IONIC-CONDUCTION OF A NOVEL COMB POLYMER ELECTROLYTE BASED ON MALEIC-ANHYDRIDE COPOLYMER WITH OLIGO-OXYETHYLENE SIDE-CHAINS

A comb-shaped polymer (BM350) with oligo-oxyethylene side chains of the type -O(CH2CH2O)(7)CH3 was prepared from methyl vinyl ether/maleic anhydride copolymer. Homogeneous amorphous polymer electrolyte complexes were made from the comb polymer and LICF(3)SO(3) by solvent casting from acetone, and their conductivities were measured as a function of temperature and salt concentration. Maximum conductivity close to 5.08 X 10(-5) Scm(-1) was obtained at room temperature and at a [Li]/[EO] ratio of about 0.12. The conductivity which displayed non-Arrhenius behaviour was analyzed using the Vogel-Tammann-Fulcher equation and interpreted on the basis of the configurational entropy model. The results of mid-IR showed that the coordination of Li+ to side chains made the C-O-C band become broader and shift slightly. X-ray photoelectron spectroscopy analysis indicated that the oxygen atoms in the two situations could coordinate to Li+ and this coordination resulted in the reduction of the electron orbit binding energy of F and S.

CURE AND IONIC-CONDUCTIVITY OF A 2-COMPONENT EPOXY NETWORK POLYMER ELECTROLYTE

In order to raise the room temperature ionic conductivity and improve the mechanical strength of a PEO-based polymer electrolyte, a non-crystalline two-component epoxy network was synthesized by curing diglycidyl ether of polyethylene glycol (DGEPEG) with triglycidyl ether of glycerol (TGEG) in the presence of LiClO4 salt, which acts in this system as both a ring opening catalyst and a source of ionic carrier. The structure of the precursors, the curing process and the cured films have been characterized by C-13 NMR, IR, DSC and ionic conductivity measurement techniques. The electrolyte system exhibits an ionic conductivity as high as similar to 10(-5) S/cm at 25 degrees C and is mechanically self-supportable. The dependence of ionic conductivity was investigated as a function of temperature, salt content, MW of PEG segment in DGEPEG and the proportion of DGEPEG in DGEPEG/TGEG ratio.

ORDERED ARRAYS OF MYOGLOBIN ADSORBED ON THE SURFACTANT MODIFIED SURFACE BY SCANNING-TUNNELING-MICROSCOPY

Myoglobin molecules were deposited on a surfactant sodium dodecyl sulfate modified HOPG surface and imaged in air with a high resolution scanning tunneling microscope (STM) for the first time. STM images exhibit not only ordered arrays of the surfactant m

INFLUENCE OF IONIC SUBSTITUTION ON THE MAGNETIC-BEHAVIOR OF Y2CU2O5

The influence of the substitution of Cu or O by various elements on the magnetic properties of Y2Cu2O5 has been studied. The substitution of Cu by metal ions with unpaired d electrons (M = Co2+, Ni2+) makes the superexchange in Cu2O8 chains stronger, but

IONIC-CONDUCTIVITY AND DYNAMIC MECHANICAL RELAXATION OF A 2-COMPONENT EPOXY NETWORK-LICLO4 ELECTROLYTE SYSTEM

The correlation between mechanical relaxation and ionic conductivity was investigated in a two-component epoxy network-LiClO4 electrolyte system. The network was composed of diglycidyl ether of polyethylene glycol (DGEPEG) and triglycidyl ether of glycerol (TGEG). The effects of salt concentration, molecular weight of PEG in DGEPEG and the proportion of DGEPEG (1000) in DGEPEG/TGEG ratio on the ionic conductivity and the mechanical relaxation of the system were studied. It was found that, among the three influential factors, the former reinforces the network chains, reduces the free volume fraction and thus increases the relaxation time of the segmental motion, which in turn lowers the ionic conductivity of the specimen. Conversely, the latter two increase the free volume and thus the chain flexibility, showing an opposite effect. From the iso-free-volume plot of the shift factor log at and reduced ionic conductivity, it is noted that the plot can be used to examine the temperature dependence of segmental mobility and seems to be useful to judge whether the incorporated salt has been dissociated completely. Besides, the ionic conductivity and relaxation time at constant reference temperature are linearly correlated with each other in all the three cases. This result gives an additional experimental confirmation of the coordinated motion model of the ionic hopping with the moving polymer chain segment, which is generally used to explain the ionic conduction in non-glassy amorphous polymer electrolytes.

