Naphthalene-Based Poly(arylene ether ketone) Copolymers Containing Sulfobutyl Pendant Groups for Proton Exchange Membranes

A new monomer 1,5-bis(4-fluorobenzoyl)-2,6-dimethoxynaphthalene (DMNF) was prepared and further polymerized to form naphthalene-based poly(arylene ether ketone) copolymers containing methoxy groups (MNPAEKs). The side-chain-type sulfortated naphthalene-based poly(arylene ether ketone) copolymers (SNPAEKs) were obtained by demethylation and sulfobutylation. Flexible and tough membranes with reasonably high mechanical strength were prepared. The SNPAEKs membrane showed anisotropic membrane swelling with larger swelling in thickness than in plane. Transmission electron microscopy (TEM) analysis revealed clear nano-phase separated structure of SNPAEKs membranes, which composed of hydrophilic side chain and hydrophobic main-chain domains.

Effect of hydroxyl and amino groups on electrochemiluminescence activity of tertiary amines at low tris(2,2 '-bipyridyl)ruthenium(II) concentrations

ECL of several amines containing different numbers of hydroxyl and amino groups was investigated. N-butyldiethanolamine is found to be more effective than 2-(dibutylamino)ethanol at gold and platinum electrodes, and is the most effective coreactant reported until now. Surprisingly, ECL intensities of monoamines, such as 2-(dibutylamino)ethanol and N-butyldiethanolamine, are much stronger than that of diamines including N,N,N',N'-tetrakis-(2-hydroxyethyl)-ethylenediamine and N,N,N',N'-tetrakis-(2-hydroxypropyl)ethlenediamine. The striking contrast between ECL signals of the investigated monoamines and diamines may result from more significant side reactions of diamines, such as the intramolecular side reactions between oxidative amine cation radicals and reductive amine free radicals.

Simulation of Banded Spherulite Patterns by Coupled Logistic Map Lattice Model in Three Dimensions

Banded spherulite patterns are simulated in three dimensions by means of a Coupled Logistic map lattice model. The patterns obtained by numerical calculation are consistent with those in experiments. The simulation results also indicate that the hand spacing is decreased with the increase of parameter mu in the Logistic map and increased with the increase of the coupling parameter e for cube lattices, and increased with the increase of the thickness of the lattice for polymer film, which is quite similar to the results in some experiments. Spiral pattern in three dimensions is also shown in this paper, which helps us understand the form of banded spherulite in polymers.

STUDY OF COARSENING OF MICRODOMAINS IN BLOCK COPOLYMERS BY LATTICE BOLTZMANN METHODS

In order to understand the coarsening of microdomains in symmetric diblock copolymers at the late stage, a model for block copolymers is proposed. By incorporating the self consistent field theory with the free energy approach Lattice Boltzmann model, hydrodynamic interactions can be considered. Compared with models based on Ginzburg-Landau free energy, this model does not employ phenomenological free energies to describe systems. The model is verified by comparing the simulation results obtained using this method with those of a dynamical version of the self consistent mean field theory. After that,the growth exponents of the characteristic domain size for symmetric block copolymers at late stage are studied. It is found that the viscosity of the system affects the growth exponents greatly, although the growth exponents are all less than 1/3 Furthermore, the relations between the growth exponent, the interaction parameter and the chain length are studied.

Bonding Characteristics, Thermal Expansibility, and Compressibility of RXO4 (R = Rare Earths, X = P, As) within Monazite and Zircon Structures

Systematically theoretical research was performed on the monazite- and zircon-structure RXO4 (R = Sc, Y, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu; X = P, As) series by using the chemical bond theory of dielectric description. The chemical bond properties of R-O and X-O bonds were presented. In the zircon phase, the covalency fractions of X-O bonds increased in the order of V-O < As-O < P-O, which was in accordance with the ionic radii and electronegative trends, and the covalency fractions of R-O bonds varied slightly due to the lanthanide contraction. While in the monazite phase, both R-O and X-O bonds were divided into two groups by their covalency fractions.

