Infrared luminescence properties of bismuth-doped barium silicate glasses

Infrared (IR) luminescence covering 1.1 to similar to 1.6 mu m wavelength region was observed from bismuth-doped barium silicate glasses, excited by a laser diode at 808 nm wavelength region, at room temperature. The peak of the IR luminescence appears at 1325 nm. A full width half-maximum (FWHM) and the lifetime of the fluorescence is more than 200 nm and 400 mu s, respectively. The fluorescence intensity increases with Al2O3 content, but decreases with BaO content. We suggest that the IR luminescence should be ascribed to the low valence state of bismuth Bi2+ or Bi+, and Al3+ ions play an indirect dispersing role for the infrared luminescent centers.

Broadband infrared luminescence from transparent glass-ceramics containing Ni2+-doped beta-Ga2O3 nanocrystals

Transparent Ni2+-doped beta-Ga2O3 glass-ceramics were synthesized. The nanocrystal phase in the glass-ceramics was identified to be beta-Ga2O3 and its size was about 3.6 nm. It was confirmed from the absorption spectra that the ligand environment of Ni2+ ions changed from the trigonal bi-pyramid fivefold sites in the as-cast glass to the octahedral sites in the glass-ceramics. The broadband infrared emission centering at 1270 nm with full width at half maximum (FWHM) of more than 250 nm was observed. The fluorescence lifetime was about 1.1 mu s at room temperature. The observed infrared emission could be attributed to the T-3 (2g) (F-3) -> (3)A (2g) (F-3) transition of octahedral Ni2+ ions. It is suggested that the Ni2+-doped transparent beta-Ga2O3 glass-ceramics with broad bandwidth and long lifetime have a potential as a broadband amplification medium.

Transparent Ni2+-doped ZnO-Al2O3-SiO2 system glass-ceramics with broadband infrared luminescence

We report transparent Ni2+-doped ZnO-Al2O3-SiO2 system glass-ceramics with broadband infrared luminescence. After heat-treatment, ZnAl2O4 crystallite was precipitated in the glasses, and its average size increased with increasing heat-treatment temperature. No infrared emission was detected in the as-prepared glass samples, while broadband infrared luminescence centered at 1310 nm with full width at half maximum (FWHM) of about 300 nm was observed from the glass-ceramics. The peak position of the infrared luminescence showed a blue-shift with increasing heat-treatment temperature, but a red-shift with an increase in NiO concentration. The mechanisms of the observed phenomena were discussed. These glass-ceramics are promising as materials for super broadband optical amplifier and tunable laser. (c) 2006 Elsevier Ltd. All rights reserved.

Fluorescent Ag nanoclusters in glass induced by an infrared femtosecond laser

We report a method for the selective introduction of fluorescent Ag nanoclusters in glass. Extinction and photoluminescence spectra show that a fraction of the Ag atoms are generated through femtosecond laser induced multiphoton reduction and then aggregate to form Ag nanoclusters after heat treatment. Red luminescence from the irradiated region is observed under blue or green laser excitation. The fluorescence can be attributed to interband transitions within Ag nanoclusters. This method provides a novel route to fabricate fluorescent nanomaterials in 3D transparent materials. (c) 2007 Elsevier B.V. All rights reserved.