Oxidative destruction of chlorobenzene and o-dichlorobenzene on a highly active catalyst: MnOx/TiO2-Al2O3

A highly active catalyst, MnOx/TiO2-Al2O3, was prepared by impregnating MnOx species on TiO2-modified Al2O3. The TiO2 species in TiO2-Al2O3 support is in a monolayer dispersion, and the MnOx species is again highly dispersed on TiO2-Al2O3 Support. The total oxidation of chlorobenzene and o-dichlorobenzene on MnOx/TiO2-Al2O3 catalyst can be achieved at 300 degreesC and 250 degreesC respectively, at the space velocity of 8000 h(-1). The activity of MnOx/TiO2-Al2O3 catalyst (Mn loading 11.2 wt%) is gradually increased in the first 10-20 h and then keeps stable at least for the measured 52 h at 16,000 h(-1). Furthermore, no chlorinated organic byproducts are detected in the effluent during the oxidative destruction of chlorobenzene and o-dichlorobenzene. It is proposed that the partially chlorinated and highly dispersed manganese oxide on a monolayer TiO2-modified Al2O3 is responsible for the high and stable activity for the total oxidation of chlorinated aromatics. (C) 2001 Academic Press.

Isospecific polymerization of styrene with modified ziegler-type catalysts

Effects of various kinds of additives as well as aging of the catalyst on the polymerization of styrene catalyzed by TiCl4/MgCl2-AlEt3 system have been studied. Experiments show that in toluene the isotacticity of polystyrene can be up to 83% for aged catalyst, whereas when the catalyst is not aged. non-stereospecific polymer is the main product. When PCl3 is used as an additive, the catalyst system gives high activity and isotacticity. The use of a mixture of AlEt3/H2O (1: 1 mole ratio) as a cocatalyst is also efficient. The catalyst [TiCl4-PCl3/MgCl2-AlEt3/H2O] displays high activity and product isotacticity (94%) with an average molecular weight up to 2 X 10(-6). When Co(acac)(3) is added to to [TiCl4/MgCl2-AlEt3] catalyst after it was aged, the isotacticity can be up to 97%. (C) 2001 Elsevier Science Ltd. All rights reserved.

High-throughput screening of HZSM-5 supported metal-oxides catalysts for the coupling of methane with CO to benzene and naphthalene

High-throughput screening of HZSM-5 supported metal-oxides catalysts were carried out for the coupling reaction of methane with CO to aromatics in a multi-stream reactor system. Zn/HZSM-5 and Mo/HZSM-5 were observed to be rather effective for the catalytic formation of aromatics from the coupling reaction of methane with CO. Temperature-programmed reaction has further proven the efficiency of the coupling of methane and CO over Zn/HZSM-5 catalyst. The results were also validated in a conventional fixed-bed reactor coupled with GC. The results propose that the coupling methane with CO toward benzene and naphthalene can be catalyzed by Zn/HZSM-5 at 500 ° C. Both methane and CO are needed for the formation of reactive coke on the catalyst, and the reactive coke may be the initial product in the producing of hydrocarbons. © 2005 Elsevier B.V. All rights reserved.

Preparation and characterization of multi-walled carbon nanotubes supported PtRu catalysts for proton exchange membrane fuel cells

A series of PtRu nanocomposites supported on H2O2-oxidized multi-walled carbon nanotubes (MWCNTs) were synthesized via two chemical reduction methods - one used aqueous formaldehyde (HCHO method) and the other used ethylene glycol (EG method) as the reducing agents. The effects of the solvents (water and ethylene glycol) and the surface composition of the MWCNTs on the deposition and the dispersion of the metal particles were investigated using N-2 adsorption. TEM. ICP-AES. FTIR and TPD. The wetting heats of the MWCNTs in corresponding solvents were also measured. The characterizations suggest that combination of the surface chemistry of the MWCNTs with the solvents decides the deposition and the dispersion of the metal nanoparticles. These nanocomposites were evaluated as proton exchange membrane fuel cell anode catalyts for oxidation of 50 ppm CO contaminated hydrogen and compared with a commercial PtRu/C catalyst. The data reveal superior performances for the nanocomposites prepared by the EG method to those by the HCHO method and even to that for tile Commercial analogue. Structure performance relationship of the nanocomposites was also studied. (C) 2005 Elsevier Ltd. All rights reserved.

Preparation of supported PtRu/C electrocatalyst for direct methanol fuel cells

In this work, high-surface supported PtRu/C were prepared with Ru(NO)(NO3)(3) and [Pt(H2NCH2CH2NH2)(2)]Cl-2 as the precursors and hydrogen as a reducing agent. XRD and TEM analyses showed that the PtRu/C catalysts with different loadings possessed small and homogeneous metal particles. Even at high metal loading (40 wt.% Pt, 20 wt.% Ru) the mean metal particle size is less than 4 nm. Meanwhile, the calculated Pt crystalline lattice parameter and Pt (220) peak position indicated that the geometric structure of Pt was modified by Ru atoms. Among the prepared catalysts, the lattice parameter of 40-20 wt.% PtRu/C contract most. Cyclic voltammetry (CV), chronoamperometry (CA), CO stripping and single direct methanol fuel cell tests jointly suggested that the 40-20 wt.% PtRu/C catalyst has the highest electrochemical activity for methanol oxidation. (c) 2004 Elsevier Ltd. All rights reserved.