Capillary electrochromatography using a strong cation-exchange column with a dynamically modified cationic surfactant

A novel mode of capillary electrochromatography (CEC), called dynamically modified strong cation-exchange CEC (DMSCX-CEC), is described in this paper. A column packed with a strong cation-exchange (SCX) packing material was dynamically modified with a long-chain quaternary ammonium salt, cetyltrimethylammonium bromide (CTAB), which was added to the mobile phase. CTAB ions were adsorbed onto the surface of the SCX packing material, and the resulting hydrophobic layer on this packing was used as the stationary phase. Using the dynamically modified SCX column, neutral solutes were separated with the CEC mode. The highest number of theoretical plates obtained was about 190 000/m, and the relative standard deviations (RSD's) for migration times and capacity factors of alkylbenzenes were less than 1.0% and 2.0% for five consecutive runs, respectively. The effects of CTAB and methanol concentrations and the pH value of the mobile phase on the electroosmotic flow and the separation mechanism were investigated. Excellent simultaneous separation of the basic and neutral solutes in DMSCX-CEC with a high-pH mobile phase was obtained, A mixture containing the acidic, basic, and neutral compounds was well separated in this mode with a low-pH mobile phase; however, peak tailing for basic compounds was observed in this mobile phase.

Capillary electrochromatography with a silica column with a dynamically modified cationic surfactant

A novel mode of capillary electrochromatography (CEC), called dynamically modified silica-capillary electrochromatography, is described in this paper. The column packed with bare silica was dynamically modified with long chain quaternary ammonium salt, cetyltrimethylammonium bromide (CTAB), which was added into the mobile phase. CTAB ions were adsorbed onto the surface of bare silica, and the resulted hydrophobic layer on the silica gel was used as the stationary phase; Using the dynamically modified silica column, neutral solutes were separated by CEC. The highest number of theoretical plates obtained was about 71 500/m and the relative standard deviations for t(0) and capacity factor of toluene were 4.7% and 4.9% for 20 consecutive runs, respectively. The separation mechanism of neutral solutes and the influence of mobile phase composition on the separation was investigated. The separation of nitrogen-containing solutes was carried out with this mode and the peak tailing of basic solute was effectively eliminated because the adsorption of basic solute on silica was blocked by the preferred adsorption of CTAB. (C) 1999 Elsevier Science B.V. All rights reserved.

Electrochemical performance of mixed ionic-electronic conducting oxides as anodes for solid oxide fuel cell

Mixed ionic-electronic conducting (MIEC) oxides, SrFeCo0.5Ox, SrCo0.8Fe0.2O3-delta and La0.6Sr0.4Fe0.8Co0.2O3-delta have been synthesized and prepared on yttria-stabilized zirconia as anodes for solid oxide fuel cells. Power output measurements show that the anodes composed of such kinds of oxides exhibit modest electrochemical activities to both H-2 and CH4 fuels, giving maximum power densities of around 0.1 W/cm(2) at 950 degrees C. Polarization and AC impedance measurements found that large activation overpotentials and ohmic resistance drops were the main causes for the relative inferior performance to the Ni-YSZ anode. While interlayered with an Ni-YSZ anode, a significant improvement in the electrochemical performance was observed. in particular, for the SrFeCo0.5Ox oxide interlayered Ni-YSZ anode, the maximum power output reaches 0.25 W/cm2 on CH,, exceeding those of both SrFeCo0.5Ox and the Ni-YSZ, as anodes alone. A synergetic effect of SrFeCo0.5Ox and the Ni-YSZ has been observed. Future work is needed to examine the long-term stability of MIEC oxide electrodes under a very reducing environment. (C) 1999 Elsevier Science B.V. All rights reserved.

In situ high temperature X-ray diffraction studies of mixed ionic and electronic conducting perovskite-type membranes

Phase structure and stability of three typical mixed ionic and electronic conducting perovskite-type membranes, SrCo0.8Fe0.2O3-delta (SCF), Ba0.5Sr0.5Co0.8Fe0.2O3-delta (BSCF) and BaCo0.4Fe0.4Zr0.2O3-delta (BCFZ) were studied by in situ high temperature X-ray diffraction at temperatures from 303 to 1273 K and under different atmospheres (air, 2% O-2 in Ar and pure Ar) at 1173 K. By analyzing their lattice parameters the thermal expansion coefficients (TECs) of BSCF, SCF and BCZF are obtained to be 11.5 x 10(-6) K-1, 17.9 x 10(-6) K-1 and 10.3 x 10(-6) K-1, respectively. A relationship between phase stability and TEC was proposed: the higher is the TEC, the lower is the operation stability of the perovskite materials. (C) 2005 Elsevier B.V. All rights reserved.

Hydrothermal synthesis of alumina nanotubes templated by anionic surfactant

The alumina nanotubes were prepared by using the anionic surfactant, sodium dodecyl sulfonate (SDS), as structure-directing template for the first time with Al(NO3)(3)center dot 9H(2)O as precursor via a hydrothermal method. Structure and morphology of the nanotubes were characterized by XRD, TEM, FT-IR, TG and N-2 adsorption-desorption. The obtained nanotubes were found having outer diameters from 6 to 8 nm with length up to 200 nm. (C) 2005 Elsevier B.V. All rights reserved.