Polyelectrolyte complexes based on chitosan and poly(L-glutamic acid)

Polyelectrolyte complexes (PECs) were prepared by mixing aqueous solutions of chitosan (CS) and poly(L-glutamic acid) (PLGA) at various pH. It was found that the stoichiometry of the PECs depends on pH.An investigation of the PECs using Fourier transform infrared spectroscopy proved that the formation of the complexes is due to electrostatic interaction between –NH3 + groups of CS and –COO− groups of PLGA. The solid PECs were characterized using wide-angle X-ray diffraction, which suggested that a strong interaction occurs between the two polymers at pH = 4 or 5 and relatively weak interaction at pH = 3. These results were further confirmed by thermogravimetric analysis data. Transmission electron microscopy showed that the complexes have a spherical shape. The effect of ionic strength on the size of the PECs was also studied using dynamic light scattering. It was found that the size of the PECs is dependent on pH.

Morphology of polyimide fibers derived from 3,3 ',4,4 '-biphenyltetracarboxylic dianhydride and 4,4 '-oxydianiline

As one member of high performance fibers, aromatic polyimide fibers possess many advantages, such as high strength, high modulus, high and low temperature resistance, and radiation resistance. However, the preparation of the high performance fibers is so difficult that the commercial fibers have not been produced except P84 with good flame retardancy. In this report, a polyimide was synthesized from 3,3',4,4'-biphenyltetracarboxylic dianhydride (BPDA) and 4,4'-oxydianiline (ODA) and the fibers were prepared from its solution by a dry-jet wet-spinning process. The formation of the as-spun fibers in different coagulation bath composition was discussed. Scanning electron microscope (SEMI) was employed to study the morphology of the as-spun fibers. As a result, the remnant solvent existed in the as-spun fibers generated from coagulation bath of alcohol and water. There were many fibrils and microvoids with the dimension of tens of nanometers in the fibers. One could observe the obvious fibrillation and the drawn fibers.

Structural stability and electronic state of transition metal trimers

Ground state geometries were searched for transition metal trimers Sc-3, Y-3, La-3, Lu-3, Ti-3, Zr-3, and Hf-3 by density functional methods. For all the studied trimers, our calculation indicates that the ground state geometries are either equilateral triangle (Zr-3 and Hf-3) or near equilateral triangle (Ti-3, Sc-3, Y-3, La-3, and Lu-3). For rare earth trimers Sc-3, Y-3, La-3, and Lu-3, isosceles triangle (near equilateral triangle) at quartet state is the ground state. Isosceles triangle at doublet state is the competitive candidate for the ground state. For Zr-3 and Hf-3, equilateral triangle at singlet state is the most stable. For Ti-3, isosceles triangle (near equilateral triangle) at quintet state gives the ground state. For Sc-3, Zr-3, and Hf-3, where experimental results are available, the predicted geometries are in agreement with experiment in which the ground state is equilateral triangle (Zr-3) or fluxional (Sc-3 and Hf-3). For Y-3, the calculated geometry is in agreement with experimental observation and previous theoretical study that Y-3 is a bent molecule for the ground state.

Electronic structures of hafnium dimer and trimer by density functional theory

Equilibrium geometries, vibrational frequencies and dissociation energies of hafnium dimer and trimer were studied by density functional methods B3LYP, BLYP, B3PW91, BHLYP, BP86, B3P86, mPW1PW91 and PBE1PBE. The results indicate that singlet is the ground state both for hafnium dimer and for trimer. For hafnium dimer, the calculated bond distance is less sensitive to the methods used. Except at BHLYP level, the calculated vibrational frequency is comparable to the experimental value. For hafnium trimer, equilateral triangle with D-3h symmetry is slightly favored compared with isosceles triangle with C-2v, symmetry except at BHLYP level. This conclusion is in agreement with experiment in which the ground state of Hf-3 is fluxional and low-spin or closed shell is preferred.

Mechanical properties of BPDA-ODA polyimide fibers

An aromatic polyimide was synthesized via a one-step polycondensation reaction between biphenyltetracarboxylic dianhydride (BPDA) and 4,4'-oxydianiline (ODA) in p-chlorophenol. The polyimide (BPDA-ODA) solution dopes were spun into fibers by means of dry-jet wet spinning. The as-spun fibers were drawn and treated in heating tubes for improving the mechanical properties. The thermal treatment on the fibers resulted in a relatively high tensile strength and modulus. Thermal mechanical analysis (TMA) was employed to study the linear coefficient of thermal expansion (CTE). Thermal gravimetry analysis (TGA) spectra showed that the BPDA-ODA fibers possessed an excellent property of thermo-oxidative degradation resistance. The sonic modulus E-s of the polyimide fibers was measured.

