The study on the interface adhesion comparison of the MgF2, Al2O3, SiO2 and Ag thin films

Adhesion between the interface of pure silver thin film and three kinds of low refractive index coatings MgF2, Al2O3, SiO2 were compared in this article. The results indicated that the adhesion of Al2O3 and Ag was evidently superior to that of MgF2 and Ag, and the adhesion of MgF2 and Ag was evidently superior to that Of SiO2 and Ag. Reasons were analyzed accordingly. On the other hand, we compared the effect on the optical characteristic of Ag film when these three kinds of films were used as protective coatings and enhanced coatings. Considering the difference of the adhesion between Ag and MgF2, Al2O3, SiO2, suited uses are given for each other. © 2004 Elsevier B.V. All rights reserved.

Influence of Cr interlayer on the structure and optical properties of Ag films on glass substrate by magnetron sputtering

Optical properties and microstructure of Ag film on glass substrate with Cr intermediate layer were studied by using spectrophotometer and XRD. The spectra results showed that introducing Cr intermediate layer reduced the surface roughness and promoted the reflectivity of Ag film. The XRD analysis showed that the crystalline grains increased and the stress decreased. The adhesion was also improved by using the tape test method. (c) 2006 Published by Elsevier B.V.

Effect of alumina and chromium interlayers on microstructures and optical properties of thin Ag films on glass substrates

Effects of alumina and chromium interlayers on the microstructure and optical properties of thin Ag films are investigated by using spectrophotometry, x-ray diffraction and AFM. The characteristics of Ag films in Ag/glass, Ag/Al2O3/glass and Ag/Cr/glass stacks are analysed. The results indicate that the insertion of an Al2O3 or Cr layer decreases the grains and influences the reflectance of Ag films. The reflectance of the Ag film can be increased by controlling the thickness of alumina interlayer. The stability of Ag films is improved and the adhesion of Ag films on glass substrates is enhanced by alumina as an interlayer.

Al2O3和Cr过渡层对Ag膜光学性质及其附着力的影响

研究了在玻璃基底上镀制Al2O3和Cr过渡层对Ag膜反射率及附着力的影响.分光光度计测试了Ag膜的反射率,结果表明,与Cr过渡层相比,Al2O3过渡层对Ag膜反射率的降低相对较小;而且,随着Al2O3厚度的增加,Ag膜的反射率先增大后减小.XRD与AES测试表明,引入Al2O3或Cr可明显细化Ag晶粒,减弱Ag膜（111）织构;Al2O3作过渡层时,Al原子向Ag层中扩散显著;而Cr作过渡层时,只有少量Cr原子扩散进入Ag层.因此,Al2O3作过渡层能显著增强薄膜与玻璃基体之间的附着力.