The investigation of exfoliation process of organic modified montmorillonite in thermoplastic polyurethane with different molecular weights

Cloisite 30B (30B) was melt-mixed with two kinds of thermoplastic polyurethane (TPU) with different molecular weights to discern the roles of molecular diffusion and shear in the exfoliation process. The higher level of exfoliation was achieved in TPU matrix with higher molecular weight due to the appropriate viscosity. In order to have an insight into the mechanism of exfoliation, the degree of dispersion and exfoliation of 30B was characterized by wide angle X-ray diffraction and transmission electron microscopy. The layers of 30B were exfoliated via a slippage process, which was also observed in polyamide 12 nanocomposites recently.

Exfoliation of Organically Modified Montmorillonite Driven by Molecular Diffusion in Maleated Polypropylene

This work is focused on the factors influencing the intercalation of maleated polypropylene (PPMA) into organically modified montmorillonite (OMMT). Two kinds of PPMA were used to explore the optimal candidate for effective intercalation into OMMT. The grafting degree of maleic anhydride and the viscosity of PPMA have effects on the diffusion of polymer molecules. Moreover, the loading level of surfactant was varied to optimize the modification of montmorillonite because the appropriate loading level can provide a balance between interlayer distance and steric hindrance. The kind of surfactant changes the interaction between OMMT and PPMA, and accordingly the intercalation of PPMA is different, resulting in the discrepancy of the intercalation of PPMA.

Effects of reinforcement filler and temperature on the stability of beta-crystal in glass bead filled polypropylene

The effects of crystallization temperature (T,), glass bead content and its size on the, formation of beta-crystal and structural stability of originally formed beta-crystal in glass bead filled polypropylene (PP) were examined. The differential scanning calorimetry (DSC) measurements indicated that the amount of beta-phase in PP crystals was a function of the crystallization temperature and glass bead content. For a constant crystallization temperature, it was observed that the amount of beta-crystal initially increased with increase in glass bead content up to 30 wt.%, and then decreased slightly with further increase in the filler content. From the DSC data, a disorder parameter (S) was derived to define the structural stability of originally formed beta-crystals. The structural stability of originally formed beta-crystals was enhanced with increase in either the crystallization temperature or the glass bead content. Also, the influence of glass bead size (4-66 mu m) on the formation and stability of beta-crystals in PP/glass bead blends was studied. Large glass bead particles suppressed the formation and decreased the stability of beta-crystals.

Relationship between the continually expanded interlayer distance of layered silicates and excess intercalation of cationic surfactants

Excess intercalation of cationic surfactants into Na-montmorillonites (MMTs) was investigated in organically modified silicates (OMSs), synthesized with MMTs and octadecylammonium chloride (OAC) by systematically varying the surfactant loading level from 0.625 to 1, 1.25, 1.56, 2, and 2.5 with respect to the cation exchange capacity (CEC) of MMTs. Wide-angle X-ray diffraction and thermogravimetric analysis results indicated that the continuous increase of interlayer distances came from the entering of surfactants into the interlayer of MMTs. Excess surfactants were extracted with a Soxhlet apparatus, which showed two kinds of intercalation states of surfactants in the interlayer when the surfactant loading level was beyond the CEC. Fourier transform infrared spectroscopy and differential scanning calorimetry were used to explore the microstructures of OMSs. It was found that the surfactants arranged more orderly as the loading level increased and the excess surfactants piled up in the interlayer together with counterions, forming a sandwiched surfactant layer. On the basis of the results, the layer structures of OMSs and the mechanism by which the surfactants entered the interlayer were expounded: surfactant cations entered the interlayer through cation exchange reactions and were tightly attracted to the silicate platelet surfaces when the surfactant loading level was below the CEC;

A Simple Method for Preparing Carbon Nanotubes/Clay Hybrids in Water

A simple novel method for preparing multiwalled carbon nanotubes/montmorillonite (MWNTs/MMT) hybrids has been established through mixing pristine MWNTs in MMT aqueous dispersion. The principle of this method is based on the formation of stable dispersion containing both MWNTs and MMT in water, which results from strong interaction between MWNTs and MMT platelets. Sedimentation experiments, measurements of potential, and Raman spectra have been used to confirm the presence of strong interaction between MWNTs and MMT sheets. The morphology observation for the dried MWNTs/MMT hybrids shows that the obtained hybrids are homogeneous, in which MWNTs exist as the state of single nanotubes that are absorbed on the surface and edge of MMT sheets.

