Synthesis, structure and ring-opening polymerization of phenolphthalein macrocyclic polyarylates

Phenolphthalein based polyarylate macrocyclic oligomers were selectively synthesized by an interfacial polycondensation reaction of o-phthaloyl dichloride with phenolphthalein. The high selectivity benefits from the role of phenolphthalein as a color indicator, an efficient phase transfer catalyst, acid a preferred conformation of the starting materials as indicated by analyzing a single-crystal X-ray structure of an analogous macrocycle. The melt ROP of phenolphthalein polyarylate cyclic dimer was studied using nucleophilic initiators, The molecular weight of the resulting polymers builds up very rapidly at the very early stage of polymerization but decreases with time. During the ROP of cyclic dimer, analogous macrocycles with higher degree of polymerization (n greater than or equal to 3) and linear oligomers were produced by backbiting reaction especially at later stage of polymerization. Conversion of cyclic dimer is very fast at the earlier stage of polymerization and then increases slowly with time as analyzed by gel permeation chromatography. However, the total amount of cyclic oligomers in the ROP system increases with time at the later stage of polymerization because of the formation of larger macrocycles. The resulting polymers are amorphous. Glass transition temperatures (T(g)s) of these polymers are influenced by the polymerization time, type of initiator, and initiator concentration.

Organic-phase enzyme electrode for phenolic determination based on a functionalized sol-gel composite

An amperometric biosensor for monitoring phenols in the organic phase was constructed by the silica sol-gel immobilization of tyrosinase on a glassy carbon electrode. The organic-inorganic hybrid materials with different sol-gel precursors and polymers were optimized, and the experimental conditions, such as the effect of the solvent, operational potential and enzyme loading were explored for the optimum analytical performance of the enzyme electrode. The biosensor can reach 95% of steady-state current in about 18 s, and the trend in the sensitivity of different phenols is as follows: catechol > phenol >p-cresol. In addition, the apparent Michaelis-Menten constants (K-m(app)) and the stability of the enzyme electrode were discussed. (C) 2000 Elsevier Science S.A. All rights reserved.

Effect of compatibilization on the properties of HIPS/PA1010 blends

Blends consisting of high-impact polystyrene (HIPS) as the matrix and polyamide 1010 (PA1010) as the dispersed phase were prepared by mixing. The grafting copolymers of HIPS and maleic anhydride (MA), the compatibilizer precursors of the blends, were synthesized. The contents of the IMA in the grafting copolymers are 4.7 wt % and 1.6 wt %, and were assigned as HAM and LMA, respectively. Different blend morphologies were observed by scanning electron microscopy (SEM); the domain size of the PA1010 dispersed phase in the HIPS matrix of compatibilized blends decreased comparing with that of uncompatibilized blends. For the blend with 25 wt % HIPS-g-MA component, the T-c of PA1010 shifts towards lower temperature, from 178 to 83 degrees C. It is found that HIPS-g-MA used as the third component has profound effect on the mechanical properties of the resulting blends. This behavior has been attributed to the chemical reaction taking place in situ during the mixing between the two components of PA1010 and HIPS-g-MA. (C) 2000 John Wiley & Sons, Inc.

A novel method for preparing ordered SnO2/TiO2 alternate nanoparticulate films

A novel method using LB films as precursors to prepare pure inorganic ordered film with periodic structure was developed. Surfactant-stabilized SnO2 nanoparticulate organosols and TiO2 nanoparticulate organosols were prepared and used as spreading solutions. Using LB technique, the good film-forming ability of the surfactant-stabilized SnO2 nanoparticles and TiO2 nanoparticles was confirmed by the determination of the pi -A isotherms. The surfactant-stabilized SnO2 and TiO2 nanoparticulate monolayers were fabricated on the water surface and then were transferred to solid substrates (CaF2, quartz, silicon, and so on) alternately, layer-by-layer. Then the as-deposited alternate LB film was treated at different temperatures. The as-deposited alternate LB film and the treated film were characterized by Fourier transform infrared spectroscopy, UV visible spectroscopy, X-ray diffraction, and X-ray photoelectron spectroscopy. The results indicate that our method was successful. The as-deposited alternate LB film formed a periodic structure with a long spacing of 6.5 nm that was composed of SnO2 nanoparticles, TiO2 nanoparticles, and arachidic acid. The treated film composed of SnO2 nanoparticles and TiO2 nanoparticles formed a pure inorganic periodic structure with an ordered distance of 5.4 nm. (C) 2001 Academic Press.

