Resumo:
Pyrolysis of hyperbranched poly[1,1'-ferrocenylene(methyl)silyne] (5) yields mesoporous, conductive, and magnetic ceramics (6). Sintering at high temperatures (1000-1200 degrees C) under nitrogen and argon converts 5 to 6N and 6A, respectively, in similar to 48-62% yields. The ceramization yields of 5 are higher than that (similar to 36%) of its linear counterpart poly[1,1'-ferrocenylene(dimethyl)silylene] (1), revealing that the hyperbranched polymer is superior to the linear one as a ceramic precursor. The ceramic products 6 are characterized by SEM, XPS, EDX, XRD, and SQUID. It is found that the ceramics are electrically conductive and possess a mesoporous architecture constructed of tortuously interconnected nanoclusters. The iron contents of 6 estimated by EDX are 36-43%, much higher than that (11%) of the ceramic 2 prepared from the linear precursor 1. The nanocrystals in 6N are mainly alpha-Fe2O3 whereas those in 6A are mainly Fe3Si. When magnetized by an external field at room temperature, 6A exhibits a high-saturation magnetization (M-s similar to 49 emu/g) and near-zero remanence and coercivity; that is, 6A is an excellent soft ferromagnetic material with an extremely low hysteresis loss.
Resumo:
The degradation behavior of polyimide (PMDA-ODA) induced by nitrogen laser irradiation was studied. The changes in the surface morphology and the composition of the irradiated polyimide films were examined by scanning electron microscopy, X-ray photoelectron spectroscopy and FT-IR spectroscopy. The initial reaction was achieved by photochemical degradation of polyimide in the highly electronic excited state by the absorption of a second 337 nm photon. Atmospheric oxygen sequentially reacted with the produced radicals to form a highly oxidized layer. The formation of carbonyl group was enhanced by the heat remaining on the irradiated polyimide film surfaces. (C) 2000 Elsevier Science B.V. All rights reserved.
Resumo:
4-Aminobenzoic acid (4-ABA) was covalently grafted on a glassy carbon electrode (GCE) by amine cation radical formation in the electrooxidation process of the amino-containing compound. X-ray photoelectron spectroscopy measurement proves the presence of 4-carboxylphenylamine monolayer on the GCE. The redox responses of various electroactive probes were investigated on the 4-ABA-modified GCE. Electron transfer to Fe(CN)(6)(3-) in solutions of various pHs was studied by both cyclic voltammetry and electrochemical impedance analysis on the modified electrode. Changes in the solution pH value result in the variation of the terminal group charge state, based on which surface pK(a) values are estimated. The 4-ABA-modified GCE was used as a suitable charged substrate to fabricate polyoxometalates-consisting (POM-consisting) monolayer and multilayer films through layer-by-layer assembly based on electrostatic attraction. Cyclic voltammetry shows the uniform growth of these three-dimensional multilayer films. Taking K10H3[Pr-(SiMo7W4O39)(2)]. H2O (abbreviated as Pr(SiMo7W4)(2)), for example, the preparation and electrochemical behavior of its monolayer and multilayer film had been investigated in detail. This modification strategy is proven to be a general one suitable for anchoring many kinds of POMs on the 4-ABA-modified GCE.
Resumo:
A novel 4-aminobenzoic acid (4-ABA) monolayer film is formed on glassy carbon electrode (GCE) by amino cation radical method. Silicotungstic heteropolyanion (SiW12O404-, denoted as SiW12)-containing multilayer films have been fabricated on the 4-ABA modified GCE surface by alternate deposition with a quaternized poly(4-vinylpyridine) partially complexed with [Os(bpy)(2)Cl](2+/+) (denoted as QPVP-Os). Cyclic voltammetry (CV), X-ray photoelectron spectroscopy (XPS) and X-ray reflectivity (XR) have been used to characterise the as-prepared multilayer films. It is proved that the multilayer films are uniform and stable. The average thickness for a bilayer of QPVP-Os/SiW12 in the multilayer film is 30.2 Angstrom. The electrocatalytic activities of the multilayer films have been investigated on the reduction of three substrates of important analytical interests, HNO2, BrO3- and H2O2. Especially, the influence of layer number of the multilayer films on the electrocatalytic reduction of HNO2 has been investigated in detail. (C) 2000 Elsevier Science B.V. All rights reserved.
