Effect of poly(propylene carbonate) on the crystallization and melting behavior of poly(beta-hydroxybutyrate-co-beta-hydroxyvalerate)

The crystallization and melting behavior of poly(beta-hydroxybutyrate-co-beta-hydroxyvalerate) (PHBV) and a 30/70 (w/w) PHBV/poly(propylene carbonate) (PPC) blend was investigated with differential scanning calorimetry (DSC) and Fourier transform infrared (FTIR). The transesterification reaction between PHBV and PPC was detected in the melt-blending process. The interaction between the two macromolecules was confirmed by means of FTIR analysis. During the crystallization process from the melt, the crystallization temperature of the PHBV/PPC blend decreased about 8 degreesC, the melting temperature was depressed by 4 degreesC, and the degree of crystallinity of PHBV in the blend decreased about 9.4%; this was calculated through a comparison of the DSC heating traces for the blend and pure PHBV. These results indicated that imperfect crystals of formed, crystallization was inhibited, and the crystallization ability of PHBV was weakened in the blend. The equilibrium melting temperatures of PHBV and the 30/70 PHBV/PPC blend isothermally crystallized were 187.1 and 179 degreesC, respectively.

The synthesis and catalytic activity of poly(bis(imino)pyridyl) iron(II) metallodendrimer

The first and second generation carbosilane dendrimers with silicon hydride terminated were synthesized, and then reacted with bis(imino)pyridyl containing allyl [4-CH2==CHCH2-2,6-(Pr2C6H3N)-Pr-i==CMe(C5H3N)MeC==N(2,6-'Pr2C6H3)], in the presence of H2PtCl6 as a hydrosilylation catalyst, to afford the first and second generation carbosilane supported ligands. Complexation reactions with FeCl(2)(.)4H(2)O give rise to iron-containing carbosilane dendrimers with FeCl2 moieties bound on the periphery. The metallodendrimers were used as catalyst precursors, activated with modified methylaluminoxane, for the polymerization of ethylene. In the case of low Al/Fe molar ratio, the metallodendrimers display much higher catalytic activity towards ethylene polymerization and produce much higher molecule weight polyethylenes than the corresponding single-nuclear complex under the same conditions.

A novel method to construct a third-generation biosensor: self-assembling gold nanoparticles on thiol-functionalized poly(styrene-co-acrylic acid) nanospheres

A novel method for fabrication of horseradish peroxidase (HRP) biosensor has been developed by self-assembling gold nanoparticles on thiol-functionalized poly(styrene-co-acrylic acid) (St-co-AA) nanospheres. At first, a cleaned gold electrode was immersed in thiol-functionalized poly(St-co-AA) nanosphere latex prepared by emulsifier-free emulsion polymerization of St with AA and function with dithioglycol to assemble the nanospheres, then gold nanoparticles were chemisorbed onto the thiol groups. Finally, horseradish peroxi- dase was immobilized on the surface of the gold nanoparticles. The sensor displayed an excellent electrocatalytical response to reduction of H2O2 without the aid of an electron mediator. The sensor was highly sensitive to hydrogen peroxide with a detection limit of 4.0 mumol l(-1), and the linear range was from 10.0 mumol l(-1) to 7.0 mmol l(-1). The biosensor retained more than 97.8% of its original activity after 60 days of use. Moreover, the Studied biosensor exhibited good current repeatability and good fabrication reproducibility.

Synthesis of four-armed poly(epsilon-caprolactone)-block-poly(ethylene oxide) by diethylzinc catalyst

Biodegradable, amphiphilic, four-armed poly(epsilon-caprolactone)-block-poly(ethylene oxide) (PCL-b-PEO) copolymers were synthesized by ring-opening polymerization of ethylene oxide in the presence of four-armed poly(epsilon-caprolactone) (PCL) with terminal OH groups with diethylzinc (ZnEt2) as a catalyst. The chemical structure of PCL-b-PEO copolymer was confirmed by H-1 NMR and C-13 NMR. The hydroxyl end groups of the four-armed PC L were successfully substituted by PEO blocks in the copolymer. The monomodal profile of molecular weight distribution by gel permeation chromatography provided further evidence for the four-armed architecture of the copolymer. Physicochemical properties of the four-armed block copolymers differed from their starting four-armed PCL precursor. The melting points were between those of PCL precursor and linear poly(ethylene glycol). The length of the outer PEO blocks exhibited an obvious effect on the crystallizability of the block copolymer. The degree of swelling of the four-armed block copolymer increased with PEO length and PEO content.

