Effects of treatment in different atmosphere on Pt3Sn/C electrocatalysts for ethanol electro-oxidation

Pt3Sn/C catalyst was prepared by a modified polyol process and treated in air, H-2/Ar, and Ar atmosphere, respectively. XRD analyses indicate that all of these catalysts have face-centered cubic (fcc) crystal structure. Temperature-programmed reduction (TPR) experiments show that more Sn exists in zero-valence in the Ar-treated PtSn catalyst than in the others. Cyclic voltammetry (CV), chronoamperometry (CA) experiments, and the performance tests of direct ethanol fuel cell (DEFC) indicate that the catalytic activity of PtSn/C for ethanol oxidation was affected significantly by the chemical state of Sn in catalyst particles. The as-prepared PtSn/C gives the higher power density, while Ar-treated PtSn/C shows the lower cell performance. It seems that the multivalence Sn rather than the zero-valence Sn in the PtSn catalyst is the favorable form for ethanol oxidation. Energy dispersion X-ray analysis (EDX) of the PtSn/C-as prepared and PtSn/C (after stability test) shows the active species (platinum, tin, and oxygen) composition changed to a different extent. Further attempt to improve the catalyst stability is needed.

Establishment of a micro-particle bombardment transformation system for Dunaliella saliva

In this study, we chronicle the establishment of a novel transformation system for the unicellular marine green alga, Dunaliella salina. We introduced the CaMV35S promoter-GUS construct into D. saliva with a PDS1000/He micro-particle bombardment system. Forty eight h after transformation, via histochemical staining, we observed the transient expression of GUS in D. salina cells which had been bombarded under rupture-disc pressures of 450 psi and 900 psi. We observed no GUS activity in either the negative or the blank controls. Our findings indicated that the micro-particle bombardment method constituted a feasible approach to the genetic transformation of D. salina. We also conducted tests of the cells' sensitivity to seven antibiotics and one herbicide, and our results suggested that 20 mu g/ ml of Basta could inhibit cell growth completely. The bar gene, which encodes for phosphinothricin acetyltransferase and confers herbicide tolerance, was introduced into the cells via the above established method. The results of PCR and PCR-Southern blot analyses indicated that the gene was successfully integrated into the genome of the transformants.

Pretreatment Method for Nitrogen Isotopic Analysis of Nitrate in Seawater

A suitable method for the pretreutment of dissolved nitrate samples in seawaters for nitrogen isotopic analysis was established. First, the seawater samples were processed by removing nitrite and amonium. Then Devard's alloy was added in sample for conversion of dissolved nitrate to ammonium. The sample was distilled, and then the ammonium condensate was collected with zeolite. after distillation, the collected condensate was filtered and prepared for determining nitropic values. Some tests of the method were conducted. The distillation condition, the influence of salinity on nitrogen isotopic analysis, absorption of ammonium onto zeolite and an improved method on a large volume of seawater were discussed in this study. The results showed that the distillation step had an average recovery of (104.9 +/- 4.2) % (n = 6) when distillating every 300 mL aliquot of the sample under a strong alkaline condition with 0.5 g devard's alloy and a distillation time of 30 min. The nitrogen isotopic fractionation decreased markedly when salinity was increased from 0% to 0.5%; further increase(1% - 3.5%) showed little effect. The adsorption rate of ammonium onto zeolite had a high yield of (95.96 +/- 1.08) % (n = 6) in average. An improved collection method was used to process a large volume of seawater with several distillations, and had good effect on analysis. The method had been applied to analyze water samples collected from Changjiang estuary. The analytical results indicate that the method is suitable for delta N-15 analysis of dissolved nitrate in seawaters. The present method could provide valuable information about the source and cycle mechanism of dissolved nitrogen in estuary waters.

Corrosion resistance of hot-dipped zinc and zinc alloy coated sheet steels under offshore atmospheric environment

The application of hot-dipped zinc and zinc-aluminum alloy coatings were introduced. Exposure tests of the steels with these coatings were conducted in the offshore atmosphere in Qingdao and Xiamen for 12 years separately. Effects of the coating thickness, alloy composition and atmospheric environment on the corrosion performance were studied. Results of the onsite exposure tests were compared with the results of a previous indoor salt spray accelerated corrosion tests. The study supports that zinc-aluminum alloy coatings are useful in providing better corrosion resistance and can be further developed for future applications.