polypropylene and polyamide 12: Effects of compatibilizer content on crystallization and blend morphology

The crystallization behavior and morphology of nonreactive and reactive melt-mixed blends of polypropylene (PP) and polyamide (PA12; as the dispersed phase) were investigated. It Was found that the crystallization behavior and the size of the PA12 particles were dependent on the content of the compatibilizer (maleic anhydride-modified polypropylene) because an in situ reaction occurred between the maleic anhydride groups of the compatibilizer and the amide end groups of PA12. When the amount of compatibilizer was more than 4%, the PA12 did not crystallize at temperatures typical for bulk crystallization. These finely dispersed PA12 particles crystallized co-incidently with the 1313 phase. The changes in domain size with compatibilizer content were consistent with Wu's theory. These investigations showed that crystallization of the dispersed phase Could not be explained solely by the size of the dispersion. The interfacial tension between the polymeric components in the blends may yield information on the fractionation of crystallization.

3{1-[2-(-3-羟基-1-甲基-2-亚丁烯氨基)-苯亚氨基]-乙基}4-甲硫基-2,4-戊二烯-2-醇的不对称Schiff碱镍(Ⅱ)配合物的合成、结构和性质

由 5-(2-乙酰基-1-甲硫基-3-羰基-亚丁基)-丙二酸亚异丙酯 (1)与邻苯二胺及乙酸镍()经一步反应合成了3{1-[2-( -3-羟基-1-甲基-2-亚丁烯氨基)-苯亚氨基 ]-乙基} 4-甲硫基-2,4-戊二烯-2-醇(3)的不对称四齿 Schiff碱镍()配合物(2),X射线衍射结果表明,配合物 2属单斜晶系,P21/C空间群.a=1.1476(2)nm,b=1.1782(2)nm,c=1.4810(3)nm;β=111.73(2)°,V=1.8602(7)nm3,Z=4,Rf=0.0535.电化学(循环伏安)测定结果表明,该配合物在测定条件下(阳极峰电位为1.1)发生了不可逆的氧化-还原反应.

镧六方铁氧体Ba_(1-x)La_xFe_(12)O_(19)的电磁性能与吸波特性

研究了掺稀土六方铁氧体Ba1-xLaxFe12O19的合成条件,测试了其结构、形貌、电磁性能与吸波特性.结果表明,稀土离子La3+的加入,降低了钡铁氧体的磁化强度、矫顽力和顽磁性,其磁特性接近软磁铁氧体材料;在1.65～2.95GHz的频率范围内,具有良好的吸波性能.

Photochromic behavior and luminescent properties of novel hybrid organic-inorganic film doped with Preyssler's heteropoly acid H-12[EuP5W30O110] and polyvinylpyrrolidone

A novel hybrid photochromic composite film composed of Preyssler's heteropoly acid H-12[EuP5W30O110] (EuP5W30) and polyvinylpyrrolidone (PVP) was prepared by dip-coating method. Atomic force microscopy (AFM) was used to investigate the surface topography. The change of characteristic peak in the infrared spectra (IR) was investigated. The TG curve showed three steps of weight loss and approximately revealed the composition of the hybrid film. Ultraviolet-visible adsorption spectra (UV-VIS) and electron resonance spectrum (ESR) were used to investigate the photochromic behavior and mechanism of hybrid film. The photoluminescent behavior of the film at room temperature was investigated to show the characteristic Eu3+ emission pattern of D-5(o)-F-7(J). The occurrence of photoluminescent activity confirms the potential for creating luminescent thin film with polyoxometalates (POMs).

Effect of alkyl group length on the conductivity in the 2,3,7,8,12,13,17,18-octakis(alkyl-thio)tetraazaporphyrins and redox properties of the metallooctakis(hexyl-thio)tetraazaporphyrins

A series of 2,3,7,8,12,13,17,18-octakis(alkyl-thio)tetraazaporphyrins (H(2)OATTAP) with different alkyl chain lengths have been synthesized. Cyclic voltammetry and differential pulse voltammetry have been used to investigate the effect of the controlled lengths of the eight peripheral thioether tails on the redox behavior of the molecules. The electrochemical reduction of octakis(hexyl-thio)tetraazaporphyrins, MOHTTAP (where M = Cu, Ni), was studied in 1,2-dichloroethane at a platinum electrode. The Cu derivative was oxidized in one single-electron-transfer step to yield a pi-cation radical and reduced in three single-electron-transfer steps to yield a pi-anion radical, dianion and trianion, respectively. For the Ni derivative, electron transfer reactions involving both the central metal atom and the macrocyclic ring were observed. Electron transfer pathways are proposed based upon voltammetric and in situ spectroelectrochemical results.

Hydrothermal synthesis and structure of [Ni(en)(2)V6O14](n)

A new complex [Ni (en)(2)V6O14](n) was hydrothermally synthesized and characterized by 2-dimensional vanadium oxide framework pillared by Ni(en)(2)group. Single crystal X-ray analysis indicates that this compound crystallizes in monoclinic system, space group P2(1)/c with a=0. 892 17(18) nm, b = 1. 711 1(3) nm, c=0. 662 73(13) nm, beta=111. 58(3)degrees, V=0.940 8(3) nm(3), Z=2, D-c=2.501 g/cm(3), R=0. 042 3, omegaR=0. 060 9, S=1. 006.