Hydrodynamic radius characterization of a vinyl-type polynorbornene by size-exclusion chromatography with a static and dynamic laser light scattering detector

Both absolute molecular weight and molecular sizes (radius of gyration and hydrodynamic radius) of a vinyl-type polynorbornene eluting from size-exclusion chromatography columns were determined by combined with a static and dynamic laser light scattering detector. The hydrodynamic radius of polymer fraction eluting from size-exclusion chromatography columns was obtained from dynamic laser light scattering measurements at only a single angle of 900 by introducing a correction factor. According to the scaling relationship between molecular sizes and molecular weight and the ratio between radius of gyration and hydrodynamic radius, the vinyl-type polynorbornene took a random coil conformation in 1,2,4-trichlorobenzene at 150 degreesC.

Enzymatic degradation of poly(L-lactide) and poly (epsilon-caprolactone) electrospun fibers

Poly(L-lactide) (PLLA) and poly(epsilon-caprolactone) (PCL) ultrafine fibers were prepared by electrospinning. The influence of cationic and anionic surfactants on their enzymatic degradation behavior was investigated by measuring weight loss, molecular weight, crystallinity, and melting temperature of the fibers as a function of degradation time. Under the catalysis of proteinase K, the PLLA fibers containing the anionic surfactant sodium docecyl sulfate (SDS) exhibited a faster degradation rate than those containing cationic surfactant triethylbenzylammonium chloride (TEBAC), indicating that surface electric charge on the fibers is a critical factor for an enzymatic degradation. Similarly, TEBAC-containing PCL fibers exhibited a 47% weight loss within 8.5 h whereas SDS-containing PCL fibers showed little degradation in the presence of lipase PS. By analyzing the charge status of proteinase K and lipase PS under the experimental conditions, the importance of the surface charges of the fibers and their interactions with the charges on the enzymes were revealed. Consequently, a "two-step" degradation mechanism was proposed: (1) the enzyme approaches the fiber surface; (2) the enzyme initiates hydrolysis of the polymer.

Probing the micellization of diblock and triblock copolymers of poly(L-lactide) and poly(ethylene glycol) in aqueous and NaCl salt solutions

The micelle formation of a series of amphiphilic block copolymers in aqueous and NaCl solutions was studied by a fluorescent probe technique using pyrene as a 'model drug'. These copolymers were synthesized from poly (ethylene glycol) (PEG) and L-lactide by a new calcium ammoniate catalyst. They had fixed PEG block lengths (44, 104 or 113 ethylene oxide units) and various poly(L-lactide) (PLLA) block lengths (15-280 lactide units). The critical micelle concentration (cmc) was found to decrease with increasing PLLA content. The distinct dissimilarity of the cmc values of diblock and triblock copolymers based on the same block length of PEG provided evidence for the different configurations of their micelles. It was also observed that the introduction of NaCl salt significantly contributed to a decrease in the cmcs of the copolymers with short PEG and PLLA blocks, while it had less influence on the cmcs of copolymers with long PEG or PLLA blocks. The dependence of partition coefficients ranging from 0.2x10(5) to 1.9x10(5) on the PLLA content in the copolymer and on the micelle configuration was also discussed.

Crosslinkable poly (p-phenylenevinylene) derivative

To simplify the fabrication of multilayer light-emitting diodes, we prepared a p-phenylenevinylene-based polymer capped with crosslinkable styrene through a Wittig reaction. Insoluble poly(p-phenylenevinylene) derivative (PPVD) films were prepared by a thermal treatment. The photoluminescence and ultraviolet-visible (UV-vis) absorbance of crosslinked films and noncrosslinked films were studied. We also studied the solvent resistance of crosslinked PPV films with UV-vis absorption spectra and atomic force microscopy. Double-layer devices using crosslinked PPVD as an emitting layer, 2-(4-tert-butylphenyl)-5-phenyl-1,3,4-oxadiazole (PBD) in poly(methyl methacrylate) as an electron-transporting layer, and calcium as a cathode were fabricated. A maximum luminance efficiency of 0.70 cd/A and a maximum brightness of 740 cd/m(2) at 16 V were demonstrated. A 12-fold improvement in the luminance efficiency with respect to that of single-layer devices was realized.