Isothermal Crystallization Behavior of Poly(L-lactic acid)/Organo-Montmorillonite Nanocomposites

The isothermal crystallization behavior of poly(L-lactic acid)/organo-montmorillonite nanocomposites (PLLA/OMMT) with different content of OMMT, using a kind of twice-functionalized organoclay (TFC), prepared by melt intercalation process has been investigated by optical depolarizer. In isothermal crystallization from melt, the induction periods (t(i)) and half times for overall PLLA crystallization (100 degrees C <= T-c <= 120 degrees C) were affected by the temperature and the content of TFC in nanocomposites. The kinetic of isothermal crystallization of PLLA/TFC nanocomposites was studied by Avrami theory. Also, polarized optical photomicrographs supplied a direct way to know the role of TFC in PLLA isothermal crystallization process. Wide angle X-ray diffraction (WAXD) patterns showed the nanostructure of PLLA/TFC material, and the PLLA crystalline integrality was changed as the presence of TFC. Adding TFC led to the decrease of equilibrium melting point of nanocomposites, indicating that the layered structure of clay restricted the full formation of crystalline structure of polymer.

Polyampholytes superabsorbent nanocomposites with excellent gel strength

A series of novel polyampholyte superabsorbent nanocomposites with excellent gel strength were synthesized by in situ solution polymerization in aqueous solution. Acrylic acid and acryloyloxyethyl trimethyl ammonium chloride (DAC) were employed as ionic monomers and montmorillonite (MMT) was used as inorganic component. The addition of cationic component could supply the positive charge in the network of nanocomposite and promote the formation of nanostructure of composites due to the interaction between DAC and clay platelets. The performance of polyampholyte nanocomposites were investigated and the result showed that the gel strength of nanocomposite hydrogel in distilled water and 0.9 wt% NaCl solution could reach 198.85 and 204.23 mJ/g, respectively, which were 13 times of the gel strength of matrix. The investigation of swelling behaviors showed that the nanocomposites had particular swelling behaviors of polyampholytes hydrogel in solution with different pH values and concentration of NaCl.

Biodegradable poly(L-lactide)/poly(epsilon-caprolactone)-modified montmorillonite nanocomposites: Preparation and characterization

New nanocomposites were prepared by melt blending poly(L-lactide) (PLLA), poly(epsilon-caprolactone) (PCL), and organically modified montmorillonite (OMMT). The obtained nanocomposites showed enhanced tensile strength, modulus and elongation at break than that of PLLA/PCL blends. The dynamic mechanical analysis showed the increasing mechanical properties with temperature dependence of nanocomposites. Wide-angle X-ray diffraction analysis and transmission electron microscopy indicated that the material formed the nanostructure. Adding OMMT improved the thermal stability and crystalline abilities of nanocomposites. The morphology was investigated by environmental scanning electron microscopy, which showed that increasing content of OMMT reduces the domain size of phase-separated particles. The specific interaction between each polymer and OMMT was characterized by the Flory-Huggins interaction parameter, B, which was determined by the equilibrium melting point depression of nanocomposites. The final values of B showed that PLLA was more compatible with OMMT than PCL.

In situ synthesis of silica gel nanowire/Na+-montmorillonite nanocomposites by the sol-gel route

Silica-gel nanowire/Na+-montmorillonite (Na+-MMT) nanocomposites were prepared by the in situ sol-gel process of tetraethyl orthosilicate (TEOS) in the presence of Na+-MMT and ammonia as catalyst. Microstructure characterization of the nanocomposites was done by SEM, , EDX, XRD and FTIR. It was found that a lot of silica-gel nanowires grew along the edges of Na+-MMT. The combination between the nanowires and Na+-MMT was accomplished via polycondensation of the hydrolyzed TEOS and the edge-OH groups of Na+-MMT.

Synthesis and characterization of polypropylene/montmorillonite nanocomposites via an in-situ polymerization approach

Polypropylene/montmorillonite (PP/MMT) nanocomposites were prepared by in-situ polymerization using a MMT/MgCl2/TiCl4-EB Ziegler-Natta catalyst activated by trietbylaluminum (TEA). The enlarged layer spacing of MMT was confirmed by X-ray wide angle diffraction (WAXD), demonstrating that MMT were intercalated by the catalyst components. X-ray photoelectron spectrometry (XPS) analysis proved that TiCl4 was mainly supported on MgCl2 instead of on the surface of MMT The exfoliated structure of MMT layers in the PP matrix of PP/MMT composites was demonstrated by WAXD patterns and transmission electron microscopy (TEM) observation. The higher glass transition temperature and higher storage modulus of the PP/MMT composites in comparison with pure PP were revealed by dynamic mechanical analysis (DMA).

