Spectroscopic properties of Yb:YAP crystal

The 10at% Yb-YAP crystal has been grown by the Czochralski method. The absorption and emission spectra and fluorescence lifetime of Yb:YAP crystal at room temperature were studied. There is a strong absorption band centered at 959 nm and the absorption cross-section of 1.51 × 10^-20 cm². The emission cross-section at 1040 nm is 0.6 × 10^-20 cm² and the fluorescence lifetime is about 1.2 ms. The effects of O₂-annealing on the spectral properties were studied. The spectroscopic properties strongly depended on the axis direction and b axis was the best direction for laser output. The spectrum parameters of Yb:YAP and Yb:YAG crystal were compared.}

Er^3＋／Yb^3＋共掺的氧化镧钇透明陶瓷的光谱性能研究

采用传统无压烧结工艺制备了Er^3＋／Yb^3＋共掺的氧化镧钇透明陶瓷并对其光谱性能进行了研究．样品具有较大的吸收和发射截面．La2O3的添加使样品的荧光寿命（τs）与玻璃接近，当Yb^3＋和Er^3＋的掺杂量分别为5at％和0．5at％时，测得τs=9．65ms．这种荧光寿命长、发射截面大和线宽窄的特性有利于微型、可集成化和大功率激光输出的实现．

Yb:YAP与Yb:YAG晶体光谱性能比较

应用中频感应提拉法生长出掺杂浓度为10 at.-%的Yb:YAG与Yb:YAP晶体，对比了室温下两种晶体的吸收和发射光谱特性。结果表明，Yb:YAG晶体比Yb:YAP晶体有更好的激光性能和低的阈值；同时对比发现，Yb:YAP晶体的吸收截面是Yb:YAG晶体的2.16倍，它容易实现LD泵；由于Yb:YAP晶体的各向异性，它有轴向效应明显，它可以产生偏振激光。

Nd：YbVO4晶体的拉曼光谱和荧光光谱研究

用群论的方法计算了Nd：YbVO4晶体的拉曼活性振动模数目，在室温下测得了其极化拉曼谱线，并指认了在不同几何配置下，各振动模式所对应的频率。同时，测得了室温下晶体的吸收谱，得到了中心波长为808am吸收峰的半高宽为12nm，并在J-O理论的基础上计算了晶体的光学参数，其三个晶场参数分别为Ω2=6．88945×10^-20cm^2。Ω4=4．13394×10^-20cm^2、Ω6=4．54503×10^-20cm^2，并由此得到^4F3／2能级的荧光寿命为178．69炉，1062nm处的荧光分支比为48．85％，积分发射截面为2．786710^-18cm^2。分别在808nm、940nm激发下测得晶体室温发射谱，观察到了Nd→Yb以及Nd←Yb间的能量传递现象。