Solution combustion synthesis, structure and luminescence of Y3Al5O12 : Tb3+ phosphors

The synthesis and optical properties of Y3Al5O12:Tb3+ phosphors are reported in this paper. Y3Al5O12:Tb3+ phosphors were synthesized by a facile solution combustion method. Citric acid traps the constituent cations and also acts as a fuel. Y3Al5O12 (YAG) phase can crystallize through sintering at 900 degrees C for 2 h, and there were no intermediate phases such as YAlO3 (YAP) and Y4Al2O9 (YAM) in the sintering process. The excitation spectra of crystalline Y3Al5O12:Tb3+ are different from that of amorphous one due to the crystal field effect. The emission spectra mainly show D-5(4) -> F-7(6) transition under UV excitation. The higher concentration quenching in Y3Al5O12:Tb3+ nanophosphors may be due to the confinement effect on resonant energy transfer of nanocrystalline. It is also indicated that the solution combustion synthesis method provides a good distribution of Tb3+ activators in Y3Al5O12 host. (c) 2005 Published by Elsevier B.V.

Synthesis and characterization of room-temperature ferromagnetism in Fe- and Ni-co-doped In2O3

Observation of room-temperature ferromagnetisin in Fe- and Ni-co-doped In2O3 samples (In0.9Fe0.1-xNix)(2)O-3 (0 <= x <= 0.1) prepared by citric acid sol-gel auto-igniting method is reported. All of the samples with intermediate x values are ferromagnetic at roomtemperature. The highest saturation magnetization (0.453 mu B/Fe + Ni ions) moment is reached in the sample with x = 0.04. The highest solubility of Fe and Ni ions in the In2O3 lattice is around 10 and 4 at%, respectively. The 10 at% Fe-doped sample is found to be weakly ferromagnetic, while the 10at% Ni-doped sample is paramagnetic. Extensive structure including Extended X-ray absorption fine structure (EXAFS), magnetic and magneto-transport including Hall effects studies on the samples indicate the observed ferromagnetism is intrinsic rather than from the secondary impurity phases. (c) 2007 Elsevier Ltd. All rights reserved.

Effects of several organic acids on the feeding behavior of Tilapia nilotica

Automatic recording of the frequency of feeding 'bites' was used to evaluate the effects of several organic acids (citric, metacectonic, lactic, acetic, and oxalic) on the stimulatory feeding behavior of Tilapia nilotica . Some of these acids are added to food stocks to retard spoilage. The results showed that citric acid at a concentration of 10(-2) to 10(-6) m, metacetonic acid at 10(-4) to 10(-6) m, and lactic acid at 10(-2) to 10(-5) m stimulated feeding. Fish tended to avoid metacetonic acid at 10(-3) m and acetic acid at 10(-3) m. Acetic acid at 10(-5) m and oxalic acid at 10(-6) m had no significant effects on fish feeding.

低分子有机酸对辣椒生长发育及叶片活性氧代谢的影响

采用盆栽试验与室内分析相结合的方法,研究了6种低分子有机酸和一种有机酸盐对辣椒生长发育和叶片活性氧代谢的影响。结果表明:柠檬酸、乙酰丙酸和有机酸钾处理不仅可显著提高辣椒根系干质量,增加辣椒vC含量,而且提高了辣椒的产量。甲酸、柠檬酸、乙酰丙酸和有机酸钾处理使根系活力比对照分别提高83%、93.8%、96.75%和99.5%。柠檬酸、乙酰丙酸和有机酸钾处理提高了辣椒叶片的SOD和POD活性,降低了膜脂过氧化产物MDA含量,延缓了叶片衰老。但是低分子有机酸处理对CAT活性的影响较小。

有机酸对茄子生长发育及产量的影响

采用盆栽试验,研究了2种含钾土壤条件下不同有机酸对茄子产量和生长发育的影响。结果表明:通过叶面喷施有机酸可提高茄子单果重,改善植株的生长发育状况。其中,有机酸钾、甲酸、柠檬酸、乙酰丙酸与对照之间有显著差异;高钾土壤高于低钾土壤产量,且差异显著。有机酸的增产效果依次为有机酸钾>甲酸>柠檬酸>乙酰丙酸>草酸>丙酸>乙酸。

