Submitted by 阎军 (yanj@red.semi.ac.cn) on 2010-06-04T07:55:26Z No. of bitstreams: 1 Diffractive Grating Based Out-of-Plane Coupling between Silicon Nanowire and Optical Fiber.pdf: 232805 bytes, checksum: 0bd17756b8a703bf8337dd25bbddaca3 (MD5)

Experimental Study on the Subthreshold Swing of Silicon Nanowire Transistors

SOI based wrap-gate silicon nanowire FETs are fabricated through electron beam lithography and wet etching. Dry thermal oxidation is used to further reduce the patterned fins cross section and transfer them into nanowires. Silicon nanowire FETs with different nanowire widths varying from 60 nm to 200 nm are fabricated and the number of the nanowires contained in a channel is also varied. The on-current (I-ON) and off-current (I-OFF) of the fabricated silicon nanowire FET are 0.59 mu A and 0.19 nA respectively. The subthreshold swing (SS) and the drain induced barrier lowering are 580 mV/dec and 149 mVN respectively due to the 30 nm thick gate oxide and 1015 cm(-3) lightly doped silicon nanowire channel. The nanowire width dependence of SS is shown and attributed to the fact that the side-gate parts of a wrap gate play a more effectual role as the nanowires in a channel get narrower. It seems the nanowire number in a channel has no effect on SS because the side-gate parts fill in the space between two adjacent nanowires.

Surface Plasmon Resonances of Cu Nanowire Arrays

Surface plasmon resonances of arrays of parallel copper nanowires, embedded in ion track-etched polycarbonate membranes, were investigated by systematic changes of nanowires’ topology and arrays area density. The extinction spectra exhibit two peaks which are attributed to interband transitions of Cu bulk metal and to a dipolar surface plasmon resonance, respectively. The resonances were investigated as a function of wire diameter and length, mean distance between adjacent wires, and angle of incidence of the light field with respect to the long wire axis. The dipolar peak shifts to larger wavelengths with increasing diameter and length, and diminishing mean distance between adjacent wires. Additionally, the shape effect on the dipolar peak is investigated.

Preparation and Optical Properties of Gold Nanowire Arrays

Gold nanowires with diameters (d) between,15 run and 200 urn and with length/diameter ratio of 700 were prepared in ion-track templates with electrode position method. The morphology and crystal structure of the gold nanowires were Studied by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The 200 nm (d) gold nanowires preferred orientation along the [100] direction were formed at the deposition voltage of 1.5 V (Without reference electrode). The optical properties of gold nanowire arrays embedded in ion-track templates were studied by UV-Vis spectrophotometer. There was a strong absorption peak at 539 nm for 45 nm (d) gold nanowire arrays. With the diameter of gold nanowires increasing, the absorption peak shifted to the longer wavelength. At last, the result was discussed combined with surface plasmon resonance of gold nanoparticles.

Controlled synthesis and diameter-dependent optical properties of Cu nanowire arrays

Using electrochemical deposition, Cu nanowire arrays have been successfully fabricated by home-made polycarbonate ion-track templates. The diameters were well controlled by etching time of templates. The minimum diameter is 15 nm. The morphologies and structures were analyzed by scanning electron microscopy, transmission electron microscopy and X-ray diffraction. The wires prefer [1 1 0] growth direction due to H ions absorption. The optical properties of Cu nanowire arrays are studied by an ultraviolet/visible/near-infrared spectrophotometer. Two extinction peaks were observed in spectra. The optical mechanism is discussed based on surface plasmon resonance

Surface-enhanced Raman scattering from surfactant-free 3D gold nanowire networks substrates

A useful method for the fabrication of three-dimensional gold nanowire networks based on the chemical reduction of HAuCl4 with trisodium citrate was presented. The coverage of the 3D gold nanowire networks was tunable by altering precursor concentration. The as-prepared 3D gold nanowire networks could be used as surface-enhanced Raman scattering (SERS) substrates and examined by 4-aminothiophenol (4-ATP) as a probe molecules.

