273 resultados para POLY(P-PHENYLENEVINYLENE) COPOLYMERS
Resumo:
With a newly synthesized poly(p-phenylene vinylene) (PPV) multiblock copolymer used in a triple-layer structure, efficient green light-emitting diodes with low driving voltage have been fabricated. The devices are turned on at 2.5 V, the brightness at 5 V is above 100 cd/m(2) and at 7 V is about 1650 cd/m(2), with an external quantum efficiency of about 1%. (C) 1998 Elsevier Science S.A. All rights reserved.
Resumo:
The blends of poly(beta-hydroxybutyrate-co-beta-hydroxyvalerate) (P(HB-co-HV)/poly(p-vinylphenol)(PVPh) were investigated by differential scanning calorimetry (DSC), Fourier transform IR (FT-IR) spectroscopy and high-resolution solid-state C-13 NMR techniques. Single glass transition temperatures existing in the whole composition range indicates that these blends are miscible. The presence of hydrogen bonding between the hydroxyl of PVPh and carbonyl of P(HB-co-HV), shown by FT-IR spectra, is the origin of the miscibility. Furthermore, results obtained by high-resolution solid-state C-13 NMR give more information about the structure of the blends. (C) 1998 Elsevier Science Ltd. All rights reserved.
Resumo:
Bright blue electroluminescent devices have been fabricated using poly (N-vinylcarbazole) (PVK) doped with perylene as the emissive layer, poly(p-phenylenevinylene) (PPV) as the hole-transporting layer, 2-(4-biphenylyl)-5-(4-tert-butylphenyl)-1,3,4-oxadiazole (PBD), tris(8-hydroxyquinoline)aluminum (Alq(3)) as the electron-transporting layer, and Al as the cathode. A luminance of 700 cd/m(2) and a luminescent efficiency of 0.8% are achieved at a drive voltage of 36 V. In the experiment, it is found that the introduction of electron-transporting layer PBD has a great effect on the emissive color of the electroluminescent devices prepared by PVK doped with perylene. Yellow-green emission is observed from the device structure of glass substrate/indium-tin-oxide/PVK:perylene/Al. The possible emissive mechanisms are given. The effect of the transporting layer on the electroluminescence is also discussed. (C) 1997 Elsevier Science S.A.
Resumo:
The miscibility and crystallization behavior of poly(beta-hydroxybutyrate) (PHB) and poly(p-vinylphenol) (PVPh) blends were studied by differential scanning calorimetry and optical microscopy (OM). The blends exhibit a single composition-dependent glass transition temperature, characteristic of miscible systems, A depression of the equilibrium melting temperature of PHB is observed. The interaction parameter values obtained from analysis of the melting point depression are of large negative values, which suggests that PHB and PVPh blends are thermodynamically miscible in the melt. Isothermal crystallization kinetics in the miscible blend system PHB/PVPh was examined by OM. The presence of the amorphous PVPh component results in a reduction in the rate of spherulite growth of PHB. The spherulite growth rate is analyzed using the Lauritzen-Hoffman model, The isothermally crystallized blends of PHB/PVPh were examined by wide-angle X-ray diffraction and smell-angle X-ray scattering (SAXS). The long period obtained from SAXS increases with the increase in PVPh component, which implies that the amorphous PVPh is squeezed into the interlamallar region of PHB.
Compatibility and specific interactions in poly(beta-hydroxybutyrate) and poly(p-vinylphenol) blends
Resumo:
The miscibility and specific interactions in poly (beta-hydroxybutyrate) (PHB)/poly(p-vinylphenol) (PVPh) blends were studied by differential scanning calorimetry(DSC) , fourier transform infrared(FTIR) spectrometer and high resolution solid state C-13 NMR, A single composition-dependent glass transition temperatures were obtained by DSC which indicate the blends of PHB/PVPh were miscible in the melt state, The experimental glass transition temperatures were fitted quite well with those obtained from Couchman-Karasz equation. The FTIR study shows that the strong intermolecular hydrogen bonding exists in blends of PHB with strong proton acceptor and PVPh with strong proton donor and is the origin of its compatibility. The CPMAS C-13 NMR spectra also show that the strong hydrogen bonding exists in PHB/PVPh blends. From the T-1 rho(H) relaxation time it follows that the blends of PHB/PVPh(40/60, 20/80) studied are completely homogeneous on the scale of about 3.2 nm.
