Effect of cross-linking of high-density polyethylene. I. On spherulitic structures

Crystallization behavior and spherulitic structure of linear high-density polyethylene (HDPE), after being irradiated in its molten state by gamma -rays, was investigated by small-angle laser scattering (SALS) and differential scanning calorimetry (DSC). Significant changes in the crystallization of HDPE during cooling in air before and after being irradiated in the melt were observed. A critical minimum average molar mass between cross-links (200 carbon-carbon bonds) for spherulite formation in such an irradiated HDPE network was obtained.

XPS STUDY OF RADIATION CROSS-LINKED COPOLYMER OF TETRAFLUOROETHYLENE WITH HEXAFLUOROPROPYLENE

In this work the radiation-induced structural changes in F-46 were studied by XPS. In carbon-1s spectra of a highly crosslinked F-46 sheet, the slight increase observed in relative area under the peak due to CF3 was explained by the radiation-induced scission of polymer chains. The peak at 287.6 eV appearing in the spectra caused by ionizing radiation was attributed to carbon structures without primary fluorine substituents, in both branching and unsaturated structures, while that at 289.3 eV was assigned to = CF groups in mid-chain double bonds.

CHARACTERIZATION OF GAMMA-RADIATION CROSS-LINKED CRYSTALLINE POLYMERS BY CRYSTALLIZATION TEMPERATURE

The effect of gamma-radlatlon on plain crystalline polymers and crystalline polymers containing different amounts of difunctional monomer both in vacuum and in air at room temperature has been investigated with DSC. It was found that the crystallization temperature T_c of crosslinked sample measured on DSC at a constant cooling rate decreases with increasing radiation dose. The difference between T_c before and after crosslinking (T_(c_0)-T_(c_R)) is linearly related to the radiation dose for plain polymer....

共混体系强化辐射交联、增强界面辐射反应研究及新型结构多官能团单体合成

本文选取比较常见的PP/EVA、PE/EVA共混体系作为增强交联研究的对象，研究了共混体系的增强交联规律，并针对目前普通使用的多官能团单体存在着与聚合物体系相容性差、易析出、高温挥发大的弱点，设计合成几种多官能团单体。此外，还研究了共混体系增强界面反应，讨论了增强界面反应的一般原理和增强界面反应对改善不相容共混体系相间粘附的作用影响。

辐射交联低烟无卤阻燃材料的研究

聚合物材料以其优异的电绝缘性能而广泛地用作电气绝缘材料。但聚合物材料易燃的缺点促使人们不断地对其进行阻燃性的研究，这种研究过程从添加卤素阻燃剂到非卤素化阻燃逐步完善。本文在阐述了聚合物材料燃烧特性及机理的基础上，介绍了几种常用的无卤阻燃剂的阻燃机理，并对氢氧化铝、氢氧化镁和红磷等应用于聚烯烃复合体系的阻燃性进行了实验研究。结果表明：氢氧化镁的阻燃性优于氢氧化铝，它们达到较好的阻燃效果时的添加量一般为120-150phr。氢氧化镁与红磷复配使用在添加量为90phr时，氧指数为40，阻燃性能十分优秀。材料具有良好的阻燃性能。但与此同时材料的机械性能、电性能及加工性能等都将受到一定程度的破坏。经过选用偶联剂及进行辐射交联改性， 材料的机械性能令人满意。交联度及电气性能的实验。最终得到符合九五科技攻关项目“辐射交联低烟无卤阻燃电线电缆的研究”的预期目标。

Electron-beam irradiation on poly(propylene carbonate) in the presence of polyfunctional monomers

Poly(propylene carbonate) (PPC) showed predominantly degradation under electron-beam irradiation, accompanied by deterioration of its mechanical performance due to sharp decrease of the molecular weight. Crosslinked PPC was prepared by addition of polyfunctional monomer (PFM) to enhance the mechanical performance of PPC. When 8 wt% of PFM like triallyl isocyanurate (TAIL) was added, crosslinked PPC with a gel fraction of 60.7% was prepared at 50 kGy irradiation dose, which showed a tensile strength at 20 degrees C of 45.5 MPa, whereas it was only 38.5 MPa for pure PPC. The onset degradation temperature (T-i) and glass transition temperature (T-g) of this crosslinked PPC was 246 degrees C and 45 degrees C, respectively, a significant increase related to pure PPC of 211 degrees C and 36 C. Therefore, thermal and mechanical performances of PPC could be improved via electron-beam irradiation in the presence of suitable PFM.