Blue light-emitting poly(fluorene-co-benzene) containing an oxadiazole moiety

A new kind of polyfluorene containing oxadiazole as the side chain was synthesized. The introduction of oxadiazole moiety as more bulky group prevents the aggregation and reduces the crystallinity of the polymers. Efficient intramolecular energy transfer from oxadiazole moiety to the conjugated backbone has been realized, leading to 70% improvement of photoluminescence quantum efficiency of the designed polymers. Compared with PAF, the PFOXD exhibits significant improvement in electroluminescence properties, with luminous efficiency of 0.8 cd/A and maximum luminance of 1800 cd/m(2).

Efficient blue electroluminescence from neutral alcohol-soluble polyfluorenes with aluminum cathode

Efficient blue polymer light-emitting diodes (PLEDs) have been fabricated with a neutral alcohol-soluble polyfluorene, i.e., poly(9,9-bis(6(')-diethoxylphosphorylhexyl)fluorene) (PF-EP), as the emitting layer, high work-function Al as the cathode, and poly(vinyl carbazole) as the hole-transporting layer. The PLEDs display a maximum luminous efficiency of 4.0 cd/A and the luminous efficiency > 2.4 cd/A in a wide range of current densities. It is found that the promising performance of the devices is attributed to the fact that the PF-EP is not only an efficient blue light-emitting polymer, but it also can facilitate efficient electron injection at the Al/PF-EP interface.

Synthesis and characterization of hyperbranched poly(ester-amide)s from commercially available dicarboxylic acids and multihydroxyl primary amines

A new method for syntheses of hyperbranched poly(ester-amide)s from commercially available A(2) and CBx type monomers has been developed on the basis of a series of model reactions. The aliphatic and semiaromatic hyperbranched poly(ester-amide)s with multihydroxyl end groups are prepared by in situ thermal polycondensation of intermediates obtained from dicarboxylic acids (A(2)) and multihydroxyl primary amines (CBx) in N,N-dimethylformamide. Analyses of FTIR, H-1 NMR, and C-13 NMR spectra revealed the structures of the polymers obtained. The MALDI-TOF MS of the polymers indicated that cyclization side reactions occurred during polymerization. The hyperbranched poly(ester-amide) s contain configurational isomers observed by C-13 and DEPT C-13 NMR spectroscopy. The DBs of the polymers were determined to be 0.38-0.62 by H-1 NMR or quantitive C-13 NMR and DEPT 135 spectra. These polymers exhibit moderate molecular weights, with broad distributions determined by size exclusion chromatography ( SEC), and possess excellent solubility in a variety of solvents such as N, N- dimethylacetamide, dimethyl sulfoxide, tetrahydrofuran, and ethanol, and display glass-transition temperatures (T(g)s) between -2.3 and 53.2 degrees C, determined by DSC measurements.

Sulfonated poly(arylene-co-naphthalimide)s synthesized by copolymerization of primarily sulfonated monomer and fluorinated naphthalimide dichlorides as novel polymers for proton exchange membranes

A novel sulfonated aromatic dichloride monomer was successfully prepared by the reaction of 2, 5-dichlorobenzophenone with fuming sulfuric acid. Copolymerization of this monomer in the form of sodium salt (1) with N-(4-chloro-2-trifluoromethylphenyl)-5-chloro-1,8-naphthalimide (2) or bis(N-(4-chloro-2-trifluoromethylphenyl)1,4,5,8-naphthalimide (3) generated two series of novel poly(arylene-co-naphthalimide) s I-x and II-x where x represents the content of the sulfonated monomer. The synthesized copolymers with the -SO3H group in the side chains possessed high molecular weights revealed by their high viscosity and the formation of tough and flexible membranes. The copolymers exhibited excellent stability toward water and oxidation due to the introduction of the hydrophobic CF3 groups. The sulfonated copolyimides that incorporated with 1,8-naphthalimide (I-x) exhibited better hydrolytic and oxidative stabilities than those with 1,4,5,8-naphthalimide. Copolymer I-50 membrane endured for more than 83 h in Fenton's reagent at room temperature. The mechanical properties of I-50 membrane kept almost unchanged after immersing membrane in boiling water for 196 h. The proton conductivities of copolymer films increased with increasing IEC and temperature, reaching values above 6.8 x 10(-1) S/cm at 80 degrees C.

