Synthesis, structural characterization and electrical property of new oxide ion conductors: La3MMo2O12 (M = In, Ga and Al)

New series of oxides, La3MMo2O12 (M = In, Ga and Al), have been prepared by the solid-state reaction. The composition and elemental distribution were analyzed by the energy-dispersive X-ray (EDX) analysis. As determined by the X-ray diffraction (XRD), these compounds have similar crystal structures that can be indexed on a monoclinic cell at room temperature. AC impedance spectra and the DC electrical conductivity measurements in various atmospheres indicate that they are oxide ion conductors with ionic conductivities between 10(-2) and 10(-3) S/cm at 800 degrees C. The conductivity decreases in the order of La3GaMo2O12 > La3AlMo2O12 > La3InMo2O12, implying that the effect of cell volume and polarization associated with In3+, Ga3+ and Al3+ play an important role in the anion transport of these materials. The reversible phase transition was observed in all these compounds as confirmed by the differential thermal analysis (DTA) and dilatometric measurements.

A new oxide ion conductor: La3GaMo2O12

A new oxide ion conductor, La3GaMo2O12, with a bulk conductivity of 2.7 X 10(-2) S.cm(-1) at 800 degrees C in air atmosphere was prepared by the traditional solid-state reaction. The room temperature X-ray diffraction data could be indexed on a monoclinic cell with lattice parameters of a=0.5602(2) nm, b=0.3224(1) nm, c= 1.5741(1) nm, beta= 102.555(0)degrees, V=0.2775(2) nm(3) and space group Pc(7). Ac impedance measurements in various atmospheres further support that it is an oxide ion conductor. This material was stable in various atmospheres with oxygen partial pressure P(O-2) ranging from 1.0 X 10(5) to 1.0 X 10(-7) Pa at 800 degrees C. A reversible polymorphic phase transition occurred at elevated temperatures as confirmed by the differential thermal analysis and dilatometric measurement.

Synthesis and fluorescence properties of Eu2+-doped KMgF3 nanoparticles

The phase diagram of a cetyltrimethyl ammonium bromide( CTAB)/n-butanol/n-octane/KNO3-Mg( NO3)(2) system was drawn. Nanoparticles of Eu2+-doped KMgF3 were prepared from the quaternary microemulsions of cetyltrimethyl ammonium bromide(CTAB), n-butanol, n-octane and water. The X-ray diffraction(XRD) patterns were indexed to a pure KMgF3 cubic phase. The environmental scanning electron microscopic (ESEM) images show the presence of spherical Eu2+-doped KMgF3 nanoparticles with a diameter of ca. 20 nm. The emission of KMgF3: Eu2+ nanoparticles peaks at 360 mn. The excitation band was observed at 250 nm with a blue shift of ca. 70 nm compared with that of KMgF3: Eu2+ single crystal. The preparation method of nano-KMgF3: Eu2+/PMMA composite films was inquired into.

Crystal structure of a noval poly(aryl ether ketone) containing meta-phenyl linkage

Crystal structure of a novel aryl ether ketone polymer poly(aryl ether ketone ether ketone ketone containing meta-phenyl linkage)(PEKEKmK) was determined by means of WAXD and ED. An orthorhombic unit cell is proposed containing two chains with a=0.772 nm, b=0.604 nm and c=2.572 nm. According to the orthorhombic system, the 10 reflections of this polymer were indexed.

Crystal structure and variation in unit cell parameters with crystallization temperatures of poly (ether ketone ether ketone ketone)s containing meta-phenyl links (PEKEKmK)

The X-ray diffraction patterns of the crystalline aromatic ketone polymer PEKEKmK (aryl ether ketone ether ketone ketone polymer containing meta-phenyl links) have been investigated (for the chemical structure, see Formula). An orthorhombic unit cell is proposed to contain two chains with a = 0.772 nm, b = 0.604 nm and c = 2.572 nm. According to the orthorhombic system, the 11 reflections of this polymer were indexed. Meanwhile, variation in unit cell parameters with crystallization temperatures of PEKEKmK was also investigated. [GRAPHICS]

Crystal structure and crystallinity of poly(aryl ether biphenyl ether ketone ketone)

The crystal structure of poly(aryl ether biphenyl ether ketone ketone) (PEDEKK) was determined to comprise a two-chain orthorhombic unit cell with dimensions a 0.778 nm, b = 0.606 nm and c = 2.375 nm by using wide-angle X-ray diffraction (WAXD). According to the orthorhombic system, the 12 reflections of this polymer were indexed. The crystallite size increases with increasing the crystallization temperature. The results of the degree of crystallinity (W-c,W-x) calculated from WAXD were compatible with those from density (W-c,W-d) and calorimetry (W-c,W-h) measurements.