Synthesis of NaA zeolite membranes from clear solution

NaA zeolite membranes were successfully synthesized on a porous alpha -Al2O3 support from clear solution. The synthesis parameters, such as surface seeding, synthesis time, synthesis stages, etc. were investigated. Surface seeding can not only accelerate the formation of NaA zeolite on the support surface, but can also inhibit the transformation of NaA zeolite into other types of zeolites. A continuous NaA zeolite membrane formed on the seeded support after 2 h of synthesis. Gas permeation results showed that a synthesis time of 3 h produced the best NaA zeolite membrane. When the synthesis time was longer than 4 h, the NaA zeolite on the support surface began to transform into other types of zeolites, and the quality of the NaA zeolite membrane decreased. The quality of the NaA zeolite membrane can be improved by employing the multi-stage synthesis method. The NaA zeolite membrane with a synthesis time of 2 h after a two-stage synthesis showed the best gas permeation performance. The permeances of H-2, O-2, N-2, and n-C4H10 decreased as the molecular kinetic diameter of the gases increased. which showed the molecular sieving effect of the NaA zeolite membrane. The permselectivities of H-2/n-C4H10 and O-2/N-2 were 19.1 and 1.8, respectively. These values are higher than the Knudsen diffusion ratios of 5.39 and 0.94. However, the permeation of n-C4H10 also indicated that the NaA zeolite membrane had certain defects with diameters larger than the pore size of NaA zeolite. A synthesis model was proposed to clarify the effect of surface seeding. (C) 2001 Elsevier Science B.V. All rights reserved.

Performance of a mixed-conducting ceramic membrane reactor with high oxygen permeability for methane conversion

A mixed-conducting perovskite-type Ba0.5Sr0.5Co0.8Fe0.2O3-delta (BSCFO) ceramic membrane reactor with high oxygen permeability was applied for the activation of methane. The membrane reactor has intrinsic catalytic activities for methane conversion to ethane and ethylene. C-2 selectivity up to 40-70% was achieved, albeit that conversion rate were low, typically 0.5-3.5% at 800-900 degreesC with a 50% helium diluted methane inlet stream at a flow rate of 34 ml/min. Large amount of unreacted molecular oxygen was detected in the eluted gas and the oxygen permeation flux improved only slightly compared with that under non-reactive air/He experiments. The partial oxidation of methane to syngas in a BSCFO membrane reactor was also performed by packing LiLaNiO/gamma -Al2O3 with 10% Ni loading as the catalyst. At the initial stage, oxygen permeation flux, methane conversion and CO selectivity were closely related with the state of the catalyst. Less than 21 h was needed for the oxygen permeation flux to reach its steady state. 98.5% CH4 conversion, 93.0% CO selectivity and 10.45 ml/cm(2) min oxygen permeation flux were achieved under steady state at 850 degreesC. Methane conversion and oxygen permeation flux increased with increasing temperature, No fracture of the membrane reactor was observed during syngas production. However, H-2-TPR investigation demonstrated that the BSCFO was unstable under reducing atmosphere, yet the material was found to have excellent phase reversibility. A membrane reactor made from BSCFO was successfully operated for the POM reaction at 875 degreesC for more than 500h without failure, with a stable oxygen permeation flux of about 11.5 ml/cm(2) min. (C) 2001 Elsevier Science B.V. All rights reserved.

Novel porous metal/ceramic membrane materials

During the past 22 months, the preparation and application of novel porous metal/ceramic membrane materials have been extensively explored in the area of membrane science and catalysis. Thus, new preparation methods and new application concepts in membrane catalysis have been developed.