Structure and chemical composition of supported Pt-Sn electrocatalysts for ethanol oxidation

Carbon supported PtSn alloy and PtSnOx particles with nominal Pt:Sn ratios of 3:1 were prepared by a modified polyol method. High resolution transmission electron microscopy (HRTEM) and X-ray microchemical analysis were used to characterize the composition, size, distribution, and morphology of PtSn particles. The particles are predominantly single nanocrystals with diameters in the order of 2.0-3.0 nm. According to the XRD results, the lattice constant of Pt in the PtSn alloy is dilated due to Sn atoms penetrating into the Pt crystalline lattice. While for PtSnOx nanoparticles, the lattice constant of Pt only changed a little. HRTEM micrograph of PtSnOx clearly shows that the change of the spacing of Pt (111) plane is neglectable, meanwhile, SnO2 nanoparticles, characterized with the nominal 0.264 nm spacing of SnO2 (10 1) plane, were found in the vicinity of Pt particles. In contrast, the HRTEM micrograph of PtSn alloy shows that the spacing of Pt (111) plane extends to 0.234 nm from the original 0.226 nm. High resolution energy dispersive X-ray spectroscopy (HR-EDS) analyses show that all investigated particles in the two PtSn catalysts represent uniform Pt/Sn compositions very close to the nominal one. Cyclic voltammograms (CV) in sulfuric acid show that the hydrogen ad/desorption was inhibited on the surface of PtSn alloy compared to that on the surface of the PtSnOx catalyst. PtSnOx catalyst showed higher catalytic activity for ethanol electro-oxidation than PtSn alloy from the results of chronoamperometry (CA) analysis and the performance of direct ethanol fuel cells (DEFCs). It is deduced that the unchanged lattice parameter of Pt in the PtSnOx catalyst is favorable to ethanol adsorption and meanwhile, tin oxide in the vicinity of Pt nanoparticles could offer oxygen species conveniently to remove the CO-like species of ethanolic residues to free Pt active sites. (C) 2005 Elsevier Ltd. All rights reserved.

Enhancement of the catalytic performance of supported-metal catalysts by pretreatment of the support

We report an interesting finding that the catalytic performance of supported Ag/SiO2 catalysts toward selective catalytic oxidation of CO in hydrogen at low temperatures can be greatly enhanced by pretreatment of the SiO2 support before catalyst preparation. Calcination of SiO2 at appropriate temperatures preferentially removes the H-bonded SiOH, which results in the highly dispersive Ag/SiO2 catalyst and thus improves the catalytic performance. (c) 2005 Elsevier Inc. All rights reserved.

The effect of Rh particle size on the catalytic performance of porous silica supported rhodium catalysts for CO hydrogenation

Silica-supported Rh catalysts with different Rh particle dimensions were investigated for CO hydrogenation. The catalysts were characterized by various techniques such as TEM, H-2-TPR and N-2 adsorption to study the catalyst morphology, the size distributions of Rh particles and the silica pores. It was found that the distribution and the size of Rh particles were affected by the silica pores, and the metal grains were enclosed in the pores of the support, and thereby their growth was limited. The catalytic activity and selectivity to C-2-oxygenates for CO hydrogenation were found to be significantly controlled by the Rh particle sizes, and the higher activity and selectivity to C2-oxygenates were obtained over bigger Rh particles, within the range of the reported particle sizes.

Factors influencing the catalytic activity of SBA-15-supported copper nanoparticles in CO oxidation

Copper nanoparticles were deposited onto mesoporous SBA-15 support via two different routes: post-grafting method and incipient wet impregnation method. Both XRD and TEM reveal that the post-grafting can make Cu particles very small in size and highly dispersed into channels of SBA-15, while the impregnation method mainly forms large Cu particles on the external surface of SBA-15. TPR experiments show that CuO species formed by the post-grafting method is more reducible than that prepared by the impregnation method. The catalytic activity tests for CO oxidation manifests that the sample prepared by the post-grafting method has a much higher activity than that prepared by the impregnation method, with a lowering of 50 degrees C for T-50, showing a strong dependence of catalytic activity on the size and dispersion of Cu particles. Besides the preparation procedure, other factors including calcination temperature, reduction treatment, copper loading as well as the feed composition, have an important effect on the catalytic activity. The best performance was obtained when the catalyst was calcined at 500 degrees C and reduced at 550 degrees C. The calcination and reduction treatment at high temperature have been found to be necessary to completely remove the organic residue and to generate active metallic copper particles. (c) 2005 Elsevier B.V. All rights reserved.