Resumo:
The preparation, structure, and electrochemical and electrocatalytical properties of a new polyoxometalate-based organic/inorganic film, composed of cetyl pyridinum 11-molybdovanadoarsenate (CPMVA) molecules, have been studied. Cyclic potential scanning in acetone solution led to a stable CPMVA film formed on a highly oriented pyrolytic graphite (HOPG) surface. X-ray photoelectron spectroscopy, scanning tunneling microscopy, and cyclic voltammetry were used for characterizing the structure and properties of the CPMVA film. These studies indicated that self-aggregated clusters were formed on a freshly cleaved HOPG surface, while a self-organized monolayer was formed on the precathodized HOPG electrode. The CPMVA film exhibited reversible redox kinetics both in acidic aqueous and in acetone solution, which showed that it could be used as a catalyst even in organic phase. The CPMVA film remained stable even at pH > 7.0, and the pH dependence of the film was much smaller than that of its inorganic film (H4AsMo11VO40) in aqueous solution. The CPMVA film showed strong electrocatalysis on the reduction of bromate, and the catalytic currents were proportional to the square of the concentration of bromate. The new kind of polyoxometalate with good stability may have extensive promise in catalysis.
Resumo:
Polyaniline nanoparticles were prepared on a highly oriented pyrolytic graphite (HOPG) surface from dilute polyaniline acidic solution (1 mM aniline + 1 M HClO4) using a pulsed potentiostatic method. Electrochemistry, Fourier transform infrared external reflection spectroscopy (FT-IR-ERS), X-ray photoelectron spectroscopy (XPS) and tapping-mode atomic force microscopy (TMAFM) were: used to characterize the composition and structure of the polyaniline nanoparticles. FT-IR-ERS and XPS results revealed that the polyaniline was in its emeraldine form. TMAFM measurement showed that the electropolymerized polyaniline nanoparticles dispersed on the:HOPG surface with a coverage of about 10(10) cm(-2). These nanoparticles were disk-shaped having a height of 10(-30) Angstrom and an apparent diameter varying from 200 to 600 Angstrom. The particle dimensions increased with the electropolymerization charge (Q) over the interval from 5.7 to 19.3 mu C cm(-2) (C) 2000 Elsevier Science S.A. All rights reserved.
Resumo:
Multilayer films were fabricated by layer-by-layer electrostatic deposition techniques between poly(diallyIdimethylammonium chloride) (PDDA) and calf thymus DNA (CT DNA) on glassy carbon and quartz substrates. Electrochemical impedance spectroscopy (EIS), Fourier transform infrared (FTIR) spectroscopy and UV-vis spectroscopy demonstrated the uniform assembly of PDDA/DNA multilayer films, and X-ray photoelectron spectroscopy confirmed the elemental composition of the films. Moreover, the interaction of DNA in PDDA/DNA films with methyl green was investigated by UV-vis spectroscopy and circular dichroism (CD). (C) 2001 Elsevier Science B.V. All rights reserved.
Resumo:
Eu3+-activated calcium silicate (CaO-SiO2:Eu3+) luminescent films were prepared by the sol-gel method. The structural evolution of the film was studied by X-ray powder diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM), and the luminescence properties of the phosphor films were investigated as a function of heat treatment temperature. The XRD study indicates that a kilchoanite phase forms in the film sintered at 800 degreesC, which is different from that in gel powder treated under the same conditions. The SEM results show that the film thickness decreases and the particles in the film become smaller with increasing heat treatment temperature. The CaO-SiO2:Eu film shows the characteristic emission of Eu3+ under UV excitation, with the Eu3+ D-5(0)-->F-7(2) band (616 nm) being the most prominent. A large difference in the Eu3+ lifetime is observed between the film samples treated at 500 and 700 degreesC (or above). Concentration quenching occurs when the Eu3+ doping concentration is above 6 mol% of Ca2+ in the film.
Resumo:
A novel method using LB films as precursors to prepare pure inorganic ordered film with periodic structure was developed. Surfactant-stabilized SnO2 nanoparticulate organosols and TiO2 nanoparticulate organosols were prepared and used as spreading solutions. Using LB technique, the good film-forming ability of the surfactant-stabilized SnO2 nanoparticles and TiO2 nanoparticles was confirmed by the determination of the pi -A isotherms. The surfactant-stabilized SnO2 and TiO2 nanoparticulate monolayers were fabricated on the water surface and then were transferred to solid substrates (CaF2, quartz, silicon, and so on) alternately, layer-by-layer. Then the as-deposited alternate LB film was treated at different temperatures. The as-deposited alternate LB film and the treated film were characterized by Fourier transform infrared spectroscopy, UV visible spectroscopy, X-ray diffraction, and X-ray photoelectron spectroscopy. The results indicate that our method was successful. The as-deposited alternate LB film formed a periodic structure with a long spacing of 6.5 nm that was composed of SnO2 nanoparticles, TiO2 nanoparticles, and arachidic acid. The treated film composed of SnO2 nanoparticles and TiO2 nanoparticles formed a pure inorganic periodic structure with an ordered distance of 5.4 nm. (C) 2001 Academic Press.