Resumo:
该论文以提高聚苯撑乙烯(PPV)类发光聚合物的空穴传输性能为主要目的,通过将具有较高空穴传输能力的芳胺类小分子基元引入发光聚合物分子链,设计并合成了一系列含芳胺基元的PPV聚合物.另外,还通过对分子结构进行设计和控制,获得了红绿蓝三基色发光.最后还利用在共轭分子主链上引入具有三维空间位阻的侧链基团,获得了高效率的绿色发光聚合物材料.
Resumo:
A soluble electroluminescent polymer containing hole-deficient triphenylamine and electron-deficient oxadiazole units in the main chains has been designed and studied. The design is based on the consideration that the triphenylamine group possesses good hole-transporting property and the oxadiazole unit is known to be of electron-transporting character. Because of the good bipolar transporting performance, the brightness and electroluminescent efficiency are significantly improved and the turn-on voltage is reduced compared with a similar polymer without the electron-deficient oxadiazole units in the main chains. For a device with configuration ITO/PEDOT/polymer/CsF/Al, a maximum brightness of 3600 cd m(-2) and a maximum luminescent efficiency of 0.65 cd A(-1) (quantum efficiency of 0.3%) were obtained in the polymer with oxadiazole units, about 15 times brighter and 15 times more efficient than the corresponding polymer without oxadiazole units.
Resumo:
A navel thermally stable terbium carboxylate complex, Tb(MTP)(3)(phen) (MTP=monotetradecyl phthalate, phen=1,10-phehanthroline), was synthesized and characterized. The device structure of glass substrate/indium-tin-oxide/poly(p-phenylenevinylene) (PPV)/poly (N-vinycarbazole) (PVK):Tb(MTP)(3)(phen): 1,3,4-oxadizole derivative (PBD)/tris(8-hydroxyquinoline) (Alq(3))/aluminum (Al) was employed to study the electroluminescent properties of Tb(MTP)(3)(phen). A green emission with extremely sharp spectral band of less than 10 nm at 544 nm peak wavelength was observed. A maximum luminance of 152 cd/m(2) and an external quantum efficiency of 0.017% were achieved at a drive voltage of 24 V. A possible mechanism of energy transfer based on the polymer doped with lanthanide organic complex was also proposed.
Resumo:
Grignard metathesis (GRIM) polymerization for all-conjugated diblock copolymers comprising poly (2,5-dihexyloxy-1,4-phenylene) (PPP) and poly(3-hexylthiophene) (P3HT) blocks were systematically studied with LiCl as additive and 1,2-bis (diphenylphosphino) ethane nickel dichloride (Ni(dppe)Cl-2) or 1,3-bis(diphenylphosphino) propane nickel dichloride (Ni(dppp)Cl-2) as catalyst. It was found that the addition order of the monomers was crucial for the success of copolymerization. With the monomer addition in the order of phenyl and then thienyl Grignard reagents, all-conjugated PPP-b-P3HT diblock copolymers with different block ratios were successfully synthesized. In contrast, the inverted addition order only afforded a mixture containing both block copolymers and deactivated or end-capped homopolymers.
Resumo:
A new class of high-performance materials, fluorinated poly(phenylene-co-imide)s, were prepared by Ni(0)-catalytic coupling of 2,5-dichlorobenzophenone with fluorinated dichlorophthalimide. The synthesized copolymers have high molecular weights ((M) over bar (W)= 5.74 x 10(4)-17.3 x 10(4) g center dot mol(-1)), and a combination of desirable properties such as high solubility in common organic solvent, film-forming ability, and excellent mechanical properties. The glass transition temperature (T(g)s) of the copolymers was readily tuned to be between 219 and 354 degrees C via systematic variation of the ratio of the two comonomers. The tough polymer films, obtained by casting from solution, had tensile strength, elongation at break, and tensile modulus values in the range of 66.7-266 MPa, 2.7-13.5%, and 3.13-4.09 GPa, respectively. The oxygen permeability coefficients (P-O2) and permeability selectivity of oxygen to nitrogen (P-O2/P-N2) of these copolymer membranes were in the range of 0.78-3.01 barrer [1 barrer = 10(-10) cm(3) (STP) cm/(cm(2) center dot s center dot cmHg)] and 5.09-6.2 5, respectively. Consequently, these materials have shown promise as engineering plastics and gas-separation membrane materials.