Large-area silver-coated silicon nanowire arrays for molecular sensing using surface-enhanced Raman spectroscopy

A new and facile method to prepare large-area silver-coated silicon nanowire arrays for surface-enhanced Raman spectroscopy (SERS)-based sensing is introduced. High-quality silicon nanowire arrays are prepared by a chemical etching method and used as a template for the generation of SERS-active silver-coated silicon nanowire arrays. The morphologies of the silicon nanowire arrays and the type of silver-plating solution are two key factors determining the magnitude of SERS signal enhancement and the sensitivity of detection; they are investigated in detail for the purpose of optimization.

Green synthesis of nanowire-like Pt nanostructures and their catalytic properties

We reported a simple and effective green chemistry route for facile synthesis of nanowire-like Pt nanostructures atone step. In the reaction, dextran acted as a reductive agent as well as a protective agent for the synthesis of Pt nanostructures. Simple mixing of precursor aqueous solutions of dextran and K2PtCl4 at 80 degrees C could result in spontaneous formation of the Pt nanostructures. Optimization of the experiment condition could yield nanowire-like Pt nanostructures at 23:1 molar ratio of the dextran repeat unit to K2PtCl4.

Monitoring catalytic degradation of dye molecules on silver-coated ZnO nanowire arrays by surface-enhanced Raman spectroscopy

Catalytic degradation of organic dye molecules has attracted extensive attention due to their high toxicity to water resources. In this paper, we propose a novel method for the fabrication of uniform silver-coated ZnO nanowire arrays. The degradation of typical dye molecule rhodamine 6G (R6G), as an example, is investigated in the presence of the as-prepared silver-coated ZnO nanowire arrays. The experimental results show that such composite nanostructures exhibit high catalytic activity, and the reaction follows pseudo-first-order kinetics. Furthermore, these nanowire arrays are desirable SERS substrates for monitoring the catalytic degradation of dye molecules. Compared with traditional UV-visible spectroscopy, SERS technology can reflect more truly the catalytic degradation process occurring on the surface of the catalysts.

Gold nanowire assembling architecture for H2O2 electrochemical sensor

Morphological control of nanomaterials is of great interest due to their size and shape-dependent chemical and physical properties and very important applications in many fields such as biomedicine, sensors, electronics and others. In this paper, we reported a simple strategy for synthesizing gold nanowire assembling architecture at room temperature. It is found that two important factors, the proper volume ratio of ethanol to water and poly(vinyl pyrrolidone) (PVP), will play important roles in synthesizing flower-like short gold nanowire assembling spheres. Furthermore, the obtained flower-like gold assembling spheres with high surface-to-volume ratio have been employed as enhancing materials for electrochemical sensing H2O2. The present electrochemical sensing platform exhibited good electrocatalytic activity towards the reduction of H2O2. The detection limit for H2O2 was found to be 1.2 mu M, which was lower than certain enzyme-based biosensors.

Native growth of vertically pattened ZnO nanowire arrays under mild conditions without templates or catalysts

Based on the implications of a pellet experiment,we have designed and implemented a low temperature(≤90℃) approach to generate native patterned,vertically aligned ZnO nanoarrys without any templates or catalysts.This simple,economic and spontaneous patterning process offers a promising avenue for overcoming several inherent limitations of the artificial manners[1].While the purity,orientation and electrical properties of the as prepared materials allow them to be applied in various fields.

A study on the antibacterial activity of one-dimensional ZnO nanowire arrays: effects of the orientation and plane surface

In this study, ZnO nanowire arrays with different orientations were prepared. Confocal laser scanning microscopy (CLSM) and field- emission scanning electron microscope (FE- SEM) technique were employed for understanding the disparities in antibacterial activity between different orientations of ZnO nanoarrays. The effects of the different planes of ZnO nanowire were also discussed for the first time.