261 resultados para Ti-sapphire


Relevância:

20.00% 20.00%

Publicador:

Resumo:

Ti-based icosahedral quasicrystalline phase (I-phase) exhibited excellent hydrogen storage property for special structure. Unfortunately, the application as the negative electrode material of the nickel-metal hydride batteries was limited due to the poor electrochemical kinetics. Meanwhile, rare-earth element was beneficial to the electrochemical properties of Ti, Zr-based alloy.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

对急冷凝固方法、熔融纺丝法、机械合金化法等制备Ti-Zr-Ni基准晶合金的方法进行探讨,综述了几种Ti-Zr-Ni基准晶合金的热力学和电化学贮氢性能

Relevância:

20.00% 20.00%

Publicador:

Resumo:

采用铜辊快速凝固方法制备了Ti45Zr30Ni25和Ti50Zr25Ni25合金,并对合金作为镍-氢二次电池负极的动力学和电化学性能进行了研究。结果表明,Ti45Zr30Ni25为非晶相合金,Ti50Zr25Ni25合金由准晶相和非晶相组成。两合金电极的最大放电容量分别为129和132mAh/g。在240mA/g电流密度下,高倍率放电性能(HRD)分别为62.7%和63.3%。合金电极的交换电流密度分别为205.1和375.6mA/g,氢在合金中的扩散系数分别为5.4×10-11和5.8×10-11cm2·s-1

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Ti40Cu40Ni10Zr10-xScx (x = 0.5 and 1, at%) alloys were prepared by copper mould casting method. Microstructures of the phi 3 mm rod alloys were investigated by XRD and SEM. The results showed that the phi 3 mm rods were glassy matrix with TiCu crystalline phase. Mechanical properties were studied by compressive test. Ti40Cu40Ni10Zr9Sc1 alloy exhibited good compressive strength over 2200 MPa and superior compressive deformation is about 7.9%.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Ti45Zr35Ni20-xPdx (x = 0, 1, 3, 5 and 7, at%) alloys were prepared by melt-spinning. The phase structure and electrochemical hydrogen storage performances of melt-spun alloys were investigated. The melt-spun alloys were icosahedral quasicrystalline phase, and the quasi-lattice constant increased with increasing x value. The maximum discharge capacity of alloy electrodes increased from 79 mAh/g (x = 0) to 148 mAh/g (x = 7). High-rate dis-chargeability and cycling stability were also enhanced with the increase of Pd content. The improvement in the electrochemical hydrogen storage characteristics may be ascribed to better electrochemical activity and oxidation resistance of Pd than that of Ni.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Ti-Zr-Co alloys have been fabricated and characterized, and their catalytic performance was discussed for the oxidation of cyclohexane with oxygen under solvent-free condition. The icosahedral quasicrystalline phase (I-phase)-forming ability of Ti-Zr-Co alloys with different compositions was discussed, and it was confirmed that I-phase could be formed as a dominating phase at the Ti-rich composition region from Ti53Zr27Co20 to Ti75Zr5Co20 in as-cast alloys. The composition and microstructure of Ti-Zr-Co alloys present crucial influences on its catalytic activity and selectivity in the oxidation of cyclohexane. The influences of some reaction parameters such as temperature, reaction time, and catalyst amounts were also investigated. Ti70Zr10Co20 alloy containing quasicrystal microstructure showed good catalytic performance with a 6.8% conversion of cyclohexane and 90.4% selectivity of cyclohexanol and cyclohexanone. It behaves as an efficient heterogeneous catalyst for the oxidation of cyclohexane and could be recycled five times without loss in activity and selectivity.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Ti44Zr32Ni22Cu2 and Ti41Zr29Ni28Cu2 alloys were prepared by the melt-spinning method. The phase structure was analyzed by X-ray diffraction, and the electrochemical performances of the melt-spun alloys were investigated. The results indicated that the Ti44Zr32Ni22Cu2 alloy was composed of the icosahedral quasicrystals and amorphous phases, and the Ti41Zr29Ni28Cu2 alloy comprised icosahedral quasicrystals, amorphous, and Laves phases. The maximum discharge capacity was 141 mAh/g for the Ti44Zr32Ni22Cu2 alloy and 181 mAh/g for the Ti41Zr29Ni28Cu2 alloy, respectively. The Ti41Zr29Ni28Cu2 alloy also showed a better high-rate dischargeabifity and cycling stability. The better electrochemical properties should be ascribed to the high content of Ni, which was beneficial to the electrochemical kinetic properties and made the alloy more resistant to oxidation, as well as to the Laves phase in the Ti41Zr29Ni28Cu2 alloy, which could work as the electro-catalyst and the micro-current collector.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Ti基准晶材料具有热力学稳定的正二十面体构造,表现出特殊的传输特性、贮氢特性和力学特性等,相关研究受到广泛关注.近年,作者所在研究组在Ti基准晶的制备和贮氢性能研究方面取得了一些新进展.综合报道了Ti-Zr-Ni-Cu系准晶相及其复合相材料的制备和贮氢性能.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Effect of cerium on the microstructure and electrochemical performance of the Ti0.25V0.35-xCexCr0.1Ni0.3 (x = 0, 0.005) electrode alloy was investigated by X-ray diffraction (XRD), field emission scanning electron microscopy/energy dispersive X-ray spectrometry (FESEM-EDS), and electrochemical impedance spectroscopy (EIS) measurements. On the basis of XRD and FESEM-EDS analysis, the alloy was mainly composed of V-based solid solution with body-centered-cubic structure and TiNi-based secondary phase. Ce did not exist in two phases, instead, it existed as Ce-rich small white particles, with irregular edges, distributed near the grain boundaries of the V-based solid solution phase. Discharge capacity, cycle stability, and high-rate discharge ability of the alloy electrode were effectively improved with the addition of Ce at 293 K. It was very surprising that the charge retention was abnormal with larger discharge capacity after standing at the open circuit for 24 h. EIS indicated that addition of Ce improved the dynamic performance, which caused the charge transfer resistance (R-T) to decrease and exchange current density (I-0) to increase markedly. The exchange current density of the electrochemical reaction on the alloy surface with Ce addition was about 2.07 and 3.10 times larger than that of the alloy without Ce at 303 and 343 K, respectively.