Synthesis of Soluble Poly(arylene ether sulfone) Ionomers with Pendant Quaternary Ammonium Groups for Anion Exchange Membranes

A new bisphenol monomer, 2,2'-dimethylaminemetllylene-4,4'-biphenol (DABP), was easily prepared by Mannich reaction of dimethylamine and formaldehyde with 4,4'-biphenol. Novel partially fluorinated poly(arylene ether sulfone)s with pendant quaternary ammonium groups were prepared by copolymerization of DABP, 4,4'-biphenol, and 3,3',4,4'- tetrafluorodiphenylsulfone, followed by reaction with iodomethane. The resulting copolymers PSQNI-x (where x represents the molar fraction of DABP in the feed) with high molecular weight exhibited outstanding solubility in polar aprotic solvents; thus, the flexible and tough membranes of PSQNI-x with varying ionic content could be prepared by casting from the DMAc solution. Novel anion exchange membranes, PSQNOH-x, were obtained by an anion exchange of PSQNI-x with 1 N NaOH.

Novel sulfonated poly(arylene ether ketone) copolymers bearing carboxylic or benzimidazole pendant groups for proton exchange membranes

A novel strategy in which the benzimidazole group and sulfonic group are simultaneously attached to an aromatic polymer has been reported in this paper. For this purpose, sulfonated poly(arylene ether ketone) copolymers containing carboxylic acid groups (SPAEK-x-COOH, x refers to the molar percentage Of sulfonated repeating units) are prepared by the aromatic nucleophilic polycondensation of sodium 5,5'-carbonyl-bis(2-fluobenzene-sulfonate) (SDFBP), 4,4'-difluorobenzophenone (DFBP) and phenolphthalin (PPL). Then the carboxylic acid groups attached to the SPAEK-x-COOH are transformed to benzimidazole units through condensation reactions (referred to as SPAEK-x-BI). Fourier transform infrared spectroscopy and H-1 NMR measurements are used to characterize and confirm the structures of these copolymers.

Synthesis and characterization of novel sulfonated poly(arylene ether ketone) copolymers with pendant carboxylic acid groups for proton exchange membranes

A series of novel side-chain-type sulfonated poly(arylene ether ketone)s with pendant carboxylic acid groups copolymers (C-SPAEKs) were synthesized by direct copolymerization of sodium 5,5'-carbonyl-bis(2-fluorobenzenesulfonate), 4,4'-difluorobenzophenone and 4,4'-bis(4-hydroxyphenyl) valeric acid (DPA). The expected structure of the sulfonated copolymers was confirmed by FT-IR and H-1 NMR. Membranes with good thermal and mechanical stability could be obtained by solvent cast process. It should be noted that the proton conductivity of these copolymers with high sulfonation degree (DS > 0.6) was higher than 0.03 S cm(-1) and increased with increasing temperature. At 80 degrees C, the conductivity of C-SPAEK-3 (DS = 0.6) and C-SPAEK-4 (DS = 0.8) reached up to 0.12 and 0.16 S cm-1, respectively, which were higher than that of Nafion 117 (0.10 S cm(-1)).

Direct electrochemistry and electrocatalysis of glucose oxidase immobilized on glassy carbon electrode modified by Nafion and ordered mesoporous silica-SBA-15

In this paper, it was found that glucose oxidase (GOD) has been stably immobilized on glassy carbon electrode modified by ordered mesoporous silica-SBA-15 and Nafion. The sorption behavior of GOD immobilized on SBA-15 matrix was characterized by transmission electron microscopy (TEM), ultraviolet-visible (UV-vis), FTIR, respectively, which demonstrated that SBA-15 can facilitate the electron exchange between the electroactive center of GOD and electrode. The direct electrochemistry and electrocatalysis behavior of GOD on modified electrode were characterized by cyclic voltammogram (CV) which indicated that GOD immobilized on Nafion and SBA-15 matrices displays direct, nearly reversible and surface-controlled redox reaction with an enhanced electron transfer rate constant of 3.89 s(-1) in 0.1 M phosphate buffer solution (PBS) (pH 7.12).

Highly ordered mesoporous carbons-based glucose/O-2 biofuel cell

This study demonstrates a novel compartment-less glucose/O-2 biofuel cell (BFC) based on highly ordered mesoporous carbons (OMCs) with three-dimensionally (3D) interconnected and ordered pore structures. OMCs are used as supports for both stably confining the electrocatalyst (i.e., meldola's blue, MDB) for NADH oxidation and the anodic biocatalyst (i.e., NAD(+)-dependent glucose dehydrogenase, GDH) for glucose oxidation, and for facilitating direct electrochemistry of the cathodic biocatalyst (i.e., laccase, LAC) for O-2 electroreduction. In 0.10 M pH 6.0 PBS containing 20 mM NAD(+) and 60 mM glucose under the air-saturated atmosphere, the open circuit voltage (0.82 V) and the maximum power output (38.7 mu W cm(-2) (at 0.54V)) of the assembled compartment-less OMCs-based BFC are both higher than those of carbon nanotubes (CNTs)-based BFC (0.75 V and 2.1 mu W cm(-2) (at 0.46 V)).

