Synthesis of a high-permeance NaA zeolite membrane by microwave heating

Zeolite membranes with high permeance and separation factors are highly desirable for practical applications. Although, in the past, very good separation factors have been obtained, it has proved difficult to achieve a high permeance. Ken a comparative study of microwave versus conventional heating in the hydrothermal synthesis of NaA zeolite membranes is made. It is demonstrated that membranes prepared by microwave heating have not only a higher permeance but also a considerably shorter synthesis time. These observations are rationalized by examining the mechanism of membrane formation.

Investigation of ideal zirconium-doped perovskite-type ceramic membrane materials for oxygen separation

Zirconium-doped perovskite-type membrane materials of BaCo0.4Fe0.6-xZrxO3-delta (x = 0-0.4) with mixed oxygen ion and electron conductivity were synthesized through a method of combining citric and EDTA acid complexes. The results of X-ray diffraction (XRD), oxygen temperature-programmed desorption (O-2-TPD) and hydrogen temperature-programmed reduction (H-2-TPR) showed that the incorporation of proper amount of zirconium into BaCo0.4Fe0.6O3-delta could stabilize the ideal and cubic structure of perovskite. Studies on the oxygen permeability of the as-synthesized membrane disks under air/He gradient indicated that the content of zirconium in these materials had great effects on oxygen permeation flux, activation energy for oxygen permeation and operation stability. The high oxygen permeation flux of 0.90 ml cm(-2) min(-1) at 950degreesC, the single activation energy for oxygen permeation in the range of 600-950 degreesC and the long-term operation stability at a relatively lower operational temperature of 800 degreesC under air/He gradient were achieved for the BaCo0.4Fe0.4Zr0.2O3-delta material. Meanwhile, the effect of carbon dioxide on structural stability and oxygen permeability of this material was also studied in detail, which revealed that the reversible stability could be attained for it. (C) 2002 Elsevier Science B.V. All rights reserved.

Synthesis of NaA zeolite membrane by microwave heating

The synthesis of NaA zeolite membrane on a porous alpha -Al2O3 support by microwave heating (MH) was investigated. The formation of a NaA zeolite membrane was drastically promoted by MH. The synthesis time was reduced from 3 h for conventional heating (CH) to 15 min for MH. Surface seeding cannot only promote the formation of NaA zeolite on the support, but also inhibit the transformation of NaA zeolite into other types of zeolites. The thickness of the NaA zeolite membrane synthesized by MH was about 4 mum, thinner than that of NaA zeolite membrane synthesized by CH. The permeance of NaA zeolite membrane synthesized by MH was four times higher than that of the NaA zeolite membrane synthesized by CH, while their permselectivities were comparable. Multi-stage synthesis resulted in the transformation of NaA zeolite into other types of zeolites, and the perfection of the as-synthesized membrane decreased.

Synthesis and perfection evaluation of NaA zeolite membrane

The synthesis of NaA zeolite membrane on a porous alpha -Al2O3 support from clear solution and the evaluation of the perfection of the as-synthesized membrane by gas permeation were investigated. When an unseeded support was used, the NaA zeolite began to transform into other types of zeolites before a continuous NaA zeolite membrane formed. When the support was coated with nucleation seeds, not only the formation of NaA zeolite on the support surface was accelerated, but also the transformation of NaA zeolite into other types of zeolites was inhibited. A continuous NaA zeolite membrane can be formed. Perfection evaluation indicated that the NaA zeolite membrane with the synthesis time of 3 h showed the best perfection after a one-stage synthesis. The perfection of NaA zeolite membrane can be improved by employing the multi-stage synthesis method. The NaA zeolite membrane with a synthesis time of 2 h after a two-stage synthesis showed the best gas permeation performance, The permselectivity of H-2/n-C4H10 and O-2/N-2 were 19.1 and 1.8, respectively, higher than those of the corresponding Knudsen diffusion selectivity of 5.39 and 0.94, which showed the molecular sieving effect of NaA zeolite. However, the permeation of n-C4H10 also indicated that the NaA zeolite membrane had certain defects, the diameter of which were larger than the NaA zeolite channels. (C) 2001 Elsevier Science B.V. All rights reserved.

Synthesis and characterization of gallium-based perovskite-type dense membrane with oxygen semipermeability

La0.15Sr0.85Ga0.3Fe0.7O3-delta (LSGFO) and La0.15Sr0.85Co0.3Fe0.7O3-delta (LSCFO) mixed oxygen-ion and electron conducting oxides were synthesized by using a combined EDTA and citrate complexing method, and the corresponding dense membranes were fabricated. The properties of the oxide powders and membranes were characterized with combined SEM, XRD, H-2-TPR, O-2-TPD techniques, mechanical strength and oxygen permeation measurement. The results showed that LSGFO had much higher thermochemical stability than LSCFO due to the higher valence stability of Ga3+. After the temperature-programmed reduction by 5% H-2 in Ar from 20 degreesC to 1020 degreesC, the basic perovskite structure of LSGFO was successfully preserved. LSGFO also favors the oxygen vacancy formation better than LSCFO. Oxygen permeation measurement demonstrated that LSGFO had higher oxygen permeation flux than LSCFO, but they had similar activation energy for oxygen transportation, with a value of 110 and 117 kJ . mol(-1), respectively The difference in oxygen permeation fluxes was correlated with the difference in oxygen vacancy concentrations for the two materials.