Tensile modulus of polymer nanocomposites

Based on Takayanagi's two-phase model, a three-phase model including the matrix, interfacial region, and fillers is proposed to calculate the tensile modulus of polymer nanocomposites (E-c). In this model, fillers (sphere-, cylinder- or plate-shape) are randomly distributed in a matrix. If the particulate size is in the range of nanometers, the interfacial region will play an important role in the modulus of the composites. Important system parameters include the dispersed particle size (t), shape, thickness of the interfacial region (tau), particulate-to-matrix modulus ratio (E-d/E-m), and a parameter (k) describing a linear gradient change in modulus between the matrix and the surface of particle on the modulus of nanocomposites (E-c). The effects of these parameters are discussed using theoretical calculation and nylon 6/montmorillonite nanocomposite experiments. The former three factors exhibit dominant influence on E-c At a fixed volume fraction of the dispersed phase, smaller particles provide an increasing modulus for the resulting composite, as compared to the larger one because the interfacial region greatly affects E-c. Moreover, since the size of fillers is in the scale of micrometers, the influence of interfacial region is neglected and the deduced equation is reduced to Takayanagi's model. The curves predicted by the three-phase model are in good agreement with experimental results. The percolation concept and theory are also applied to analyze and interpret the experimental results.

Preparation and characterization of poly(ethyl acrylate)/bentonite nanocomposites by in situ emulsion polymerization

Transparent poly(ethyl acrylate) (PEA)/bentonite nanocomposites containing intercalated-exfoliated combinatory structures of clay were synthesized by in situ emulsion polymerizations in aqueous dispersions containing bentonite. The samples for characterization were prepared through direct-forming films of the resulting emulsions without coagulation and separation. An examination with X-ray diffraction and transmission electron microscopy showed that intercalated and exfoliated structures of clay coexisted in the PEA/bentonite nanocomposites. The measurements of mechanical properties showed that PEA properties were greatly improved, with the tensile strength and modulus increasing from 0.65 and 0.24 to 11.16 and 88.41 MPa, respectively. Dynamic mechanical analysis revealed a very marked improvement of the storage modulus above the glass-transition temperature. In addition, because of the uniform dispersion of silicate layers in the PEA matrix, the barrier properties of the materials were dramatically improved. The permeability coefficient of water vapor decreased from 30.8 x 10(-6) to 8.3 x 10(-6) g cm/cm(2)s cmHg. (C) 2002 Wiley Periodicals, Inc.

Research on Bearing Capacity Calculation Method of Large Diameter Cylinder in Soft Clay

A large diameter cylinder inserted in soils is a new type of engineering structures used in offshore and port engineering. The mechanism of its bearing capacity and the analysis of its stability are important to its design and applications. In this paper, the finite element method is used to analyze the reacting forces of the soft soil foundation on the structure under the wave action. A simplified method is proposed, based on the plastic limit method, for the safety and stability analysis. Our analysis shows that the assumptions made in this paper and the mechanism used are reasonable, and the results obtained are appropriate. The calculation method is very efficient and can be used to evaluate main parameters of the structure in its preliminary designs.

Post-cyclic Strength Degradation of Undisturbed and Remolded Marine Silty Clay

A series of static and cyclic-static tri-axial compression tests under consolidated-undrained conditions are carried out to study the characteristics of post-cyclic strength of the undisturbed and the remolded samples of marine silty clay. It is found that the post-cyclic monotonic strength decreases if the cyclic strain or pore pressure is over a certain value. The maximum degradation is 10% for undisturbed samples while 70% for remolded ones. The relationship between normalized undrained shear strength and apparent overconsolidation ratio, which is determined by the excess pore pressure induced by cyclic loading, is also established. Static consolidated-undrained tests on overconsolidated remolded samples are also performed. It is proposed that the static consolidated-undrained tests may be substituted for the cyclic-static consolidated-undrained tests if the post-cyclic strength degradation of remolded silty clay is needed to be evaluated simply.

Transparent and Light-Emitting Epoxy Super-Nanocomposites Containing ZnO-QDs/SiO2 Nanocomposite Particles as Encapsulating Materials for Solid-State Lighting

In this article, the ZnO quantum dots-SiO2 (Z-S) nanocomposite particles were first synthesized. Transparent Z-S/epoxy super-nanocomposites were then prepared by introducing calcined Z-S nanocomposite particles with a proper ratio of ZnO to SiO2 into a transparent epoxy matrix in terms of the filler-matrix refractive index matching principle. It was shown that the epoxy super-nanocomposites displayed intense luminescence with broad emission spectra. Moreover, the epoxy super-nanocomposites showed the interesting afterglow phenomenon with a long phosphorescence lifetime that was not observed for ZnO-QDs/epoxy nanocomposites. Finally, the transparent and light-emitting Z-S/epoxy super-nanocomposites were successfully employed as encapsulating materials for synthesis of highly bright LED lamps.