The influence of nitrogen clustering effect on optical transitions in GaInNAs/GaAs quantum wells

Photoluminescence (PL) spectra of GaInNAs/GaAs multiple quantum wells and GaInNAs epilayers grown on GaAs substrate show an apparent "S-shape" temperature-dependence of the of dominant luminescence peak. At low temperature and weak excitation conditions, a PL peak related to nitrogen cluster-induced bound states can be well resolved in the PL spectra. It displays a remarkable red shift of up to 60 meV and is thermally quenched below 100 K with increasing temperature, being attributed to N-cluster induced bound states. The indium incorporation exhibits significant effect on the cluster formation. The rapid thermal annealing treatment at 750 C can essentially remove the bound states-induced peak.

Influence of nitrogen implantation into the buried oxide on the radiation hardness of silicon-on-insulator wafers

摘要: In order to improve the total-dose radiation hardness of the buried oxide of separation by implanted oxygen silicon-on-insulator wafers, nitrogen ions were implanted into the buried oxide with a dose of 10(16)cm(-2), and subsequent annealing was performed at 1100 degrees C. The effect of annealing time on the radiation hardness of the nitrogen implanted wafers has been studied by the high frequency capacitance-voltage technique. The results suggest that the improvement of the radiation hardness of the wafers can be achieved through a shorter time annealing after nitrogen implantation. The nitrogen-implanted sample with the shortest annealing time 0.5 h shows the highest tolerance to total-dose radiation. In particular, for the 1.0 and 1.5 h annealing samples, both total dose responses were unusual. After 300-krad(Si) irradiation, both the shifts of capacitance-voltage curve reached a maximum, respectively, and then decreased with increasing total dose. In addition, the wafers were analysed by the Fourier transform infrared spectroscopy technique, and some useful results have been obtained.