Crosslinking of polyimides via spirodilactone unit in polymer backbone

A new approach for the crosslinking of polyimides via the lactamization of spirodilactone unit in polyimide backbone was studied by two means: model reaction and the comparison of the properties of the polyimide precursors to those of the crosslinking polymers. Polyimides 4 and 5 were soluble in N,N'dimethylacetamide (DMAc), dimethylformamide (DMF), dimethylsulfoxide (DMSO), N'-methylpyrrolidone (NMP), and other common organic solvents, whereas their corresponding crosslinking polymers were insoluble in these solvents. The glass transition temperatures for polyimide 5 and its crosslinking polymer were 262 degrees C and 291 degrees C, whereas those for polyimide 4 and its crosslinking polymer were 265 degrees C and 360 degrees C. The weight-loss rate of the crosslinling polymers was apparently slower than that of the precursors when the temperature was >400 degrees C. The 10% weight-loss temperature for the polyimides 4 and 5 was <500 degrees C, whereas that for the crosslinking polymers was close to or above 600 degrees C. The results indicate that this type of crosslinking polymer has good thermal properties. The temperature for the formation of lactam was above 180 degrees C. (C) 1999 John Wiley & Sons, Inc.

Synthesis and polymerization of some macrocyclic (arylene ether sulfone) containing cardo groups and macrocyclic (arylene ether ketone sulfone) oligomers

Some novel macrocyclic (arylene ether sulfone) containing cardo groups and (arylene ether ketone sulfone) oligomers have been synthesized in high yields by a nucleophilic aromatic substitution reaction of 4,4'-difluorophenylsulfone with bisphenols in the presence of anhydrous potassium carbonate under a pseudo-high-dilution condition. Detailed structural characterization of these oligomers by matrix-assisted laser desorption/ionization-time of flight-mass spectrometry (MALDI-TOF-MS), fast atom bombardment mass spectrometry (f.a.b.-m.s.), nuclear magnetic resonance spectrometry (n.m.r.) and single-crystal X-ray structure analysis confirms their cyclic nature, and the composition of the oligomeric mixtures is provided by g.p.c. analysis. Ring polymerization of cyclic oligomers 3a to a high molecular weight polymer with M-w of 59.1 k was achieved by heating at 290 degrees C for 40 min in the presence of a nucleophilic initiator. (C) 1998 Elsevier Science Ltd. All rights reserved.

X-ray crystallographic structure of meta- and para-dimethyl ester of pyromellitic acid

The polycrystalline powder of para- and meta-dimethyl ester of pyromellitic acid (PMDE) have been prepared by fractional crystallization, and their crystal structures have been determined by Wide-Angle X-ray Diffraction (WAXD). Both p-PMDE and m-PMDE was found to be orthorhombic crystal system, and their unit cell parameters a = 0.840 nm, b = 0.707 nm, c = 1.136 nm and a = 1.032 nm; b = 0.835 nm, c = 0.714 nm, respectively. Space group all belongs to P-mmm. p-PMDE has two molecules per unit cell with crystal density 1.388 g . cm(-3), while m-PMDE has two molecules per unit cell with crystal density 1.522 g . cm(-3). Indices of crystal diffraction peaks are also detailed in the present work. The difference in crystal structures between p-PMDE and m-PMDE has thus been used to explain the curing behavior of isomerically pyromellitic dianhydride-based poly(amic ester)s.

Synthesis and imidization of poly(amic methyl ester)s

The synthesis and characterization of a series of poly(amic methyl ester)s from five aromatic dianhydrides and a diamine, 4,4'-oxydianiline (ODA), are described. These poly(amic ester)s are obtained by the low-temperature polycondensation from dianhydrides derived diester-diacyl chlorides and ODA in DMAc solution with the inherent viscosities in the 0.5-0.9 dL/g range. These precursors are readily soluble in aprotic solvents. A detailed thermal study of the imidization process is presented, based on dynamic and isothermal TGA measurements, FTIR spectroscopy, and dynamic mechanical analysis. (C) 1997 John Wiley & Sons, Inc.

Sol-gel synthesis and luminescence of Y4Al2O9:RE3+(RE=Eu, Tb)

Y4Al2O9 (YAM) was prepared by a sol-gel process, using yttrium and aluminum citrate complexes as precursors. The sol-gel process produced single-phase YAM at 900 degrees C, as opposed to the conventional solid-state reaction, which led to the formation of other phases, even if at 1600 degrees C. The emission and excitation spectra of Eu3+ and Tb3+ in YAM showed the existence of two luminescence centers, agreeing with the crystal structure of YAM. The spectral properties of the samples are discussed.

SYNTHESIS AND CHARACTERIZATION OF TRISUBSTITUTED HETEROPOLYTUNGSTOGERMANATES CONTAINING GROUP 3A ELEMENTS

Six new compounds, alpha,beta-KaHb[GeW(9)M(3)(H2O)(3)O-37]. xH(2)O(M = Al, Ga, In; a + b = 7) and alpha-K9H5[Ge2W18Ga6(H2O)(3)O-74]. 20H(2)O, were synthesized from the lacunary precursors a and beta-GeW9O3410- and characterized by elemental analysis, spectroscopy and electrochemistry. Tungsten-183 NMR spectra of the title complexes consist of two lines with intensity ratio 2:1 as expected for trisubstituted heteropoly anions. The intensity ratio of alpha-Ga compound is 1:2, which is different from others(a:1). With the help of FAB mass spectrum, we concluded that it is a dimer with D-3h structure in aqueous, and the others exist by monomers with C-3v structures.