Effect of gamma-radiation on the thermal and mechanical properties of a commercial poly(butylene adipate-co-terephthalate)

BACKGROUND: Poly(butylene adipate-co-terephthalate) (PBAT) has attracted wide interest as a biodegradable polymer. However, its use is restricted in certain applications due to its low melting point.RESULTS: PBAT was treated using gamma-radiation. The radiation features were analyzed using Soxhlet extraction, and the ratio of chain scission and crosslinking and gelation dose were determined using the classical Charlesby-Pinner equation. The results showed that PBAT is a radiation-crosslinkable polymer. The degree of crosslinking increased with increasing radiation dose; the relation between sol fraction and dose followed the Charlesby-Pinner equation. Differential scanning calorimetry analyses showed that the melting temperature (T-m) and the heat of fusion (Delta H-m) of PBAT exhibited almost no change in the first scan. The second scan, however, showed a decrease in T-m and Delta H-m. The glass transition temperature of irradiated PBAT increased with increasing radiation dose.

Radiation effects on the immiscible polymer blend of nylon1010 and high-impact polystyrene (HIPS) I: Gel/dose curves, mathematical expectation theorem and thermal behaviour

This paper studies the radiation properties of the immiscible blend of nylon1010 and HIPS. The gel fraction increased with increasing radiation dose. The network was found mostly in nylon1010, the networks were also found in both nylon1010 and HIPS when the dose reaches 0.85 MGy or more. We used the Charleby-Pinner equation and the modified Zhang-Sun-Qian equation to simulate the relationship with the dose and the sol fraction. The latter equation fits well with these polymer blends and the relationship used by it showed better linearity than the one by the Charleby-Pinner equation. We also studied the conditions of formation of the network by the mathematical expectation theorem for the binary system. Thermal properties of polymer blend were observed by DSC curves. The crystallization temperature decreases with increasing dose because the cross-linking reaction inhibited the crystallization procession and destroyed the crystals. The melting temperature also reduced with increasing radiation dose. The dual melting peak gradually shifted to single peak and the high melting peak disappeared at high radiation dose. However, the radiation-induced crystallization was observed by the heat of fusion increasing at low radiation dose. On the other hand, the crystal will be damaged by radiation. A similar conclusion may be drawn by the DSC traces when the polymer blends were crystallized. When the radiation dose increases, the heat of fusion reduces dramatically and so does the heat of crystallization. (C) 1999 Elsevier Science Ltd. All rights reserved.

Stabilization of poly(lactic acid) by polycarbodiimide

Polycarbodiimide (CDI) was used to improve the thermal stability of poly(L-lactic acid) (PLA) during processing. The properties of PLA containing various amounts of CDI were characterized by GPC, DSC, rheology, and tensile tests. The results showed that an addition of CDI in an amount of 0.1-0.7 wt% with respect to PLA led to stabilization of PLA at even 210 degrees C for up to 30 min, as evidenced by much smaller changes in molecular weight. melt viscosity, and tensile strength and elongation compared to the blank PLA samples. In order to examine the possible stabilization mechanism, CDI was reacted with water, acetic acid, L-lactic acid, ethanol and low molecular weight PLA. The molecular structures of the reaction products were measured with FTIR.

