Synthesis of NaA zeolite membranes from clear solution

NaA zeolite membranes were successfully synthesized on a porous alpha -Al2O3 support from clear solution. The synthesis parameters, such as surface seeding, synthesis time, synthesis stages, etc. were investigated. Surface seeding can not only accelerate the formation of NaA zeolite on the support surface, but can also inhibit the transformation of NaA zeolite into other types of zeolites. A continuous NaA zeolite membrane formed on the seeded support after 2 h of synthesis. Gas permeation results showed that a synthesis time of 3 h produced the best NaA zeolite membrane. When the synthesis time was longer than 4 h, the NaA zeolite on the support surface began to transform into other types of zeolites, and the quality of the NaA zeolite membrane decreased. The quality of the NaA zeolite membrane can be improved by employing the multi-stage synthesis method. The NaA zeolite membrane with a synthesis time of 2 h after a two-stage synthesis showed the best gas permeation performance. The permeances of H-2, O-2, N-2, and n-C4H10 decreased as the molecular kinetic diameter of the gases increased. which showed the molecular sieving effect of the NaA zeolite membrane. The permselectivities of H-2/n-C4H10 and O-2/N-2 were 19.1 and 1.8, respectively. These values are higher than the Knudsen diffusion ratios of 5.39 and 0.94. However, the permeation of n-C4H10 also indicated that the NaA zeolite membrane had certain defects with diameters larger than the pore size of NaA zeolite. A synthesis model was proposed to clarify the effect of surface seeding. (C) 2001 Elsevier Science B.V. All rights reserved.

A novel process for converting coalmine-drained methane gas to syngas over nickel-magnesia solid solution catalysts

A novel process is developed in this paper for utilizing the coalmine-drained methane gas that is usually vented straight into the atmosphere in most coalmines worldwide. It is expected that low-cost syngas can be produced by the combined air partial oxidation and CO2 reforming of methane, because this process utilizes directly the methane, air, and carbon dioxide in the coalmine-drained gas without going through the separation step. For this purpose, a nickel-magnesia solid solution catalyst was prepared and its catalytic performance for the proposed process was investigated. It was found that calcination temperature has significant influence on the catalytic performance due to the different extent of solid solution formation in the catalysts. A uniform nickel-magnesia solid solution catalyst exhibits higher stability than the catalysts in which NiO has not completely formed solid solution with MgO. Its catalytic activity and selectivity remain stable during 120 h of reaction. The product H-2/CO ratio is mainly dependent on the feed gas composition. By changing CO2/air ratio of the feed gases, syngas with a H-2/CO ratio between 1 and 1.9 can be obtained. The influences of reaction temperature and nickel loading on the catalytic performance were also investigated. (c) 2004 Elsevier B.V All rights reserved.

Cobalt boride catalysts for hydrogen generation from alkaline NaBH4 solution

Cobalt boride precursors were synthesized via chemical reaction of aqueous sodium borohydride with cobalt chloride, and followed by heat-treating at various temperatures. The as-prepared Co-B catalysts were characterized and analyzed by X-ray diffraction (XRD), nitrogen adsorption-desorption and catalytic activity test; and were adopted to help accelerating hydrolysis reaction of NaBH4 alkaline solution. The Co-B catalyst treated at 500 degrees C exhibits the best catalytic activity, and achieves an average H, generation rate of 2970 ml/min/g, which may give a successive H, supply for a 481 W proton exchange membrane fuel cell (PEMFC) at 100% H-2 utilization. (c) 2005 Elsevier B.V. All rights reserved.