SYNTHESIS AND CHARACTERIZATION OF ALPHA,BETA-TRIINDIUM SUBSTITUTED HETEROPOLYTUNGSTATES

The complexes of alpha,beta-K(a)H(b)XW(9)O(37)(InH2O)(3) . xH(2)O (X = Si, Ge; a+b = 7) were synthesized from their lacunary precursors alpha,beta-XW(9)O(34)(10-) (X = Si, Ge) and characterized by elemental analysis, W-183 NMR, IR and UV spectroscopy and polarography. W-183 NMR spectra of the title complexes consist of two lines with intensity ratio 2:1, as expected for the C-3 nu structure of trisubstituted A alpha- and A beta-Keggin anions.

CURE AND IONIC-CONDUCTIVITY OF A 2-COMPONENT EPOXY NETWORK POLYMER ELECTROLYTE

In order to raise the room temperature ionic conductivity and improve the mechanical strength of a PEO-based polymer electrolyte, a non-crystalline two-component epoxy network was synthesized by curing diglycidyl ether of polyethylene glycol (DGEPEG) with triglycidyl ether of glycerol (TGEG) in the presence of LiClO4 salt, which acts in this system as both a ring opening catalyst and a source of ionic carrier. The structure of the precursors, the curing process and the cured films have been characterized by C-13 NMR, IR, DSC and ionic conductivity measurement techniques. The electrolyte system exhibits an ionic conductivity as high as similar to 10(-5) S/cm at 25 degrees C and is mechanically self-supportable. The dependence of ionic conductivity was investigated as a function of temperature, salt content, MW of PEG segment in DGEPEG and the proportion of DGEPEG in DGEPEG/TGEG ratio.

ALKYLATION OF ISOBUTANE WITH BUTENE OVER LAYERED DOUBLE HYDROXIDE PILLARED HETEROPOLYOXOMETALATE ACID-BASE CATALYSTS

[Si(W2O7)(6)](8-) pillared LDH structure hydroxides were synthesized by the method of restructuring of the thermally decomposed hydrotalcite-like compounds for Zn-Al and Mg-Al oxide systems. [P(W2O7)(6)](8-) pillared Ni-Al LDH structure hydroxide was synt

2-COMPONENT EPOXY NETWORK-LICLO4 POLYMER ELECTROLYTE

An epoxy network-LiClO4 electrolyte system was prepared from diglycidyl ether of polyethylene glycol and triglycidyl ether of glycerol, cured in the presence of LiClO4 only. Various techniques were used to characterize the chemical structure of the precursors and the correlation between the viscoelasticity and conductivity of the cured films was examined.

SYNTHESES OF METHYLCYCLOPENTADIENYL DERIVATIVES OF LANTHANIDES (LN = LA-ND) AND CRYSTAL-STRUCTURES OF [(THF)2LI(MU-CL)2]2[MECPND(THF)] AND [LI(DME)3][MECPLA(NPH2)3]

The reaction of LnCl3.2LiCl with 1 equiv of MeCpNa in THF gives the complexes [(THF)2Li(mu-Cl)2]2[MeCpLn(THF)] (Ln = Nd (1), La (2)) in good yield. These precursors react further with 2 equiv of LiNPh2 to produce the new complexes [Li(DME)3][MeCpLn(NPh2)3] (Ln = La (3), Pr (4), Nd (5)). They have been characterized by elemental analyses and IR and NMR spectra, as well as by structural analyses of 1 and 3. The chloride 1 crystallizes in the monoclinic space group P2(1)/n (No. 14) with a = 12.130 (5) angstrom, b = 17.343 (5) angstrom, c = 17.016 (5) angstrom, beta = 108.54 (3)-degrees, V = 3393.87 angstrom3, Z = 4, and D(c) = 1.45 g/cm3. Least-squares refinement led to a final R value of 0.051 (I greater-than-or-equal-to 3-sigma(I(o))) for 2004 independent reflections. Complex 3 crystallizes in the monoclinic space group P2(1)/c (No. 14) with a = 18.335 (6) angstrom, b = 16.576 (5) angstrom, c = 17.461 (6) angstrom, beta = 96.04 (3)-degrees, V = 5277.17 angstrom3, D(c) = 1.26 g/cm3, Z = 4, and R = 0.057 (I greater-than-or-equal-to 2.5-sigma(I(o))) for 3378 reflections. The structure of 3 consists of discrete ion pairs [Li(DME)3]+ and [MeCpLa(NPh2)3]- with average La-N and La-C(ring) distances of 2.459 (8) and 2.84 (1) angstrom, respectively.