Preparation of zeolite-metal composite membrane

A NaA zeolite membrane was synthesized on the surface of the stainless steel stab. The membrane was characterized by XRD and SEM. The membrane was continuous and highly intergrown. The size of NaA zeolite crystals was about 5 similar to 6 mum.

Synthesis of NaA zeolite membranes from clear solution

NaA zeolite membranes were successfully synthesized on a porous alpha -Al2O3 support from clear solution. The synthesis parameters, such as surface seeding, synthesis time, synthesis stages, etc. were investigated. Surface seeding can not only accelerate the formation of NaA zeolite on the support surface, but can also inhibit the transformation of NaA zeolite into other types of zeolites. A continuous NaA zeolite membrane formed on the seeded support after 2 h of synthesis. Gas permeation results showed that a synthesis time of 3 h produced the best NaA zeolite membrane. When the synthesis time was longer than 4 h, the NaA zeolite on the support surface began to transform into other types of zeolites, and the quality of the NaA zeolite membrane decreased. The quality of the NaA zeolite membrane can be improved by employing the multi-stage synthesis method. The NaA zeolite membrane with a synthesis time of 2 h after a two-stage synthesis showed the best gas permeation performance. The permeances of H-2, O-2, N-2, and n-C4H10 decreased as the molecular kinetic diameter of the gases increased. which showed the molecular sieving effect of the NaA zeolite membrane. The permselectivities of H-2/n-C4H10 and O-2/N-2 were 19.1 and 1.8, respectively. These values are higher than the Knudsen diffusion ratios of 5.39 and 0.94. However, the permeation of n-C4H10 also indicated that the NaA zeolite membrane had certain defects with diameters larger than the pore size of NaA zeolite. A synthesis model was proposed to clarify the effect of surface seeding. (C) 2001 Elsevier Science B.V. All rights reserved.

On the formation of vertically oriented MCM-22 zeolite crystal films

Growth of MCM-22 zeolite films on glass substrates was studied with the focus on the understanding of the unusual vertical crystal orientation. The films formed were characterized by scanning electron microscopy and X-ray diffraction. Separate thin disk-like MCM-22 crystals were found vertically oriented at the early crystallization stage. With crystallization the crystals grew into thick disks and finally into continuous films. The vertically oriented MCM-22 thin crystals could be developed from the orientation of columnar MCM-22 nuclei, which have larger parameters in their c-directions than those in a and b directions. The preferred orientation of MCM-22 nuclei and the fast growth rate in the layer direction are responsible for the vertical growth of MCM-22 zeolite films. (C) 2001 Elsevier Science B.V. All rights reserved.

白杄花粉管微丝骨架介导信号传导的蛋白质组学研究

在高等植物有性生殖过程中，花粉管作为运输精子到胚珠的载体，它的生长具有高度极性化，并且要依赖于微丝。由于花粉管本身所具的特性，它已经成为研究细胞相互识别、胞内和胞外信号的模式系统。本文为了研究微丝在白杄（Picea meyeri Rehd. et Wils.）花粉管生长中的作用，我们应用不同浓度的微丝聚合抑制剂Latrunculin B (LATB) 处理花粉管，并通过激光共聚焦显微镜观察微丝聚合状态的动态变化。结果发现，在低浓度下的LATB能使花粉管中的微丝严重解聚，且抑制其顶端生长。 我们进一步利用蛋白质组学的手段，分析了白杄花粉管微丝解聚后蛋白质的表达图谱。通过双向电泳分离出500个左右考马斯亮兰染色的蛋白质斑点，经过软件分析发现，其中大部分蛋白质的表达量未发生变化，而只有110个蛋白斑点有较大变化。将这些蛋白斑点从胶上切下酶解后用于质谱鉴定，最终鉴定出35个蛋白，其中有18个为上调蛋白，17个下调蛋白。根据其主要功能，通常可分为碳水化合物代谢、胁迫反应、信号和细胞扩展等几类。我们发现由于微丝解聚引起的能量代谢水平降低，可能与依赖于信号传导的微丝重组过程相关。此外，当LATB浓度增加到50 nM时，与细胞壁多糖合成相关的两个蛋白，如reversibly glycosylated polypeptide和type IIIa membrane protein cp-wap13几乎不表达，这说明当微丝聚合完全被抑制后，依赖于微丝的分泌系统也受到影响，从而引起相应蛋白质变化，最终导致细胞壁成分合成的减少。细胞骨架蛋白actin的下调，进一步说明微丝在花粉管生长过程中起着提供或支持的一种机制，也就是能调节信号介导的花粉管生长，并使其在特定的时期到达特定的部位，从而完成植物的受精作用。