New titanium complexes with two beta-enaminoketonato chelate ligands: Syntheses, structures, and olefin polymerization activities

New titanium complexes with two nonsymmetric bidentate beta-enaminoketonato (N,O) ligands (4a-e), [(Ph)NC(R-2)C(H)C(R-1)O](2)TiCl2, have been synthesized. X-ray crystal structure reveals that complex 4a has a C-2-symmetric conformation with a distorted octahedral geometry around the titanium center. With modified methylaluminoxane (MMAO) as a cocatalyst, complexes 4a-e are active catalysts for ethylene polymerization at room temperature, producing high molecular weight polyethylenes bearing linear structures. The 4a,b/MMAO catalyst systems exhibit the characteristics of a quasi-living polymerization of ethylene, producing polyethylenes with narrow molecular weight distributions. Moreover, the 4a-d/MMAO catalyst systems are also capable of promoting the quasi-living copolymerization of ethylene with norbornene at room temperature, yielding high molecular weight alternating copolymers with narrow molecular weight distributions. The quasi-living nature of the catalysts allows the synthesis of new A-B polyethylene-block-poly(ethylene-conorbornene) diblock copolymer.

Synthesis of four-armed poly(epsilon-caprolactone)-block-poly(ethylene oxide) by diethylzinc catalyst

Biodegradable, amphiphilic, four-armed poly(epsilon-caprolactone)-block-poly(ethylene oxide) (PCL-b-PEO) copolymers were synthesized by ring-opening polymerization of ethylene oxide in the presence of four-armed poly(epsilon-caprolactone) (PCL) with terminal OH groups with diethylzinc (ZnEt2) as a catalyst. The chemical structure of PCL-b-PEO copolymer was confirmed by H-1 NMR and C-13 NMR. The hydroxyl end groups of the four-armed PC L were successfully substituted by PEO blocks in the copolymer. The monomodal profile of molecular weight distribution by gel permeation chromatography provided further evidence for the four-armed architecture of the copolymer. Physicochemical properties of the four-armed block copolymers differed from their starting four-armed PCL precursor. The melting points were between those of PCL precursor and linear poly(ethylene glycol). The length of the outer PEO blocks exhibited an obvious effect on the crystallizability of the block copolymer. The degree of swelling of the four-armed block copolymer increased with PEO length and PEO content.

Probing the micellization of diblock and triblock copolymers of poly(L-lactide) and poly(ethylene glycol) in aqueous and NaCl salt solutions

The micelle formation of a series of amphiphilic block copolymers in aqueous and NaCl solutions was studied by a fluorescent probe technique using pyrene as a 'model drug'. These copolymers were synthesized from poly (ethylene glycol) (PEG) and L-lactide by a new calcium ammoniate catalyst. They had fixed PEG block lengths (44, 104 or 113 ethylene oxide units) and various poly(L-lactide) (PLLA) block lengths (15-280 lactide units). The critical micelle concentration (cmc) was found to decrease with increasing PLLA content. The distinct dissimilarity of the cmc values of diblock and triblock copolymers based on the same block length of PEG provided evidence for the different configurations of their micelles. It was also observed that the introduction of NaCl salt significantly contributed to a decrease in the cmcs of the copolymers with short PEG and PLLA blocks, while it had less influence on the cmcs of copolymers with long PEG or PLLA blocks. The dependence of partition coefficients ranging from 0.2x10(5) to 1.9x10(5) on the PLLA content in the copolymer and on the micelle configuration was also discussed.

Biochemical properties of C78SC96S rhFGF-2: A double point-mutated rhFGF-2 increases obviously its activity

Fibroblast growth factor-2 (FGF-2) is a multifunctional polypeptide that affects many cellular functions and phenomena. The wild-type recombinant human fibroblast growth factor rhFGF-2(W) and the mutant C78SC96S rhFGF-2(M) were expressed in Escherichia coli and their products were purified. The results by the means of fluorescence spectroscopy and CD spectrums, suggested that due to its decreased hydrophobicity rhFGF-2 is not deposited as an inclusion body. The mitogenic activity of the expressed rhFGF-2(M) on 3T3 fibroblasts was shown to be 10-fold more than the expressed rhFGF-2(W) of which the biological activity was a little less than that of the standard rhbFGF(W), indicating that the increased biological activity was due to the change of its secondary structure, dimerization and affinity binding to FGF receptor (FGFR).

Neodymium-cerium oxide as new thermal barrier coating material

Neodymium-cerium oxide (Nd2Ce2O7) was proposed as a new thermal barrier coating material in this work. Monolithic Nd2Ce2O7 powder was prepared by the solid-state reaction at 1400 degrees C. The phase composition, thermal stability and thermophysical properties of Nd2Ce2O7 were investigated. Nd2Ce2O7 with fluorite structure was thermally stable in the temperature range of interest for TBC applications. The results indicated that the thermal expansion coefficient (TEC) of Nd2Ce2O7 was higher than that of YSZ (6-8 Wt-% Y2O3 + ZrO2) and even more interesting was the TEC change as a function of temperature paralleling that of the superalloy bond coat. Moreover, the thermal conductivity of Nd2Ce2O7 is 30% lower than that of YSZ, which was discussed based on the theory of heat conduction. Thermal barrier coating of Nd2Ce2O7 was produced by atmospheric plasma spraying (APS) using the spray-dried powder. The thermal cycling was performed with a gas burner test facility to examine the thermal stability of the as-prepared coating.

