Preparation of Y1.84La0.16O3 nanopowders by oxalate co-precipitation method

Nanopowder of Y(1.84)mLa(0.16)O(3) was prepared by oxalate co-precipitation method. The powder was characterized by TG-DTA, XRD and TEM. The results show that the precursor is Re-2 (NO3)(2) (C2O4)(2)center dot 2H(2)O (Re=Y, La), and the Y1.84La0.16O3 nanopowders produced by calcining the precursor at 1000 degrees C for 4 h are 20 similar to 40 nm spherical particles and well dispersed. The powders were with high sintering activity and could be fabricated to transparent ceramic without additive at 1450 similar to 1550 degrees C in H-2 atmosphere for 3 hours. The total transmission of the transparent ceramic could reach 80%.

Precipitation of Ge nanoparticles from GeO2 glasses in transmission electron microscope

We show, using spatially resolved energy loss spectroscopy in a transmission electron microscopy (TEM), that GeO2 and GeO2-SiO2 glasses are extremely sensitive to high energy electrons. Ge nanoparticles can be precipitated in GeO2 glasses efficiently by the high-energy electron beam of a TEM. This is relevant to TEM characterization of luminescent Ge nanoparticles in silicate glasses, which may produce artificial results. (C) 2005 American Institute of Physics.