Ceramic materials for thermal barrier coatings

This paper summarizes the basic properties of ceramic materials for thermal barrier coatings. Ceramics, in contrast to metals, are often more resistant to oxidation, corrosion and wear, as well as being better thermal insulators. Except yttria stabilized zirconia, other materials such as lanthanum zirconate and rare earth oxides are also promising materials for thermal barrier coatings.

Synthesis and characterization of SiO2/Gd2O3 : Eu core-shell luminescent materials

Europium-doped Gd2O3 with an average size of similar to15 nm was coated on the surface of preformed silica nanospheres by the wet chemical method. SEM and TEM photographs showed that SiO2/Gd2O3:Eu core-shell submicrospheres are obtained. XRD patterns indicated that the Gd2O3:Eu shell is crystalline after heat treatment. FTIR and XPS spectra showed that the Gd2O3:Eu shell is linked to the silica surface by forming a Si-O-Gd bond. Photoluminescence studies showed that the luminescent properties are still retained after coating on an inert silica core; additionally, we noted that the emitting peaks are broadened, which results from size effects and interface effects of nanocrystal.

In situ synthesis and characterization of multiwalled carbon nanotube/Au nanoparticle composite materials

An effective and facile in Situ reduction approach for the fabrication of carbon nanotube-supported Au nanoparticle (CNT/Au NP) composite nanomaterials is demonstrated in this article. Linear polyethyleneimine (PEI) is ingeniously used as both a functionalizing agent for the multiwalled carbon nanotubes (MWNTs) and a reducing agent for the formation of An NPs. This method involves a simple mixing process followed by a mild heating process. This approach does not need the exhaustive surface oxidation process of CNTs. The coverage of Au NPs on CNTs is tunable by varying the experimental parameters, such as the initial molar ratio of PEI to HAuCl4, the relative concentration of PEI and HAUCl(4) to MWNTs, and the temperature and duration of the heat treatment. More importantly, even the heterogeneous CNT/Au composite nanowires are obtainable through this method. TEM, XPS, and XRD are all used to characterize the CNT/Au composite materials. In addition, the optical and electrocatalytic properties are investigated.

Enhancement of molar heat capacity of nanostructured Al2O3

The nanosized alumina prepared by the hydrolysis method with an average particle size of 20 nm was characterized by X-ray diffraction. The heat capacity measurements of the prepared sample were carried out using an adiabatic calorimeter in the temperature range from 78 to 370 K. Enhancement of heat capacity was observed in the nanostructured materials as the heat capacity data were compared with those of the corresponding coarse-grained materials. The enhanced heat capacity was discussed on the basis of experiments. Differential scanning calorimetry and thermogravimetry were used to determine the thermal stability of the nanostructured alumina.

A novel method to synthesize amorphous silica-alumina materials with mesoporous distribution without using templates and pore-regulating agents

In this study, a novel sol-gel method is used to synthesize amorphous silica-alumina materials with a narrow mesoporous distribution and various Si/Al molar ratios without using any templates and pore-regulating agents. During the preparation procedure, only inexpensive inorganic salts were used as raw materials, instead of expensive and harmful alkoxides. The precursor sol was dried at room temperature in a vacuum box kept at 60 mmHg until it began to form the gel. The results of a nitrogen sorption experiment indicate that the synthesized materials with different Si/Al molar ratios have similar mesoporous distributions (within 2-12 nm). Moreover, it was found that the material's pore size distribution remains at a similar value during the heat treatment from room temperature to 550 degreesC. On the basis of the nitrogen sorption, TEM, and AFM characterization results, a formation mechanism of mesopores which accounts for the experimental data is also suggested. This suggested mechanism involves rearrangement of the primary particles during the drying process to form the precursors of the similarly sized mesopores. The synthesized materials were characterized by XRD, thermal analysis (TG/DTA), Al-27 and Si-29 MAS NMR spectroscopy, SEM, TEM, and AFM. The results of Al-27 and 29Si MAS NMR indicate that the distribution of silicon and aluminum in the synthesized materials is more uniform and homogeneous than that in the mixed oxides prepared via the traditional sol-gel method even at high alumina contents. The type and density of the acid sites were studied using pyridine adsorption-desorption FTIR spectroscopy. It was shown that the acidity of the synthesized materials is higher than that of the silica-alumina materials prepared by conventional methods.