Crack growth by grain boundary cavitation in the transient and extensive creep regimes

Crack growth due to cavity growth and coalescence along grain boundaries is analyzed under transient and extensive creep conditions in a compact tension specimen. Account is taken of the finite geometry changes accompanying crack tip blunting. The material is characterized as an elastic-power law creeping solid with an additional contribution to the creep rate arising from a given density of cavitating grain boundary facets. All voids are assumed present from the outset and distributed on a given density of cavitating grain boundary facets. The evolution of the stress fields with crack growth under three load histories is described in some detail for a relatively ductile material. The full-field plane strain finite element calculations show the competing effects of stress relaxation due to constrained creep, diffusion and crack tip blunting. and of stress increase due to the instantaneous elastic response to crack growth. At very high crack growth rates the Hui-Riedel fields dominate the crack tip region. However. the high growth rates are not sustained for any length of time in the compact tension geometry analyzed. The region of dominance of the Hui-Riedel field shrinks rapidly so that the near-tip fields are controlled by the HRR-type field shortly after the onset of crack growth. Crack growth rates under various conditions of loading and spanning the range of times from small scale creep to extensive creep are obtained. We show that there is a strong similarity between crack growth history and the behaviour of the C(t) and C(t) parameters. so that crack growth rates correlate rather well with C(t) and C(t). A relatively brittle material is also considered that has a very different near-tip stress field and crack growth history.

Laser Guiding in the Randomicity of Discrete Surface Strengthening by Arc Discharge

Several discharge areas by laser-guided discharge (LGD) were compared with those by common arc discharge. The randomicity of discharge areas by common arc discharge was controlled by laser guiding on two scales: large scale (the spacing of the discharge areas) and small scale (the inside of the discharge area). The position of the discharge area overlapped completely with a laser focus; therefore, the distribution and surface shape of the discharge areas were controlled. The stochastic movement of anode spot in the discharge area was controlled by laser guiding. As such, the repetitive melting and solidifying of microstructures in the discharge area was constrained. The tempered microstruc- tures in the discharge area were voided, the utilization efficiency of input energy was improved, and the strengthened depth of the discharge areas was increased. The regularity of cross-sectional shape of the discharge area was also improved. The hardness of microstructures in both discharge areas is greater than that of the base material. The highest level of hardness of microstructures in both discharge areas measures above 1000 HV. In summary, the hardness ofmicrostructures in the discharge area by LGD is larger and more discrete than that by common arc discharge.

Growth, characterization and optical quality of CaF2 single crystals grown by the temperature gradient technique

The CaF2 single crystals with diameters up to 200 mm were successfully grown by modified temperature gradient technique (TGT), which are suitable for application as optical elements in the ultraviolet range. The optimizations of various growth parameters were systematically studied. Properties of as-grown CaF2 crystals were characterized by the nature of inclusions, dislocations, crystallinity, and impurities contents. The results showed that the dislocations and multinucleation were mostly constrained in the conical part of the crystals with the cylindrical parts having the best crystalline quality and lowest impurity contents. The high optical quality of TGT-grown CaF2 single crystals was also confirmed to have excellent optical transmission in 190-2500 nm and refractive index homogeneity. (c) 2005 Elsevier Ltd. All rights reserved.

Impacts of a small dam on riverine zooplankton

In order to explore the temporal impacts of a small dam on riverine zooplankton, monthly samples were conducted from November 2005 to June 2006 in a reach of Xiangxi River, China, which is affected by a small hydropower plant. A total of 56 taxa of zooplankton were recorded during the study and rotifers were the most abundant group, accounting for 97% of total taxa, while the others were copepod nauplii and copepod adults. This study indicated that: (1) the small dam in the Xiangxi River study area created distinct physical and ecological conditions relative to free-flowing lotic reaches despite the constrained channel and small size of the dam; (2) the existence of the plant's small dam had a significant effect on the zooplankton community. In long periods of drought or dry seasons the effect of the dam on potamoplankton was more pronounced (e.g., November, February, March, and May). But the downfall or the connectivity of channel appeared to decrease the effect of small hydropower plants on riverine zooplankton (e.g., April). The present observation underscores the need for additional studies that provide more basic data on riverine zooplankton communities and quantify ecological responses to dam construction over longer time spans.