Resumo:
A series of light-emitting poly(p-phenylene vinylene)s with triphenylamine units as hole-transporting moieties in the main chain were synthesized via Wittig condensation in good yields. The newly formed vinylene double bonds possessed a trans configuration, which was confirmed by Fourier transform infrared and NMR spectroscopy. The high glass-transition temperature (83-155 degreesC) and high decomposition temperature (> 300 degreesC) suggested that the resulting copolymers possessed high thermal stability. These copolymers, especially TAAPV1, possessed a high weight-average molecular weight (47,144) and a low polydispersity index (1.55). All the copolymers could be dissolved in common organic solvents, such as tetrahydrofuran (THF), CHCl3, CH2Cl2, and toluene, and exhibited intense photoluminesence in THF (the emission maxima were located from 478 to 535 nm) and in film (from 478 to 578 nm). The low onsets of the oxidation potential (0.6-0.75 V) suggested that the alternating copolymers possessed a good hole-transporting property due to the incorporation of triphenylamine moieties. (C) 2001 John Wiley & Sons, Inc.
Resumo:
Poly(vinyl acetate-co-vinyl alcohol) copolymers (P(VAc-co-VA)) were synthesized by hydrolysis-alcoholysis of PVAc. The miscibility, crystallization, and morphology of poly(P-hydroxybutyrate) (PHB) and P(VAc-co-VA) blends were studied by differential scanning calorimetry, optical microscopy (OM), and SAXS. It is found that the P(VAc-co-VA)s with vinyl alcohol content of 9, 15, and 22 mol % will form a miscible phase with the amorphous part of PHB in the solution-cast samples. The melting-quenched samples of PHB/P(VAc-co-VA) blends with different vinyl alcohol content show different phase behavior. PHB and P(VAc-co-VA9) with low vinyl alcohol content (9% mel) will form a miscible blend in the melt state. PHB and P(VAc-co-VA15) with 15 mol % vinyl alcohol will not form miscible blends while PHB/P(VAc-co-VA15) blend with 20/80 composition will form a partially miscible blend in the melt state. PHB and P(VAc-co-VA22) with 22 mol % vinyl alcohol are not miscible in the whole composition range. The single glass transition temperature of the blends within the whole composition range suggests that PHB and P(VAc-co-VA9) are totally miscible in the melt. The crystallization kinetics was studied from the whole crystallization and spherulite growth for the miscible blends. The equilibrium melting point of PHB in the PHB/P(VAc-co-VA9) blends, which was obtained from DSC results using the Hoffman-Weeks equation, decreases with the increase in P(VAc-co-VA9) content. The negative value of the interaction parameter determined from the equilibrium melting point depression supports the miscibility between the components. The kinetics of spherulitic crystallization of PHB in the blends was analyzed according to nucleation theory in the temperature range studied in this work. The best fit of the data to the kinetic theory is obtained by employing WLF parameters and the equilibrium melting points obtained by DSC. The addition of P(VAc-co-VA) did not affect the crystalline structure of PHB, as shown by the WAXD results. The long periods of blends obtained from SAXS increase with the increase in P(VAc-co-VA) content. It indicates that the amorphous P(VAc-co-VA) was rejected to interlamellar phase corporating with the amorphous part of PHB.
Resumo:
The microstructure of two bicomponent and one tricomponent segmented copolymers, based on polydimethylsiloxane, poly(p-hydroxystyrene) or/and polysulfone, were investigated using an extended Goldman-Shen pulse sequence, proton spin-spin relaxation measurements, and C-13 and Si-29 NMR spectra. The results indicate that there exist four phases with different sizes, components and morphological structure in the segmented copolymers studied in this work, i. e., a rigid-chain phase of very slow motion, a rigid-chain-rich phase of slow motion, a flexible-chain-rich phase of fast motion and a flexible-chain phase of faster motion. The sizes of different domains, calculated from the spin diffusion rates, are about 50-100 angstrom for the flexible-chain-rich phase of fast motion and 200-300 angstrom for the flexible-chain phase of faster motion. The relative quantities of polydimethylsiloxane in the flexible-chain phase of fast motion are slightly different in different kinds of segmented copolymers.
Resumo:
We functionalize the focal group of hyperbranched poly(phenylene sulfide) (HPPS) with benzyl, phenyl, and naphthyl group, respectively. DSC analysis shows that T-g of HPPS is increased from 55 to 93 degrees C by functionalization of the focal group with a conjugated naphthyl group. The fluorescence properties of the three core-functionalized HPPS' are studied under the comparison with the original HPPS.