Characterization of Er3+-doped Na2O-WO3-TeO2 glass for ion-exchanged waveguide amplifiers and lasers

Er^(3+)-doped Na2O-WO3-TeO2 glass consistent with standard ion-exchange technology has been fabricated and characterized. The measured absorption and emission spectra of the glass were analyzed by the Judd-Ofelt and McCumber theories. The intensity parameters are Ω2 = 7.01

Spectroscopic and fluorescence decay behaviors of Yb3+ -doped SiO2-PbO-Na2O-K2O glass

The spectroscopic and fluorescent decay behaviors of Yb3+-doped SiO2-PbO-Na2O-K2O glass is reported in this work. Yb2O3 contents of 1, 1.5 and 2mol% are added into the glass. Through the measurement of absorption and fluorescence spectra, and fluorescent decay rate at room temperature and at low temperature (18 K), it is found that the nonradiative decay rate of Yb3+ ions is mainly determined by the interaction between residual hydroxyl groups and Yb3+ ions. Concentration quenching effect can be omitted in this glass up to the Yb3+ ion concentration of 8.98 x 10(20)/cm(3). Multiphonon decay rate is also very small because of the large energy gap between F-2(5/2) and F-2(7/2) levels of Yb3+ ions. (c) 2004 Elsevier B.V. All rights reserved.

Spectroscopic properties of Er3+ doped TeO2-BaO (Li2O, Na2O)-La2O3 glasses for 1.5-mu m optical amplifiers

This paper reports on the optical spectroscopic properties and thermal stability of Er3+-doped TeO2-BaO (Li2O,NaO)-La2O3 glasses for developing 1.5-mu m fiber amplifiers. Upon excitation at 977 nm laser diode, an intense 1.53-mu m infrared fluorescence has been observed with a broad full width at half maximum (FWHM) of about 60 nm for the Er3+-doped TeO2-BaO (Li2O, Na2O)-La2O3 glass with 10 mol% of BaO. The calculated fluorescence lifetime and the emission cross-sections of the 1.53-mu m transition are 2.91 ms and similar to 9.97 x 10(-21) cm(2), respectively. It is noted that the gain bandwidth, a, x FWHM, of the TeO2-BaO-La2O3Er2O3 glass is about 600, which is significantly higher than that in silicate and phosphate glasses. Meanwhile, it is interesting to note that the TeO2-BaO-La2O3-Er2O3 glass has shown a high glass thermal stability and good infrared transmittance. As a result, TeO2-BaO (Li2O, Na2O)-La2O3 glass with 10 mol% of BaO has been considered to be more useful as a host for broadband optical fiber amplifier. (c) 2005 Elsevier B.V. All rights reserved.

NOVEL COMPOSITES OF POLY(L-LACTIDE) AND SURFACE MODIFIED BIOACTIVE SiO2-CaO-P2O5 GEL NANOPARTICLES: MECHANICAL AND BIOLOGICAL PROPERTIES

Bioactive SiO2-CaO-P2O5 gel (BAG) nanoparticles with 40 nm in diameter were synthesized by the sol-gel route and further modified via the ring-opening polymerization of lactide on the surface of particles. Surface modified BAG (mBAG) was introduced in poly(L-lactide) (PLLA) matrix as bioactive filler. The dispersibility of mBAG in PLLA matrix was much higher than that of rough BAG particles. Tensile strength of the mBAG/PLLA composite could be increased to 61.2 MPa at 2 wt% filler content from 53.4 MPa for pure PLLA. The variation of moduli of the BAG/PLLA and mBAG/PLLA composites always showed an enhancement tendency with the increasing content of filler loading. The SEM photographs of the fracture surfaces showed that mBAG could be homogeneously dispersed in the PLLA matrix, and the corrugated deformation could absorb the rupture energy effectively during the breaking of materials. In vitro bioactivity tests showed that both BAG and mBAG particles could endow the composites with ability of the calcium sediment in SBF, but the surface modification of BAG particles could weaken this capability to some extent. Biocompatibility tests showed that both BAG and mBAG particles could facilitate the attachment and proliferation of the marrow cells on the surface of the composite.

Long lasting phosphorescence of Eu2+ in reduced SrO-B2O3 glasses

The blue long-lasting phosphorescence (LLP) phenomenon was observed for Eu2+-doped SrO-B2O3 glasses prepared in the reducing atmosphere. The phosphorescence peaks at about 450 nm due to the 4f5d -> 4f transition of Eu2+. With the doping of different amounts of Eu2+, the concentration-quenching phenomenon was observed for both the LLP and photoluminescence of the glasses, and the critical concentration for the two cases was same, i.e., 0.02 mol% Eu2+. And by the investigation of the TL curves, the content of Eu2+ had an effect on the trap depth of the samples. At last the possible mechanism of the LLP of the samples was suggested.

A new type of highly efficient luminescent material - The system Al2O3-B2O3 containing Ce3+ and Tb3+ ions

The system Al2O3-B2O3 containing Ce3+ and Tb3+ ions was investigated for the first time. It was found that certain compositions give rise to a new highly efficient green luminescent material.

Multi-color long-lasting phosphorescence in Mn2+-doped ZnO-B2O3-SiO2 glass-ceramics

Multi-color LLP phenomenon was observed in Mn2+-doped ZnO-B2O3-SiO2 glassceramics after the irradiation of a UV lamp at room temperature. Transparent ZnO-B2O3-SiO2 glass emitted reddish LLP while opaque glass-ceramics prepared by the glass sample after heat treatment emitted yellowish or greenish LLP. The change of the phosphorescence is due to the alteration of co-ordination state of Mn2+. The phosphorescence of the samples was seen in the dark with naked eyes even 12 h after the irradiation with a UV lamp (lambda(max) = 254 nm) for 30 min. Based on the approximative t(-1) decay law of the phosphorescence, we suggest that the LLP is attributed to the thermally assisted electron-hole recombination.