Ordered magnetic core-manganese oxide shell nanostructures and their application in water treatment

In this paper, we have reported a facile method for the synthesis of ordered magnetic core-manganese oxide shell nanostructures. The process included two steps. First, manganese ferrite nanoparticles were obtained through a solvothermal method. Then, the manganese ferrite nanoparticles were mixed directly with KMnO4 solution without any additional modified procedures of the magnetic cores. It has been found that Mn element in the core can react with KMnO4 to form manganese oxide which acts as a seed for the in-situ growth of manganese oxide shells. This is significant for the controllable fabrication of symmetrical ordered manganese oxide shell structures. The shell thickness can be easily controlled through the reaction time. Transmission electron microscopy, scanning electron microscopy, X-ray photoelectron spectroscopy, X-ray powder diffraction and energy-dispersive X-ray spectroscopy have been employed to characterize the products at different reaction time.

Super-hydrophobicity of silica nanoparticles modified with vinyl groups

Super-hydrophobic films with vinyl-modified silica nanoparticles (V-SiOx-NPs) were successfully prepared. The rough surface, which was composed of microstructures of disordered V-SiOx-NPs and nanostructures on the surface of V-SiOx-NPs, rather than the chemical composition devoted to the super-hydrophobicity of film. The relationship between contact angle and diameter of V-SiOx-NPs was then investigated. The sessile contact angles (CA) of films with 150-1600nm V-SiOx-NPs were around 166 regardless the diameter, while the film with 85 nm V-SiOx-NPs had the lowest CA of about 158. The packing manner of V-SiOx-NPs determined the air fraction on the surface and then the CA.

Effects of polymerization conditions on hydrophilic groups in aromatic polyamide thin films

For polyamide used in reverse osmosis (RO) membranes, the content of pendant acid groups is critical to its performance. In this work, FTIR was used to analyze the acid contents in the polyamide films prepared via interfacial polymerization of trimesic acid trichloride (TMC) in hexane and 1,3-phenylenediamine (MPDA) in water, and the effects of reaction conditions, including monomer concentrations, time, and temperature, were studied. It was found that more pendant acid groups are present in the polyramide film at higher TMC concentrations or lower MPDA concentrations, and longer reaction times and lower temperatures also favor the formation of the free acids. These results can be explained by the monomer diffusion in the interfacial polymerization process. This work may help the design and fabrication of RO membranes with different hydrophilicity and target performance.

Direct synthesis of ordered N-methylimidazolium functionalized mesoporous silica as highly efficient anion exchanger of Cr(VI)

Ordered N-methylimidazolium functionalized mesoporous silica (SBA-15) anion exchangers were directly synthesized by co-condensation of tetraethoxysilane with 1-methyl-3(triethoxysilylpropyl)imidazolium chloride. The prepared samples with rod-like morphology showed high surface areas (> 400 m(2) g(-1)), well-ordered pores (> 58 angstrom), and excellent thermal stability up to 387 degrees C. The adsorption behaviors of Cr(VI) from aqueous solution on the anion exchangers were studied using the batch method. The anion exchangers had high adsorption capacity ranging from 50.8 to 90.5 mg g(-1), over a wider pH range (1-8) than amino functionalized mesoporous silica. The adsorption rate was fast, and the maximum adsorption was obtained at pH 4.6. The adsorption data for the anion exchangers were consistent with the Langmuir isotherm equation. Most active sites of the anion exchangers were easily accessible. The mixed solution of 0.1 mol L-1 NH3 center dot H2O and 0.5 mol L-1 NH4Cl was effective desorption solution, and 95% of Cr(VI) could be desorbed.

Hydrothermal Synthesis and Luminescent Properties of Novel Ordered Sphere CePO4 Hierarchical Architectures

The ordered-sphere CePO4 hierarchical architectures have been successfully synthesized by a simple hydrothermal method through the controlled growth of the CePO4 nanorods and self-assemble hierarchical structure under various reaction conditions. The evolution of the morphology of the samples has been investigated in detail. It was found that the coexistence of citric acid and cetaltrimethylammonium bromide in the reaction system plays an important role in the formation of the spherical CePO4 hierarchical architectures. A possible mechanism of the formation and growth of the hierarchical structure was suggested according to the experimental results and analysis. The effects of the reaction time as well as the variation of the morphologies on the luminescent properties of the products were also studied.