Thermal stability of double-ceramic-layer thermal barrier coatings with various coating thickness

Double-ceramic-layer (DCL) coatings with various thickness ratios composed of YSZ (6-8 wt.% Y2O3 + ZrO2) and lanthanum zirconate (LZ, La2Zr2O7) were produced by the atmospheric plasma spraying. Chemical stability of LZ in contact with YSZ in DCL coatings was investigated by calcining powder blends at different temperatures. No obvious reaction was observed when the calcination temperature was lower than 1250 degrees C, implying that LZ and YSZ had good chemical applicability for producing DCL coating. The thermal cycling test indicate that the cycling lives of the DCL coatings are strongly dependent on the thickness ratio of LZ and YSZ, and the coatings with YSZ thickness between 150 and 200 mu m have even longer lives than the single-layer YSZ coating. When the YSZ layer is thinner than 100 mu m, the DCL coatings failed in the LZ layer close to the interface of YSZ layer and LZ layer. For the coatings with the YSZ thickness above 150 mu m, the failure mainly occurs at the interface of the YSZ layer and the bond coat.

Lanthanum zirconate nanofibers with high sintering-resistance

The PVP/lanthanum nitrate/zirconium oxychloride (PVP-precursor) nanofiber was prepared by electrospinning technique. Lanthanum zirconate (La2Zr2O7, LZ) in the nanofiber is formed after calcination at 800 degrees C and the nanofiber with pyrochlore structure and a diameter of 100-500 nm can be obtained by calcination of the above precursor fiber at 1000 degrees C for 12 h. The surface of the fiber is rough but the continuous microstructure is still maintained after calcination. LZ fibers stack randomly, resulting in a structure with a low contact area between the fibers. This special structure makes the fiber to have a high resistance to sintering at elevated temperatures. The BET (Brunauer-Emmett-Teller) specific surface areas of the LZ fiber and powder calcined at different temperatures are shown in this paper, and the fiber was characterized by TG-DTA (thermal gravimetry-differential thermal analysis), XRD (X-ray diffraction), N-2 absorption-desorption porosimetry and SEM (scanning electron microscopy).

Synthesis and characterization of PCL/PEG/PCL triblock copolymers by using calcium catalyst

Triblock copolymer PCL-PEG-PCL was prepared by ring-opening polymerization of epsilon-caprolactone (CL) in the presence of poly(ethylene glycol) catalyzed by calcium ammoniate at 60 degreesC in xylene solution. The copolymer composition and triblock structure were confirmed by H-1 NMR and C-13 WR measurements. The differential scanning calorimetry and wide-angle X-ray diffraction analyses revealed the micro-domain structure in the copolymer. The melting temperature T-c and crystallization temperature T-c of the PEG domain were influenced by the relative length of the PCL blocks. This was caused by the strong covalent interconnection between the two domains. Aqueous micelles were prepared from the triblock copolymer. The critical micelle concentration was determined to be 0.4-1.2 mg/l by fluorescence technique using pyrene as probe, depending on the length of PCL blocks, and lower than that of corresponding PCL-PEG diblock copolymers. The H-1 NMR spectrum of the micelles in D2O demonstrated only the -CH2CH2O- signal and thus confirmed. the PCL-core/PEG-shell structure of the micelles.

Resonant two-photon cross-section calculations for transitions to 4f5d state in Pr3+: YAG using density matrix theory

The density matrix resonant two-photon absorption (TPA) theory is applied to a rare-earth ion-doped laser crystal. TPA cross sections for transitions from the ground state to the first 4f5d state in Pr3+:YAG are calculated. The results indicate the density matrix TPA theory is attractive in studying TPA in laser crystals. (C) 2000 Elsevier Science B.V. All rights reserved.

Calculations of cross sections of resonant two-photon transitions to the second excited 4f5d state in Pr3+: Y3Al5O12 using density matrix theory

The density matrix resonant two-photon absorption (TPA) theory applicable to laser crystals doped with rare earth ions is described. Using this theory, resonant TPA cross sections for transitions from the ground state to the second excited state of the 4f5d configuration in cm(4)s Pr3+:Y3Al5O12 are calculated. The peak value of TPA cross section calculated is 2.75 x 10(-50) cm(4)s which is very close to the previous experimental value 4 x 10(-50) cm(4) s. The good agreement of calculated data with measured values demonstrates that the density matrix resonant TPA theory can predict resonant TPA intensity much better than the standard second-order perturbation TPA theory.