磷酸盐激光玻璃聚（CH3）2SiO／SiO2防潮膜改性研究

采用溶胶-凝胶方法制备的（CH2）2Si（OC2H5）2预聚体涂膜液中，掺入碱催化的SiO2悬胶体涂膜液，采用旋涂法在掺钕磷酸盐激光玻璃棒端面涂制了改性的防潮膜。当涂膜液中（CH2）2Si（OC2H5）2和SiO2物质的量之比为1：1时。热处理后的膜层耐摩擦性能明显改善；表面粗糙度的均方根值为1．245nm；膜层激光破坏阈值大于15J／cm^2（1053nm，1ns）；在80℃和95％RH的封闭环境中静置336h，膜层的透过率、接触角基本不变。结果证明膜层具有稳定的疏水结构和很好的防潮性能，膜层强度增加，

磷酸盐激光玻璃凝胶防潮膜和减反膜

采用溶胶-凝胶方法制备（CH3）2Si（OC2H5）2预聚体涂膜液以及掺入SiO2悬胶体涂膜液改性，采用旋转法在掺钕磷酸盐激光玻璃棒端面涂制防潮膜，热处理后膜层固化。SiO2改性的CH3O防潮膜，热处理后的膜层耐摩擦性能明显改善。然后旋转涂制第二层多空性SiO2减反膜，涂膜胶体通过硅酸乙脂碱催化水解缩聚制得，减反膜的折射率为约1．25，玻璃棒涂膜后激光波长1053nm减少表面反射率6．5％-7．5％，双层膜激光破坏阈值12J／cm^2，1053nm／1ns，膜层表面粗糙度（RMS）2．523nm。直径20

Optical properties and structure of Sb-rich AgInSbTe phase change thin films

A new composition content quaternary-alloy-based phase change thin film, Sb-rich AgInSbTe, has been prepared by DC-magnetron sputtering on a K9 glass substrate. After the film has been subsequently annealed at 200degreesC for 30 min, it becomes a crystalline thin film. The diffraction peak of antimony (Sb) are observed by shallow (0.5 degree) x-ray diffraction in the quaternary alloy thin film. The analyses of the measurement from differential scanning calorimetry (DSC) show that the crystallization temperature of the phase change thin film is about 190degreesC and increases with the heating rate. By Kissinger plot, the activation energy for crystallization is determined to be 3.05eV. The reflectivity, refractive index and extinction coefficient of the crystalline and amorphous phase change thin films are presented. The optical absorption coefficient of the phase change thin films as a function of photon energy is obtained from the extinction coefficient. The optical band gaps of the amorphous and crystallization phase change thin films are 0.265eV and 1.127eV, respectively.

Study on readout durability of super-RENS disk

Characteristics essential for the readout durability of a superresolution near-field structure (super-RENS) disk are studied experimentally by using a home-built optical measuring setup and atomic force microscope, based on a simplified PtOx super-RENS disk. The experimental results show that for a super-RENS disk with constant structure and materials, readout signals including transmittance and reflectance vary with changes in bubble shape and size, indicating that the readout durability of the disk has a strong dependence on bubble stability, which is closely related to the thickness of the cover layer, the recording power and readout power, and the mechanical properties of the dielectric layer. Based on our experimental results, the main direction for improving readout durability is also proposed. (c) 2008 Optical Society of America.

The intensity distribution and thermal stability of InnoSlab laser

Partially end-pumped slab laser is an innovative solid state laser, namely InnoSlab. Combining the hybrid resonator with partially end-pumping, the output power can be scaled with high beam quality. In this paper, the output intensity distributions are simulated by coordinate transformation fast Fourier transform (FFT) algorithm, comparing the thermal lens influence. As the simulated curves showed, the output mode is still good when the thermal lens effect is strong, indicating the good thermal stability of InnoSlab laser. Such a new kind of laser can be designed and optimized on the base of this simulation.

芦笋抗氨基酸及氨基酸类似物突变体的筛选

由芦笋无菌苗诱导得到的愈伤组织，经甲基磺酸乙酯（EMS）诱变处理后，进行抗氧乙基半胱氨酸(AEC)和赖氨酸加苏氨酸(Lys十Thr)的突变体筛选工作，得到如下结果: ①AE C可抑制芦笋愈伤组织的生长，但此抑制作用可被赖氨酸或甲硫氨酸都分解除。利用AEC的抑制作用筛选得到抗0.5mMAEC的愈伤组织AR10并再生植株。AR10愈伤组织离开选择剂两代后仍保持对AE C的抗性。还发现抗性愈伤组织对2mM的半胱氨酸的抑制作用具有交叉抗性，对1mM的Lys+Thr的抑制作用有较弱的交叉抗性。AR10的再生植株一部分表出对A EC的抗性，另一部分则无抗性氨基酸分析表明，抗性愈伤组织内游离赖氨酸、苏氨酸、甲硫氨酸和异亮氨酸有所增加，而在开生植株中发现了半胱氨酸和赖氨酸的特异性增加（分别是对照的4•56和5 •39倍)。AR10的抗性机理目前尚不清楚。 ②2mM的Lys十Thr Lys+Thr对芦笋愈伤组织生长具有抑制作用。甲硫氨酸可部分解除.Ly s十Thr的抑制作用。用2mM的Lys+Thr筛选得到的抗性细胞系LTR2. LTR3，在离开选择压力一代，细胞增殖五倍的情况下仍保持对选择剂的稳定抗性。LTR2、L T R3愈价组织对A E C如仰制作用表现出部分的交叉抗性。另外还发现抗性系对苏氨酸(2mM )的生长抑制作用具有抗性，对赖氨酸(2mM)的生长抑制作用却无抗性，氨基酸分析表明。LTR2LTR3愈份组织内游离赖氨酸含量明显提高(分别是对照的2•18和2.67倍)，另发现一种峰值介于赖氨酸与游离氨之间的未知氨基酸增加更为显著(分别是对照的4•03和11•42倍)。这些结果表明抗性愈伤组织内氨基酸合成的某些关键酶可能发生了改变，对末端物的反馈抑制敏感性有所降低。