Early ontogeny of Ancherythroculter nigrocauda and effects of delayed first feeding on larvae

Development of embryos and larvae in Ancherythroculter nigrocauda Yih et Woo (1964) and effects of delayed first feeding on larvae were observed after artificial fertilization. The fertilized eggs were incubated at an average temperature of 26.5 degrees C (range: 25.7-27) and the larvae reared at temperatures ranging from 21.8 to 28 degrees C. First cleavage was at 50 min, epiboly began at 7 h 5 min, heartbeat reached 72 per min at 24 h 40 min and hatching occurred at 43 h 15 min after insemination. Mean total length of newly hatched larvae was 4.04 +/- 0.03 mm (n = 15). A one-chambered gas bladder was observed at 70 h 50 min, two chambers occurred at 15 days, and scales appeared approximately 30 days after hatching. Larvae began to feed exogenously at day 4 post-hatch at an average temperature of 24 degrees C. Food deprivation resulted in a progressive atrophy of skeletal muscle fibres, deterioration of the larval digestive system and cessation of organ differentiation. Larval growth under food deprivation was significantly affected by the time of first exogenous feeding. Starved larvae began to shrink, with negative growth from day 6 post-hatch. The point of no return (PNR) was reached at day 11 after hatching. Mortality of starved larvae increased sharply from day 12 after hatching.

Influences of quantum noises on direct-modulated properties of 1.3-mu m InGaAsP/InP laser diodes

Due to the zero dispersion point at 1.3-mu m in optical fibres, 1.3-mu m InGaAsP/InP laser diodes have become main light sources in fibre communication systems recently. In fluences of quantum noises on direct-modulated properties of single-mode 1.3-mu m InGaAsP/InP laser diodes are investigated in this article. Considering the carrier and photon noises and the cross-correlation between the two noises, the power spectrum of the photon density and the signal-to-noise ratio (SNR) of the direct-modulated single-mode laser system are calculated using the linear approximation method. We find that the stochastic resonance (SR) always appears in the dependence of the SNR on the bias current density, and is strongly affected by the cross-correlation coeffcient between the carrier and photon noises, the frequency of modulation signal, and the photon lifetime in the laser cavity. Hence, it is promising to use the SR mechanism to enhance the SNR of direct-modulated InGaAsP/InP laser diodes and improve the quality of optical fibre communication systems.

Polarization properties of elliptical core non-hexagonal symmetry polymer photonic crystal fibre

In this paper, polarization properties and propagation characteristics of polymer photonic crystal fibres with elliptical core and non-hexagonal symmetry structure are investigated by using the full vectorial plane wave method. The results how that the birefringence of the fibreis induced by asymmetries of both the cladding and the core. Moreover, by adjusting the non-symmetrical ratio factor of cladding eta from 0.4 to 1 in step 0.1, we find the optimized design parameters f the fibre with high birefringence and limited polarization mode dispersion, operating in a single mode regime at an appropriate wavelength range. The range of wavelength approaches the visible and near-infrared which is consistent with the communication windows of polymer optical fibres.

A four-phase confocal elliptical cylinder model for predicting the effective thermal conductivity of coated fibre composites

A four-phase confocal elliptical cylinder model is proposed from which a generalised self-consistent method is developed for predicting the thermal conductivity of coated fibre reinforced composites. The method can account for the influence of the fibre section shape ratio on conductivity, and the physical reasonableness of the model is demonstrated by using the fibre distribution function. An exact solution is obtained for thermal conductivity by applying conformal mapping and Laurent series expansion techniques of the analytic function. The solution to the three-phase confocal elliptical model, which simulates composites with idealised fibre-matrix interfaces, is arrived at as the degenerated case. A comparison with other available micromechanics methods, Hashin and Shtrikman's bounds and experimental data shows that the present method provides convergent and reasonable results for a full range of variations in fibre section shapes and for a complete spectrum of the fibre volume fraction. Numerical results show the dependence of the effective conductivities of composites on the aspect ratio of coated fibres and demonstrate that a coating is effective in enhancing the thermal transport property of a composite. The present solutions are helpful to analysis and design of composites.