Macrocycle-Terminated Core-Cross-Linked Star Polymers: Synthesis and Characterization

We have synthesized macrocyclic polystyrene- (PS-) terminated PS star polymers via a core-cross-linking approach in this work. A tadpole-shaped macrocyclic PS-linear-PS copolymer was synthesized at first via click chemistry and ATRP polymerization method. The "living" ATRP initiating chain-ends of the tadpole-shaped copolymers were linked together via ATRP polymerization with divinylbenzene to form a core-cross-linked macrocyclic star polymer. The number of arms attached to the macrocyclic star polymers was measured with NMR. and absolute molecular weights with gel permeation chromatography (GPC) with multiangle laser light scattering detector. These macrocyclic star polymers had a highly cross-linked core and many radiating arms. The shorter tadpole-shaped precursors caused core-cross-linked star polymers with higher molecular weights and more arm numbers. The macrocycle-terminated core-cross-linked star polymers showed two glass transition temperatures, one arising from the linear branches and another from the macrocycles.

Synthesis and characterization of photo-cross-linked hydrogels based on biodegradable polyphosphoesters and poly(ethylene glycol) copolymers

Novel biodegradable hydrogels by photo-cross-linking macromers based on polyphosphoesters and poly(ethylene glycol) (PEG) are reported. Photo-cross-linkable macromers were synthesized by ring-opening polymerization of the cyclic phosphoester monomer 2-(2-oxo-1,3,2-dioxaphospholoyloxy) ethyl methacrylate (OPEMA) using PEG as the initiator and stannous octoate as the catalyst. The macrorners were characterized by H-1 NMR, Fourier transform infrared spectroscopy, and gel permeation chromatography measurements. The content of polyphosphoester in the macromer was controlled by varying the feed ratio of OPEMA to PEG. Hydrogels were fabricated by exposing aqueous solutions of macromers with 0.05% (w/w) photoinitiator to UV light irradiation, and their swelling kinetics as well as degradation behaviors were evaluated. The results demonstrated that cross-linking density and pH values strongly affected the degradation rates. The macromers was compatible to osteoblast cells, not exhibiting significant cytotoxicity up to 0.5 mg/mL. "Live/dead" cell staining assay also demonstrated that a large majority of the osteoblast cells remained viable after encapsulation into the hydrogel constructs, showing their potential as tissue engineering scaffolds.

Investigation of irradiated PA1010 containing heterogeneous nuclei

This paper deals with radiation effects on PA1010 containing heterogeneous nuclei (Nd2O3). With the help of DSC, WAXD and ESR techniques, the change in the crystallinity and the perfection of the crystal of irradiated PA1010 containing heterogeneous nuclei were studied. Copyright (C) 1996 Elsevier Science Ltd.

SYNTHESIS AND CHARACTERIZATION OF CROSS-LINKED 2ND-ORDER NONLINEAR-OPTICAL POLYMER

The present paper reports the synthesis of glycidyl monoether of 4-[(p-nitrophenyl) azo] phenol (GMNA) and crosslinking reaction of GMNA with hexamethylene diisocyanate biuret (HDIB). The Tg of crosslinked polymer was investigated by DSC. The orientation and stability of the poled and crosslinked polymer film were studied by UV-Vis spectra and Maker fringe method.

CHARACTERIZATION OF GAMMA-IRRADIATED CRYSTALLINE POLYMER .3. THERMAL-BEHAVIOR OF GAMMA-IRRADIATED POLYAMIDE-1010

Thermal behaviour of gamma-irradiated plain PA1010 and PA1010 containing different amounts of difunctional cross-linking agent BMI was investigated. In DSC endo- and exotherm, it was found that during irradiation, the presence of BMI markedly changes the melting and crystallisation characteristics of PA1010. A supposition that the network of BMI-containing specimens is rather loose in structure was proposed to explain the discrepancy in thermal behaviour between these two kinds of specimens. The supposition was further ascertained by the less brittleness in mechanical property of specimens containing BMI. Besides, the complexity of the thermal behaviour of gamma-irradiated PA1010 was discussed and attributed mainly to the increase in sigma-e, the fold surface free energy of chain fold crystals.