Multiform oxide optical materials via the versatile Pechini-type sol-gel process: Synthesis and characteristics

This feature article highlights work from the authors' laboratories on the various kinds of oxide optical materials, mainly luminescence and pigment materials with different forms (powder, core-shell structures, thin film and patterning) prepared by the Pechini-type sol-gel (PSG) process. The PSG process, which uses the common metal salts (nitrates, acetates, chlorides, etc.) as precursors and citric acid (CA) as chelating ligands of metal ions and polyhydroxy alcohol (such as ethylene glycol or poly ethylene glycol) as a cross-linking agent to form a polymeric resin on molecular level, reduces segregation of particular metal ions and ensures compositional homogeneity. This process can overcome most of the difficulties and disadvantages that frequently occur in the alkoxides based sol-gel process.

Hydrothermal Synthesis and Luminescent Properties of Novel Ordered Sphere CePO4 Hierarchical Architectures

The ordered-sphere CePO4 hierarchical architectures have been successfully synthesized by a simple hydrothermal method through the controlled growth of the CePO4 nanorods and self-assemble hierarchical structure under various reaction conditions. The evolution of the morphology of the samples has been investigated in detail. It was found that the coexistence of citric acid and cetaltrimethylammonium bromide in the reaction system plays an important role in the formation of the spherical CePO4 hierarchical architectures. A possible mechanism of the formation and growth of the hierarchical structure was suggested according to the experimental results and analysis. The effects of the reaction time as well as the variation of the morphologies on the luminescent properties of the products were also studied.

Synthesis and structural characterization of new tungsten(VI) complexes with polycarboxylate ligands

The reactions of (NH4)(2)WS4 and three polycarboxylate ligands {including nitrilotriacetate (nta(3-)), citrate (Hcit(3-)) and ethylenediaminetetra acetate (EDTA(4-))} in H2O/EtOH at ambient temperature have resulted in three new trioxotungsten (VI) complexes, K-3[WO3(nta)]center dot H2O 1, (NH4)(4)[WO3(cit)]center dot 2 H2O 2 and K-2(NH4)(2)[W2O6(EDTA)]center dot 4H(2)O 3, respectively. These three complexes have been characterized by IR, XPS, TGA-DTA, H-1 and C-13 NMR spectroscopy. And their structures have been determined by X-ray crystallographic studies, which confirm that I and 2 are mononuclear compounds and 3 is a binuclear compound. Each tungsten atom in 1-3 is coordinated to three unshared oxygen atoms, which adopt fac stereochemistry, while the remaining fac positions are occupied by three atoms from the ligands. The electrochemical properties of 2 and 3 have been investigated.

Rapid synthesis of Mn0.65Zn0.35Fe2O4/SiO2 homogeneous nanocomposites by modified sol-gel auto-combustion method

MnZn-ferrite/SiO2 nanocomposites with different silica content were successfully fabricated by a novel modified sol-gel auto-combustion method using citric acid as a chelating agent and tetraethyl orthosilicate (TEOS) as the source of silica matrix. The auto-combustion nature of the dried gel was studied by X-ray diffraction (XRD), Infrared spectra (IR), thermogravimetry (TG) and differential thermal analysis (DTA). Transmission electron microscope (TEM) observation shows that the MnZn-ferrite particles are homogeneously dispersed in silica matrix after auto-combustion of the dried gels. The magnetic properties vary with the silica content. The transition from the ferromagnetic to paramagnetic state is observed by Mossbauer spectra measurement with the increasing silica content. Vibrating sample magnetometer (VSM) shows that the magnetic properties of Mn0.65Zn0.35Fe2O4/SiO2 nanocomposites strongly depend on the silica content.