活性炭纤维(ACF)吸附法处理河流突发污染事故模拟研究

环境突发污染事故给人民生活、经济发展和生态环境造成重大影响，研究污染物泄漏造成河流突发污染事故的应急处理方法十分必要。本论文选取苯酚、苯胺和亚甲基蓝等典型污染物为实验对象，采用吸附容量大、密度与水接近的活性炭纤维(ACF)为吸附剂。在自制的河流模型中，研究了ACF以苯酚、苯胺和亚甲基蓝为典型污染物的吸附过程，考察了吸附剂投加量、污染物浓度、吸附剂比表面积、吸附剂投加方式、水流速度与水质等对吸附速率与吸附效果的影响。实验结果表明，ACF能以较快的速率吸附苯酚、苯胺和亚甲基蓝，吸附率都在95％以上； ACF投加量是影响吸附速率最重要的因素，当一次性投加ACF质量之比为 1:2:4时，吸附速率常数之比近似为1:2:4；污染物浓度对吸附速率的影响显著，浓度较低时吸附速率较高。苯酚初始浓度为7mg·L-1时，经过86分钟的吸附，处理后的浓度可以达到地表水Ⅴ类水中挥发酚的限值要求(0.1mg·L-1)；在吸附11分钟左右追加适量的ACF，能够明显提高吸附速率；河水流速和河流中的天然有机物、浊度、河水硬度对ACF吸附都不产生显著影响，这说明ACF作为河流突发污染事故应急处理的吸附剂，有广泛的适应性。在实际河水中，ACF对苯酚的吸附过程与在模拟河水中相似，吸附效果显著。实验结果还表明，ACF对苯酚的吸附是放热反应，符合Freundlich模型和Langmuir模型。事故应急处理后，应该及时将吸附了污染物的ACF打捞上来，有利于进行后续处理。 Emergency environmental pollution accidents pose significant impacts on our living, economic development and ecological environment. The study on the approach of emergency control for the contingency caused by leakage of pollutants in rivers is very necessary. In the experiment, phenol, aniline and methylene blue were selected as representative pollutant and activated carbon fiber (ACF) was selected as adsorbent, which has strong adsorption capacity and similar density to water. In the self-made river model, the effects of ACF dosage, pollutant concentration, ACF surface area, ACF adding ways, water flow rate and water quality on adsorption courses were investigated. The experimental results showed that ACF could adsorb pollutant quickly and effectively. The ACF dosage was the most important factor that affected adsorption rate .When the ACF dosage rate was 1:2:4, the constants of adsorption rate was approximately 1:2:4. The effect of pollutant concentrations on the adsorption rate was notable. Faster adsorption rates were achieved at low pollutant concentrations. Phenol concentration reached the limits of volatile phenol in Category Ⅴ surface water (0.1 mg·L-1) after 86 minutes of adsorption with initial phenol concentration of 7 mg·L-1. After 11 minutes of adsorption, certain amount of ACF was added and the adsorption rate was improved significantly. River flow rate and water quality have little effect on the adsorption rate. The adsorption results obtained in actual river water were comparable with that in simulating river water. The results also showed that, ACF on the absorption of phenol is exothermic reaction, witch matched with the Freundlich model and the Langmuir model. After emergency treatment, the ACF absorbed pollutants should be promptly salvaged for follow-up treatment.

Morphology observation of carbon deposition by CH4 decomposition over Ni-based catalysts

We found a novel morphology variation of carbon deposition derived from CH4 decomposition over NI-based catalysts. By altering the chemical composition and particle size of Ni-based catalysts, carbon filaments, nanofibres and nanotubes were observed over conventional Ni/y-Al2O3, Ni-Co/gamma-Al2O3 and nanoscale Ni-Co/gamma-Al2O3 catalysts, respectively. The simple introduction of Co into a conventional Ni/gamma-Al2O3 catalyst can vary the carbon deposition from amorphous filamentous carbon to ordered carbon fibres. Moreover, carbon nanotubes with uniform diameter distribution can be obtained over nanosized Ni-Co/gamma-Al2O3 catalyst particles. In addition, the oxidation behaviour of the different deposited carbon was studied by using a temperature-programmed oxidation technique. This work provides a simple strategy to control over the size and morphology of the carbon deposition from catalytic decomposition of CH4.

