Rare-earth-doped silica microchip laser fabricated by sintering nanoporous glass

We report a new method for fabricating rare-earth-doped silica glasses for laser materials obtained by sintering nanoporous silica glasses impregnated with rare-earth-doped ions. The fabricated materials have no residual pores and show good optical and mechanical properties. Good performance from a Nd3+-doped silica microchip laser operating at 1.064 mum is successfully demonstrated, suggesting that the fabricated silica glasses have potential for use as active materials for high-power solid-state lasers. (C) 2005 Optical Society of America.

Yb：YAG晶体的闪烁特性

通过不同Yb^3＋掺杂浓度（5％-30％，原子数分数）的Yb：YAG晶体的阴极射线发光谱、衰减时间、光输出及其温度依赖关系的测量，研究了Yb：YAG晶体的闪烁性能。不同Yh^3＋掺杂浓度的Yb：YAG晶体具有不同的光输出和猝灭温度，光输出随Yb^3＋掺杂浓度的增大而降低，猝灭温度则随掺杂浓度的增大而升高。室温下Yb：YAG晶体的发光衰减时间较短，均小于50ns。Yb^3＋掺杂浓度为5％的Yb：YAG晶体具有较高的光输出和较低的猝灭温度。

高浓度掺Er^3＋铌酸锂晶体的光谱参数计算

用提拉法成功地生长了6mol％的高浓度掺铒铌酸锂晶体。测量了晶体的两个非偏振方向（X和Z）以及两个偏振方向（π和δ）的吸收光谱。高浓度掺铒铌酸锂晶体的吸收系数高，有利于提高泵浦效率。根据所测的吸收光谱用Judd-Ofelt理论拟合出了Er^3＋离子的强度参数Ωλ。所得的均方差结果显示偏振拟合的误差要小于非偏振拟合。利用偏振吸收数据计算了各能级跃迁的自发辐射跃迁几率（AJJ’）、辐射寿命（τ）、荧光分支比（β）和积分发射截面（σp）等参数，对计算结果进行了讨论并与其他文献的报道结果进行了比较。

Nd：YAG透明陶瓷的烧成及其显微结构

由溶胶一凝胶／燃烧合成结合法合成了Nd：YAG(掺钕钇铝石榴石，neodymium—doped yttrium aluminium garnet)粉体，用真空烧结法制备了Nd：YAG透明陶瓷。研究了显微结构随烧结温度和保温时间的变化，并对透明陶瓷的晶界结构和成分分布进行了表征。随着烧结温度的提高和保温时间的延长，Nd：YAG陶瓷的密度增大，晶形发育完整，透过率提高。晶粒内部和晶界的化学组成基本相同。所制备的Nd：YAG透明陶瓷在激光工作波长1064nm的透过率达到75％。

Yb：YAG及Cr，Yb：YAG晶体的发光特性

研究了室温下Yb：YAG的上转换荧光光谱，此荧光归因于Yb^3＋离子的“合作”发光和Yb抖离子到稀土杂质离子的能量转移。测试了Yb；YAG晶体的X射线荧光，发光峰对应于电荷迁移态到Yb^3＋离子的基态、激光态间的跃迁。研究了Cr，Yb：YAG晶体的荧光光谱。讨论了Cr^4＋激光输出的可能性。

Tm：YAG晶体的研究进展

Tm：YAG晶体是性能优异的LD泵浦激光晶体。本文总结了Tm：YAG晶体的生长、光谱性质以及激光性能的研究和发展，并指出了Tm：YAG晶体发展中需要解决的问题。

Er^3＋掺杂钨酸铅晶体的发光和光谱特征

本试验测试了Er^3＋掺杂钨酸铅晶体（PbWO4：Er^3＋）的吸收光谱，依据J-O理论，首次计算报道了光谱项特征：J-O强度参数、量子荧光效率、荧光分支比等，Ω2=3．75×10^-20cm^2，Ω4=0．67×10^-20cm^2，Ω6=0．41×10^-20cm^2。计算证实，PWO：Er^3＋中几乎有80％的激发能量非辐射跃迁转移致^4I13／2能级，^4I13／2的计算寿命是5200μs，J-O计算显示，在PWO中产生^4I13/2→^4I15/2和发射1．53μm．有高的几率。讨论了不同浓度E

Optimization of thermal environment during crystal growth of large-sized Nd : YAG by Temperature Gradient Technique

A finite-element model is employed to analysis the thermal environments in Temperature Gradient Technique (TGT) furnace during the growth of large-sized Nd:YAG crystal. The obtained results show that when the crucible is located at the lower position inside of the heater, a flatter solid-liquid interface is established, which makes it easier to obtain the core-free Nd:YAG crystal. Meanwhile, the lower crucible position can induce higher axial temperature gradient, which is beneficial to the release of latent heat. (c) 2007 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Diode-pumped passively q-switched Nd : YAG ceramic laser with a Cr4+: YAG crystal-satiable absorber

Transparent polycrystalline Nd:YAG ceramics were fabricated by solid-state reactive sintering a mixture of commercial Al2O3,Y2O3, and Nd2O3 powders. The powders were mixed in ethanol and doped with 0.5 wt% tetraethoxysilane, dried, and pressed. Pressed samples were sintered at 1750 degrees C in vacuum. Transparent fully dense samples with average grain sizes of 10 mu m were obtained. The 1 at.% Nd:YAG ceramic was used to research passively Q-switched laser output with a Cr4+:YAG crystal as a saturable absorber. An average output power of 94 mW with a pulse width of 50 ns was obtained when the incident pump power was 750 mW. The slope efficiency was 13%. The pulse energy is 5 mu J, and the peak power is about 100 W.

