Effect of cryoprotectants on hatching rate of red seabream (Pagrus major) embryos

The objectives were to investigate the effect of cryoprotectants on the hatching rate of red seabream embryos. Heart-beat embryos were immersed in: five permeable cryoprotectants, dimethyl sulfoxide (DMSO), glycerol (Gly), methanol (MeOH), 1,2-propylene glycol (PG), and ethylene glycol (EG). in concentrations of 5-30% for 10, 30, or 60 min; and two non-permeable cryoprotectants: polyvinylpyrrolidone (PVP), and sucrose (in concentrations of 5-20% for 10 or 30 min). The embryos were then washed and incubated in filtered seawater until hatching occurred. The hatching rate of the embryos treated with permeable cryoprotectants decreased (P < 0.05) with increased concentration and duration of exposure. In addition, PG was the least toxic permeable cryoprotectant, followed by DMSO and EG, whereas Gly and MeOH were the most toxic. At a concentration of 15% and 30 min exposure, the hatching rate of the embryos immersed in PG was 93.3 +/- 7.0% (mean +/- S.D.), however. in DMSO. EG, Gly. and MeOH, it was 82.7 +/- 10.4, 22.0 +/- 5.7, 0.0 +/- 0.0, and 0.0 +/- 0.0%, respectively. Hatching rate of embryos treated with PVP decreased (P < 0.05) with the increase of concentration and exposure time, whereas for embryos treated with sucrose, there was no significant decrease in comparison with the control at the concentrations used. (C) 2008 Elsevier Inc. All rights reserved.

Effect of H2S on stress corrosion cracking and hydrogen permeation behaviour of X56 grade steel in atmospheric environment

Susceptibility to stress corrosion cracking of X56 steel and its relationship with hydrogen permeation behaviour in atmospheric environment containing H2S was investigated by hydrogen permeation tests at a slow strain rate. The results show that: the fracture strain decreases with the decrease of strain rate under the same experimental conditions; the fracture strain also decreases with the increase of H2S concentration under the same strain rate, and the increased concentration of H2S has no significant effect on the hydrogen permeation in the first wet, etc. dry cycle, however has lead to increased hydrogen permeation in the later cycles. The SEM images of the fractured surfaces show clear evidences of enhanced stress corrosion cracking susceptibility by H2S.

Effect of Cl- on the corrosive wear of AISI 321 stainless steel in H2SO4 solution

The effect of Cl- on the corrosive wear behaviour of AISI 321 stainless steel in H2SO4 solution was studied via the corrosive wear rate, the load bearing capacity of passive film and the relationship between pitting and corrosive wear. There is a critical load at natural potential, below which the corrosive wear rate is slightly lowered by Cl-, while above which is increased. At natural potential there are more pits at low load than that at a higher one in the wear tracks and the pits are also deeper. The load bearing capacity is lowered by Cl- at passive region and then the corrosive wear rate increased.

The effect of additives on Cu/HZSM-5 catalyst for DME synthesis

The addition of ZnO or ZrO2 into CuO/HZSM-5 was investigated for DME synthesis from syngas by using the reactive frontal chromatography method, TPR and in situ TPR. These promoters enhanced the catalytic activity of Cu/HZSM-5 and promotion with ZnO and ZrO2 produced a maximum activity, which could be explained by the improvement of the dispersion of Cu and the promotion of CuO reduction. The Cu+ species existing during the reaction have been detected, based on which a Cu-0 <-> Cu+1 redox cycle model was put forward.

The effect of oxygen on the aromatization of methane over the Mo/HZSM-5 catalyst

The aromatization of methane over a Mo/HZSM-5 catalyst was carried out in the presence of oxygen. It is shown that the addition of a small amount of oxygen is beneficial to improve the durability of the catalyst. UV-Raman spectra disclose that the carbonaceous deposits formed on the HZSM-5 are mainly polyolefinic and aromatic, while that on the Mo/HZSM-5 is mainly polyaromatic. The small amount of O-2 added may partly remove the coke deposits on the active sites and keep the catalyst as MoOxCy/HZSM-5, thus resulting in an improvement of the catalytic performance of the Mo/HZSM-5 catalyst.

The effect of chromium on sulfur resistance of Pd/HY-Al2O3 catalysts for aromatic hydrogenation

Sulfur is a major poison to noble metal catalysts for deep aromatic hydrogenation in the petroleum refining industry. In order to study the sulfur resistance of Pd-based catalysts, a series of Pd, Cr, and PdCr catalysts supported on HY-Al2O3 were studied by NH3-TPD, pyridine-adsorption IR, TPR, IR spectra of adsorbed CO, and toluene hydrogenation in the presence of 3000 ppm sulfur as thiophene under the following conditions: 533-573 K, 4.2 MPa, and WHSV 4.0 h(-1). Cr has no influence on the acidity of the catalysts. TPR patterns and in situ IR spectra of adsorbed CO revealed a strong interaction between Cr and Pd, and the frequency shift of linear bonded CO on Pd indicates that the electron density of Pd decreases with the increase of the Cr/Pd atomic ratio. The catalytic performance of Pd, Cr, and PdCr catalysts shows that the sulfur resistance of Pd is strongly enhanced by Cr, and the activity reaches its maximum when the Cr/Pd atomic ratio equals 8. The active phase model "Pd particles decorated by Cr2O3" is postulated to explain the behavior of PdCr catalysts. (C) 2001 Academic Press.