Low temperature heat capacity and thermal stability of nanocrystalline nickel

The heat capacity (C-p) of nanocrystalline nickel (nc-Ni, 40 mn crystallite size) has been measured over the temperature range of 78-370 K with a high-resolution automated adiabatic calorimeter. The measured results are compared with the C-p values of the corresponding coarse-grained crystal, and an enhancement of heat capacity of the nanocrystalline nickel was observed to be 2-4% in the temperature range between 100 and 370 K. The thermal stability of the nanocrystalline nickel sample was determined by a differential scanning calorimeter and a thermogravimetric system. The melting point of nc-Ni is the same as that of the corresponding coarse-grained crystalline nickel and the sample is stable at temperature lower than 500 K. (C) 2002 Elsevier Science B.V. All rights reserved.

Heat capacity enhancement and thermodynamic properties of nanostructured amorphous SiO2

The heat capacity of nanostructured amorphous SiO2 (na-SiO2) has been measured by adiabatic calorimetric method over the temperature range 9-354 K. TG and differential scanning calorimeter (DSC) were also employed to determine the thermal stability. Glass transition temperature (T-g) for the two same grain sizes with different specific surface of naSiO(2) samples and one coarse-grained amorphous SiO2 (ca-SiO2) sample were determined to be 1377, 1397 and 1320 K, respectively. The low temperature experimental results show that there are significant heat capacity (C-P) enhancements among na-SiO2 samples and ca-SiO2. Entropy, enthalpy, Gibbs free energy and Debye temperature (theta (D)) were obtained based on the low temperature heat capacity measurement of na-SiO2. The Cp enhancements of na-SiO2 were discussed in terms of configurational and vibrational entropy. (C) 2001 Elsevier Science B.V. All rights reserved.

Enhancement of molar heat capacity of nanostructured Al2O3

The nanosized alumina prepared by the hydrolysis method with an average particle size of 20 nm was characterized by X-ray diffraction. The heat capacity measurements of the prepared sample were carried out using an adiabatic calorimeter in the temperature range from 78 to 370 K. Enhancement of heat capacity was observed in the nanostructured materials as the heat capacity data were compared with those of the corresponding coarse-grained materials. The enhanced heat capacity was discussed on the basis of experiments. Differential scanning calorimetry and thermogravimetry were used to determine the thermal stability of the nanostructured alumina.