The effect of formulated molecular weight on temperature resistance and mechanical properties in polyimide based composites

This experimental study examines the role of formulated molecular weight between crosslink sites on the temperature resistance and mechanical properties of composites based on a polyimide containing a diphenyl thioether unit (PTI). The composites are fabricated by in situ polymerization of monomer reactants (PMR) using three monomeric ingredients: bis(3,4-dicarboxyphenyl) sulfide dianhydride (TDPA); 4,4'-methylene dianiline (MDA); and the monomethyl ester of norbornene anhydride (NE). By changing monomeric molar ratio, three formulations are prepared, in which formulated molecular weight between crosslink sites varies from 1487 to 3446 g mol(-1). Unidirectional composite laminates from each formulation and T300 carbon fibres are compression moulded and cut into a series of test specimens. By measuring the glass transition temperature (T-g), Mode I interlaminar fracture toughness (G(IC)) and other mechanical properties at room and elevated temperatures, the influences of formulated molecular weight on the temperature resistance and mechanical properties of PTI-based composites are investigated.

Synthesis and characterization of aromatic liquid crystalline poly(ester-imide)s derived from an imidodicarboxylic acid

A new class of liquid crystalline poly(ester-imide)s was synthesized by melt polycondensation. The basic physical properties of the resulting polymers were investigated by differential scanning calorimetry (d.s.c.), wide-angle X-ray diffraction (WAXD), polarized light microscopy, scanning electron microscopy (SEM), thermogravimetric analysis (t.g.a.), and rheological and mechanical testing. All of these poly(ester-imide)s were amorphous, as reflected by the results obtained from the WAXD and d.s.c. studies. Characterization and comparison of these poly(ester-imide)s with the corresponding polyesters suggested that the introduction of imide groups into the polyester chain is favourable for the formation of liquid crystalline phases. These results, together with the rheological studies, suggested that there existed a form of strong inter- or intramolecular electron donor-acceptor interaction which played a significant role in the liquid crystalline properties of the poly(ester-imide)s. The polymer products thus obtained exhibited good mechanical properties, with flexural strengths and moduli as high as 174 MPa and 6.9 GPa, respectively. The morphology of the fracture surfaces of extruded rod samples showed a sheet-like structure which consisted of ribbons and fibres oriented along the flow direction. The glass transition temperatures and thermal stabilities of the polymers were improved by the incorporation of imide groups. Copyright (C) 1996 Elsevier Science Ltd.

CRYSTAL-STRUCTURE AND THERMODYNAMIC PARAMETERS OF NYLON-1010

WAXD, SAXS, FTIR, DSC and density techniques have been used to investigate the crystal structure, crystal density rho(c), amorphous density rho(a), equilibrium heat of fusion DELTAH(m)degrees and equilibrium melting temperature T(m)degrees. By extrapolating the straight lines in the FTIR absorbance against density plot to zero intensity, rho(c) and rho(a) were estimated to be 1.098 and 1.003 g/cm3 respectively. The rho(c) obtained was too low in value. From X-ray diffraction patterns of uniaxially oriented fibres, the crystal structure of Nylon-1010 was determined. The Nylon-1010 crystallized in the triclinic system, with lattice dimensions: a = 4.9 angstrom, b = 5.4 angstrom, c = 27.8 angstrom, alpha = 49-degrees, beta = 77-degrees, gamma = 63.5-degrees. The unit cell contained one monomeric unit, the space group was P1BAR, and the correct value of rho(c) was 1.135 g/cm3. The degree of crystallinity of the polymer was determined as about 60% (at RT) using Ruland's method. SAXS has been used to investigate the crystalline lamellar thickness, long period, transition zone, the specific inner surface and the electron density difference between the crystalline and amorphous regions for Nylon-1010. The analysis of data was based upon a one-dimensional electron-density correlation function. DELTAH(m)degrees was estimated to be 244.0 J/g by extrapolation of DELTAH(m)degrees in the plot of heat of fusion against specific volume of semicrystalline specimens to the completely crystalline condition (V(sp)c = 1/rho(c)). Owing to the ease of recrystallization of melt-crystallized Nylon-1010 specimens, the well-known Hoffman's T(m)-T(c) method failed in determining T(m)degrees and a Kamide double extrapolation method was adopted. The T(m)degrees value so obtained was 487 K.