Formation of the V center on H-type zeolites with thermal treatment

The effect of thermal treatment on H-MCM-22 and H-ZSM-5 zeolites was investigated using the electron spin resonance technique. A six-line signal (denoted as A, g = 2.048, A = 22. 15 G) was detected on H-MCM-22 after He purging at high temperatures, whose intensities increased with the treating temperature. The same signal was also found on H-ZSM-5 zeolites with different crystal sizes. The paramagnetic center was identified as a V center, namely, a hole of an electron trapped on an oxygen atom bonding to a nearby aluminum atom. These signals appeared only on a dealuminated sample or a sample concomitantly with dealumination. The formation of the hole might involve an electron transferring from the lattice oxygen to a nonframework aluminum species, and the hyperfine splitting is caused by the interaction between the electron hole locating on the p orbit of oxygen and the framework aluminum bonding with the oxygen. The signal disappeared after the sample was exposed to air or oxygen at room temperature. However, the process was reversible. A new set of signals (denoted as B, g(1) = 2.008, g(2) = 2.003, g(3) = 1.9985) was observed after oxygen adsorption on the H-MCM-22 pretreated with He at 973 K or He purging at 973 K on the H-MCM-22 pretreated with oxygen at 813 K, which was attributed to the O- species.

Fast formation of NaA zeolite membrane in the microwave field

NaA zeolite membrane was successfully synthesized on the porous alpha-Al2O3 support by microwave heating. The synthesis of NaA zeolite membrane in the microwave field only needs 15 min and the synthesis time is 10 times shorter than that by conventional heating. SEM characterization indicates that the zeolite crystals in the NaA zeolite membrane synthesized by microwave heating are uniform in size; the membrane thickness is about 4 mu m and is thinner than that of the NaA zeolite membrane synthesized by conventional heating. Gas permeation studies indicate that the permeances of the NaA zeolite membrane synthesized by microwave heating are 3-4 times higher than those of the NaA zeolite membrane synthesized by conventional heating, while their permselectivities are comparable.

Different mechanisms for the formation of acetaldehyde and ethanol on the Rh-based catalysts

Different mechanisms for the formation of acetaldehyde and ethanol on the Rh-based catalysts were investigated by the TPR (temperature programmed reaction) method, and the active sites were studied by CO-TPD, TPSR (temperature programmed surface reaction of preadsorbed CO by H-2) and XPS techniques. The TPR results indicated that ethanol and acetaldehyde might be formed through different intermediates, whereas ethanol and methanol might result from the same intermediate. Results of CO-TPD, TPSR, and XPS showed that on the Rh-based catalyst, the structure of the active sites for the formation of C-2-oxygenates is ((RhxRhy+)-Rh-0)-O-Mn+ (M=Mn or Zr, x>>y, 2 less than or equal ton less than or equal to4). The tilt-adsorbed CO species is the main precursor for CO dissociation and the precursor for the formation of ethanol and methanol. Most of the linear and geminal adsorbed CO species desorbed below 500 K. Based on the suggested model of the active sites, detailed mechanisms for the formation of acetaldehyde and ethanol are proposed. Ethanol is formed by direct hydrogenation of the tilt-adsorbed CO molecules, followed by CH2 insertion into the surface CH2-O species and the succeeding hydrogenation step. Acetaldehyde is formed through CO insertion into the surface CH3-Rh species followed by hydrogenation, and the role of the promoters was to stabilize the intermediate of the surface acetyl species. (C) 2000 Academic Press.