Comparative study on the luminescent properties of Y3Al5O12 : RE3+ (RE : Eu, Dy) phosphors synthesized by three methods

By using metal nitrates and oxides as the starting materials, Y3Al5O12 (YAG) and YAG: RE3+ (RE: Eu, Dy) powder phosphors were prepared by solid state (SS), coprecipitation (CP) and citrate-gel (CG) methods, respectively. The resulting YAG based phosphors were characterized by XRD and photoluminescent excitation and emission spectra as well as lifetimes. The purified crystalline phases of YAG were obtained at 800degreesC (CG) and 900degreesC (CP and SS), respectively. Great differences were observed for the excitation and emission spectra of Eu3+ and Dy3+ between crystalline and amorphous states of YAG, and their emission intensities increased with increasing the annealing temperature. At an identical annealing temperature and doping concentration, the Eu3+ and Dy3+ showed the strongest and weakest emission intensity in CP- and CG-derived YAG phosphors, respectively. The poor emission intensity for CG-derived phosphors is mainly caused by the contamination organic impurities from citric acid in the starting materials. Furthermore, the lifetimes for the samples derived from CG and CP routes are shorter than those derived from the SS route.

Citrate-gel synthesis and luminescent properties of alpha-Zn-3(PO4)(2) doped with Eu3+

By using inorganic salts as raw materials and citric acid as complexing agent, alpha-Zn-3(PO4)(2) and Eu3+ doped alpha-Zn-3(PO4)(2) phosphor powders were prepared by a citrate-gel process. X-ray diffraction, (XRD), TG - DTA, FT - IR and luminescence excitation and emission spectra were used to characterize the resulting products. The results of XRD reveal that the powders begin to crystallize at 500 degreesC and pure alpha-Zn-3(PO4)(2) phase is obtained at 800 degreesC. And the results of XRD reveal that Eu3+ exists Lis EoPO(4) ill the powder. In the phosphor powders, the Eu3+ shows its characteristic red-orange (592 nm, D-5(0) - F-7(1)) emission and has no quenching concentration.

Synthesis and characterization of spherical Sr2CeO4 phosphors by spray pyrolysis for field emission displays

A blue emitting Sr2CeO4 phosphor with a one-dimensional structure has been prepared by a two-step spray pyrolysis (SP) method, starting from the aqueous solutions of metal nitrates with citric acid and polyethylene glycol (PEG) as additives. The material is ultimately designed for field emission displays (FEDs). X-ray diffraction (XRD), thermogravimetric and differential thermal analysis (TG-DTA), field emission scanning electron microscope pictures (FE-SEM) as well as photoluminescence (PL) and cathodoluminescence (CL) spectroscopy and lifetime measurements have been employed to characterize the samples. The morphology, PL and low voltage CL properties of Sr2CeO4 phosphors as-prepared using the SP method have been investigated by changing the concentration of the precursor solution, concentration of PEG, annealing temperature, acceleration voltage and filament current. The obtained Sr2CeO4 phosphor particles are spherical and of submicron size, 0.5-2 mu m. The emission spectrum of the phosphors shows a broad band with maximum at 467 nm (lifetime = 37.4 mu s; CIE chromaticity coordinates: x = 0.15 and y = 0.21), presumably due to a ligand-to-metal charge-transfer transition.

Morphology control and luminescence properties of YAG : Eu phosphors prepared by spray pyrolysis

Starting from nitrate aqueous solutions with citric acid and polyethylene glycol (PEG) as additives, Y3Al5O12:Eu (YAG:Eu) phosphors were prepared by a two-step spray pyrolysis (SP) method. The obtained YAG:Eu phosphor particles have spherical shape, submicron size and smooth surface. The effects of process conditions of the spray pyrolysis on the crystallinity, morphology and luminescence properties of phosphor particles were investigated. The emission intensity of the phosphors increased with increasing of sintering temperature and solution concentration due to the increase of the crystallinity and particles size, respectively. Adequate amount of PEG was necessary for obtaining spherical particles, and the optimum emission intensity could be obtained when the concentration of PEG was 0.10 g/ml in the precursor solution. Compared with the YAG:Eu phosphor prepared by citrate-gel (CG) method with non-spherical morphology, spherical YAG:Eu phosphor particles showed a higher emission intensity.