Charge-sensitive deep level transient spectroscopy of helium-ion-irradiated silicon, as-irradiated and after thermal annealing

Electrically active defects in the phosphor-doped single-crystal silicon, induced by helium-ion irradiation under thermal annealing, have been investigated. Isothermal charge-sensitive deep-level transient spectroscopy was employed to study the activation energy and capture cross-section of helium-induced defects in silicon samples. It was shown that the activation energy levels produced by helium-ion irradiation first increased with increasing annealing temperature, with the maximum value of the activation energy occurring at 873K, and reduced with further increase of the annealing temperature. The energy levels of defects in the samples annealed at 873 and 1073K are found to be located near the mid-forbidden energy gap level so that they can act as thermally stable carrier recombination centres.

Formation of Au nanoparticles in sapphire by using Ar ion implantation and thermal annealing

In this paper, we present results of the synthesis of gold nanoclusters in sapphire, using Ar ion implantation and annealing in air. Unlike the conventional method of Au implantation followed by thermal annealing, Au was deposited on the surface of m- and a- cut sapphire single crystal samples including those pre-implanted with Ar ions. Au atoms were brought into the substrate by subsequent implantation of Ar ions to form Au nanoparticles. Samples were finally annealed stepwisely in air at temperatures ranging from 400 to 800 C and then studied using UV–vis absorption spectrometry, transmission electron microscopy and Rutherford backscattered spectrometry. Evidence of the formation Au nanoparticles...

The influence of the microstructure evolution on the surface morphology in the annealing process of helium-implanted spinel

Single-crystalline spinel (MgAl2O4) specimens were implanted with helium ions of 100 keV at three successively increasing fluences of (0.5, 2.0 and 8.0) x 10(16) ions/cm(2) at room temperature. The specimens were subsequently annealed in vacuum at different temperatures ranging from 500 to 1100 degrees C. Different techniques, including Fourier transformed infrared spectroscopy (FTIR), thermal desorption spectrometry (TDS), atomic force microscopy (AFM) and scanning electron microscopy (SEM) were used to investigate the specimens, It was found that the absorbance peak in the FTIR due to the stretching vibration of the Al-O bond shifts to smaller wave numbers with increasing fluence, shifting back to larger wave numbers with an increase of annealing temperature. The absorbance peak shift has a linear relationship with the fluence increase in the as-implanted state, while it does not have a linear relationship with the fluence increase after the annealing process. Surface deformation occurred in the specimens implanted with fluences of 2.0 and 8.0 x 10(16) ions/cm(2) in the annealing process. The phenomena described above can be attributed to differences in defect formation in the specimens. (C) 2008 Elsevier B.V. All rights reserved.

Annealing effects in silicon implanted with helium

Silicon samples were implanted with helium and analyzed by atomic force microscopy (AFM) and Raman spectroscopy before and after annealing in the range of 523-1273 K. After annealing at 523 K, the amorphous area induced by He-ion implantation at room temperature was partially recovered and grain sizes became larger. The surface morphology was analyzed through AFM measurements and it was observed that root mean square of the surface roughness alters upwards and then downwards with annealing temperature. (C) 2008 Elsevier B.V. All rights reserved.

Effects of annealing on the photoluminescence of He ion implanted sapphire after 230-MeV Pb ion irradiation

Single crystal sapphire (Al2O3) samples implanted with 110 keV He and irradiated at 320 K by Pb-208(27), ions with energy of 1.1 MeV/u to the fluences ranging from 1 X 10(12) to 5 X 10(14) ion/cm(2) and subsequently annealed at 600, 900 and 1100 K. The obtained PL spectra showed that emission peaks centred at 375, 390, 413, and 450 nm appeared in irradiated samples. The peak of 390 ran became very intense after 600 K annealing. The peak of 390 nm weakened and 510 nm peak started to build up at 900 K annealing, the peak of 390 nm vanished and 510 nm peak increased with the annealing temperature rising to 1100 K. Infrared spectra showed a broadening of the absorption band between 460 cm(-1), and 510 cm(-1) indicating strongly damaged regions being formed in the Al2O3 samples and position shift of the absorption band at 1000-1300 cm(-1) towards higher wavenumber after Pb irradiation.

Temperature annealing of tracks induced by ion irradiation of graphite

Highly oriented pyrolytic graphite (HOPG) samples were irradiated by Xe ions of initial kinetic energy of 3 MeV/u. The irradiations were performed at temperatures of 500 and 800 K. Scanning tunneling microscopy (STM) images show that the tracks occasionally have elongated structures under high-temperature irradiation. The track creation yield at 800 K is by three orders of magnitude smaller compared to that obtained during room-temperature irradiation. STM and Raman spectra show that amorphization occurs in graphite samples irradiated at 500 K to higher fluences, but not at 800 K. The obtained experimental results clearly reveal that the irradiation under high temperature causes track annealing.