Resumo:
A simple route to the fabrication of multilayer films containing Pd nanoparticles is described. Following layer-by-layer assembly of PdCl42- and polycation, QPVP-Os (a quaternized poly(4-vinylpyridine) complexed with [Os(bpy)(2)Cl](2+/+)), on 4-aminobenzoic acid-modified glassy carbon electrodes, the three-dimensional Pd nanoparticle multilayer films are directly formed on electrode surfaces via electrochemical reduction of PdCl42- sandwiched between polymers. The growth of PdCl42- is easy on electrode surfaces by electrostatic interaction, and the assembly processes are monitored by cyclic voltammetry and UV-vis spectroscopy. The depth profile analyses by X-ray photoelectron spectroscopy verify the constant composition of the Pd nanoparticle multilayer films. Atomic force microscopy proves that the as-prepared Pd nanoparticles are uniformly distributed with an average particle diameter of 3-7 mn. The resulting Pd nanoparticle multilayer-modified electrode possesses high catalytic activity for the reduction of dissolved oxygen and oxidation of hydrazine compounds in aqueous solution.
Resumo:
1,7-Diaminoheptane (DAH) had been covalently grafted on glassy carbon electrode by amino cation radical formation, which resulted in a stable cationic monolayer under proper pH conditions. Dawson-type tungstodiphosphate anion, P2W18O626- and small molecule, Ru(NH3)(6)(3+) were alternately assembled on the DAH modified electrode through layer-by-layer electrostatic interaction. Thus-prepared multilayer film had been characterized by cyclic voltammetry and X-ray photoelectron spectroscopy. The P2W18O626- multilayers exhibit high electrocatalytic response and sensitivity towards the reduction of iodate. With the increase of the number of P2W18O626- the catalytic current was enhanced and the catalytic potential shifted positively. Iodate in table salt was determined at the modified electrode containing three layers of P2W18O626- with satisfactory results. The multilayer electrode is promising as an electrochemical sensor for the detection of trace iodate.
Resumo:
The use of functional groups bearing silica/poly(styrene-co-4-vinylpyridine) core-shell particles as a support for a zirconocene catalyst in ethylene polymerization was studied. Several factors affecting the behavior of the supported catalyst and the properties of the resulting polymer, such as time, temperature, Al/N (molar ratio), and Al/Zr (molar ratio), were examined. The conditions of the supported catalyst preparation were more important than those of the ethylene polymerization. The state of the supported catalyst itself played a decisive role in both the catalytic behavior of the supported catalyst and the properties of polyethylene (PE). IR and X-ray photoelectron spectroscopy were used to follow the formation of the supports. The formation of cationic active species is hypothesized, and the performance of the core-shell-particle-supported zirconocene catalyst is discussed as well. The bulk density of the PE formed was higher than that of the polymer obtained from homogeneous and polymer-supported Cp2ZrCl2/methylaluminoxane catalyst systems. (C) 2001 John Wiley & Sons, Inc.
Resumo:
In an acidic aqueous solution of acetonitrile, the catalytic activity of the catalysts consisted of Pd(OAc)(2)/hydroquinone(HQ) with iron phthalocyanine (FePc) from various sources was obviously different in the oxidation of cyclohexene to cyclohexanone, The analysis of the FePc using IR spectroscopy, Mossbauer spectroscopy, X-ray photoelectron spectroscopy (XPS), X-ray powder diffraction (XRD), scanning electron microscopy(SEM) and BET surface area measurement indicated that the catalytic activity of the multicomponent catalytic system composed of iron phthalocyanines depends on the amount of mu -oxo FePc, the crystallinity and the surface structure of iron phthalocyanine.
Resumo:
Selective crystallization of BaF2 crystals under a compressed Langmuir monolayer of behenic acid [CH3(CH2)(20)COOH] has been studied by using X-ray diffraction, X-ray photoelectron spectroscopy, scanning electron microscopy, and energy-dispersive X-ray analysis. It was found that, in the absence of a monolayer, three kinds of crystals (Ba2ClF3, BaClF, and BaF2) can be obtained by mixing BaCl2 with a NH4F solution. However, in the presence of the monolayer of behenic acid, only BaF2 crystals appear at the monolayer-subphase interface and crystals have a special crystal face (100). During this process of crystallization, the monolayer plays a very important role and acts as a template that can preferentially select a special crystal and a special crystal face. The above results can be explained in terms of a specific molecular interaction between ions and the headgroups of the monolayer and specific electrostatic, geometric, and stereochemical interactions at the organic-inorganic interface.
Resumo:
SnO2 thin films with extremely preferred orientation along (101) plane were made by LB technique and characterized by FTIR,, UV-visible, X-ray diffraction, X-ray photoelectron spectroscopy and SEM.