Diode-pumped Yb : YAG ceramic laser

Transparent polycrystalline Yb:YAG ceramics were fabricated by solid-state reactive sintering a mixture of commercial Al2O3, Y2O3, and Yb2O3 powders. The powders were mixed in ethanol and doped with 0.5 wt% tetraethoxysilane, dried, and pressed. Pressed samples were sintered at 1730 degrees C in vacuum. Transparent fully dense samples with grain sizes of several micrometers were obtained. The phase from 1500 degrees to 1700 degrees C was important for the grain growth, in which the grains grew quickly and a mass of pores were eliminated from the body of the sample. Annealing was an important step to remove the vacancies of oxygen and transform Yb2+ to Yb3+. The 1 at.% Yb:YAG ceramic sample was pumped by a diode laser to study the laser properties. The maximum output power of 1.02 W was obtained with a slope efficiency of 25% at 1030 nm. The size of the lasering sample was 4 mm x 4 mm x 3 mm.

Infrared to visible upconversion fluorescence in Yb,Tm : YAG single crystal

Absorption spectrum from 400 to 2000 run and upconversion fluorescence spectra under 940 nm pumping of YAG single crystal codoped with 5 at.% Yb3+ and 4 at.% Tm3+ were studied at room temperature. The blue upconversion emission centered at 483 nm corresponds to the transition (1)G(4) -> H-3(6), the emission band around 646 nm corresponds to the transition (1)G(4) -> F-3(4) of Tm3+. Energy transfer from Yb3+ to Tm3+ is mainly nonradiative and the transfer efficiency was experimentally assessed. The line strengths, transition probabilities and radiative lifetimes of (1)G(4) level were calculated by using Judd-Ofelt theory. Gain coefficient calculated from spectra shows that the upconversion corresponding with transitions (1)G(4) -> H-3(6) in YAG doped with Yb3+ and Tm3+ is potentially useful for blue light Output. (c) 2006 Elsevier B.V. All rights reserved.

Gamma-irradiation effects on Ce-doped YAG crystals grown by Cz and TGT method

Gamma-rays radiation effects on Ce:YAG crystals grown by Czochralski (Cz) and temperature gradient techniques (TGT) have been studied by means of optical absorption and luminescence spectra. Valence of Ce3+ ion changes during the gamma-ray irradiation process and this result indicates Ce4+ ion may exist in both Cz-Ce:YAG and TGT-Ce:YAG crystals. Thermally stimulated luminescence measurements reveal intense thermoluminescence peaks in gamma-irradiated Ce:YAG crystals and trap parameters were calculated by general-order kinetics expression. (C) 2006 Elsevier B.V. All rights reserved.

Yb：YAG透明陶瓷的制备和激光输出

制备了高质量的Yb：YAG透明陶瓷．Yb：YAG透明陶瓷的晶粒尺寸为10μm左右且分布均匀，晶界处和晶粒中没有杂质、气孔的存在．Yb：YAG样品中所有元素分布均匀，不同的晶粒间，晶粒和晶界间成分是一致的，没有出现成分的偏析．4mm厚样品的透过率为80％．LD泵浦获得了波长为1030nm，最大功率为268mW的连续激光输出．

温度梯度法生长Nd：YAG激光晶体的核心分布

用温度梯度法生长了直径为75mm大尺寸的Nd：YAG激光晶体，通过退火排除了生长过程中进入晶体的碳原子．用正交偏光显微镜观察了晶体的核心分布以及生长条纹．测试了室温下的吸收谱并利用吸收谱研究了Nd离子在YAG晶体中的分布．比较了温度梯度法与提拉法生长晶体的区别．

国产Yb∶YAG透明陶瓷实现激光输出

YAG单晶是高功率激光的重要材料，近年来高透明度多晶陶瓷作为激光介质引起人们广泛的注意。YAG陶瓷相对单晶具有易制造大尺寸、掺杂浓度高、易批量生产等优点。在Nd：YAG陶瓷获得长足发展的同时，Yb掺杂的陶瓷也得到了越来越多的关注。Yb：YAG陶瓷与Nd：YAG陶瓷相比具有许多优点：Yb掺杂的激光介质无交叉弛豫振荡和激发态吸收，有较宽的吸收带，较长的荧光寿命及较高的量子效率等。因此，高质量的Yb：YAG陶瓷将是非常理想的高功率激光材料。