Cobalt boride catalysts for hydrogen generation from alkaline NaBH4 solution

Cobalt boride precursors were synthesized via chemical reaction of aqueous sodium borohydride with cobalt chloride, and followed by heat-treating at various temperatures. The as-prepared Co-B catalysts were characterized and analyzed by X-ray diffraction (XRD), nitrogen adsorption-desorption and catalytic activity test; and were adopted to help accelerating hydrolysis reaction of NaBH4 alkaline solution. The Co-B catalyst treated at 500 degrees C exhibits the best catalytic activity, and achieves an average H, generation rate of 2970 ml/min/g, which may give a successive H, supply for a 481 W proton exchange membrane fuel cell (PEMFC) at 100% H-2 utilization. (c) 2005 Elsevier B.V. All rights reserved.

Catalytic steam reforming of ethanol to produce hydrogen and acetone

Steam reforming of ethanol over CuO/CeO2 was studied. Acetaldehyde and hydrogen were mainly produced at 260degreesC. At 380degreesC, acetone was the main product, and 2 mol of hydrogen was produced from 1 mol of ethanol. The formation of hydrogen accompanied by the production of acetone was considered to proceed through the following, consecutive reactions: dehydrogenation of ethanol to acetaldehyde. aldol condensation of the acetaldehyde, and the reaction of the aldol with the lattice oxygen [O(s)] on the catalyst to form a surface intermediate, followed by its dehydrogenation and decarboxylation. The overall reaction was expressed by2C(2)H(5)OH + H2O --> CH3COCH3 + CO2 + 4H(2). Ceria played an important role as an oxygen supplier. The addition of MgO to CuO/CeO2 resulted in the production of hydrogen at lower temperatures by accelerating aldol condensation. (C) 2004 Elsevier B.V. All rights reserved.

Reaction-controlled phase transfer catalysis for styrene epoxidation to styrene oxide with aqueous hydrogen peroxide

The epoxidation of styrene catalyzed by a reaction-controlled phase transfer catalyst [(C18H37(30%)+C16H33(70%))N(CH3)(3))(3)](3)-[PW4O16] with H2O2 in a biphasic medium was investigated. Under certain conditions, the selectivity for styrene oxide was 95%, the conversion of styrene based on H2O2 was 85%, and the reaction time was less than 1 h. During the reaction, this catalyst powder formed soluble active species by the action of H2O2, was recovered as a precipitate, and was reused after H2O2 was used up. After two times recycling, the catalyst kept almost the same activity.

Preparation of a novel polysulfone/polyethylene oxide/silicone rubber multilayer composite membrane for hydrogen-nitrogen separation

A novel poly sulfone/polyethylene oxide/silicone rubber (PSOPEO/SR) multilayer composite membrane was fabricated by double coating polysulfone substrate membrane with polyethylene oxide and silicone rubber. Gas permeation experiments were performed at 30 degrees C for hydrogen and nitrogen. PSf(PEO/SR membrane displayed high and steady performance for H-2/N-2: permeances of H-2 and N-2 of 49.51 and 0.601 GPU, respectively, and H-2/N-2 ideal separation factor of 82.3. It was explained that layer interfaces due to the introduction of PEO layer act as the permselective media and are responsible for the higher H-2/N-2 ideal separation factor which has exceeded the intrinsic permselectivities of the three polymers used in this study. (c) 2005 Elsevier B.V. All rights reserved.