Poly(aryl ether)s containing ter- and pentafluorene pendants for efficient blue light emission

Four novel thermally stable poly(aryl ether)s, e.g., P3F, P5F, P2A3F, and P2A5K containing ter- or pentafluorene units in the side chains for efficient blue light emission have been designed and synthesized. All the polymers show the optical properties identical to the corresponding monomers and are amorphous with higher glass transition temperature (T-g) than their monomeric Counterparts. The polymer light-emitting diodes (PLEDs) were fabricated with the device structure of ITO/(PEDOT:PSS)/polymer/Ca/Al. The incorporation of diphenylamine group to oligofluorene terminals significantly reduces the hole-injection energy barrier in PLEDs. The devices based on P2A3F and P2A5F show the luminous efficiencies of 1.2 and 2.0 cd/A at a brightness of 300 cd/m(2) with the Commission Internationale de L'Eclairage (CIE) coordinates of (0.15, 0.13) and (0.19, 0.20), respectively. All these indicate that the high-performance light-emitting polymers can be synthesized with the traditional condensation polymerization through careful design of polymer structures.

Synthesis and characterization of blue-light-emitting poly(aryl ether)s containing oligofluorenes in the main chain

A series of blue light-emitting poly(aryl ether)s (PAEs) containing ter- or pentafluorenes in the main chain have been synthesized via nucleophilic substitution polycondensation reaction. The energy levels of the polymers were tuned by introducing hole-transporting triaryamine groups in the side chains and/or incorporating electron-transporting oxadiazole segments in the main chain. The optical properties of the polymers are dominantly determined by the well-defined oligofluorene segments, and therefore all polymers show high photoluminescence quantum yield. Differential scanning calorimeter (DSC) characterizations indicate that they are vitrified polymers with high glass transition temperature (up to 156 degrees C). The polymers comprising pentafluorenes exhibit electroluminescent properties equal to or better than fully conjugated fluorene homopolymers. With the device structure of ITO/PEDOT:PSS/polymer/Ca/Al, an external quantum efficiency of 1.4% along with Commission Internationale de L'Eclairage (CIE) coordinates of (0.17, 0.09) has

Synthesis and characterization of RGD peptide grafted poly(ethylene glycol)-b-poly(L-lactide)-b-poly(L-glutamic acid) triblock copolymer

Advances in tissue engineering require biofunctional scaffolds that can provide not only physical support for cells but also chemical and biological cues needed in forming functional tissues. To achieve this goal, a novel RGD peptide grafted poly(ethylene glycol)-b-poly(L-lactide)-b-poly(L-glutamic acid) (PEG-PLA-PGL/RGD) was synthesized in four steps (1) to prepare diblock copolymer PEG-PLA-OH and to convert its -OH end group into -NH2 (to obtain PEG-PLA-NH2), (2) to prepare triblock copolymer PEG-PLA-PBGL by ring-opening polymerization of NCA (N-carboxyanhydride) derived from benzyl glutamate with diblock copolymer PEG-PLA-NH2 as macroinitiator, (3) to remove the protective benzyl groups by catalytic hydrogenation of PEGPLA-PBGL to obtain PEG-PLA-PGL, and (4) to react RGD (arginine-glycine-(aspartic amide)) with the carboxyl groups of the PEG-PLA-PGL. The structures of PEG-PLA-PGL/RGD and its precursors were confirmed by H-1 NMR, FT-IR, amino acid analysis, and XPS analysis. Addition of 5 wt % PEG-PLA-PGL/RGD into a PLGA matrix significantly improved the surface wettability of the blend films and the adhesion and proliferation behavior of human chondrocytes and 3T3 cells on the blend films. Therefore, the novel RGD-grafted triblock copolymer is expected to find application in cell or tissue engineering.