Infrared (1.2-1.6 mu m) luminescence in Yb, Cr : YAG with 940 nm diode pumping

Infrared (1.2-1.6 mum) luminescence in a yttrium aluminium garnet (YAG) crystal, co-doped with Yb (10 at.%) and Cr (0.05 at.%) ions, was investigated under CW laser diode pumping (lambda = 940 nm). The Cr4+ emission band was observed with its peak at 1.35 mum and measured to be about 6% with respect to Yb3+ IR luminescence (lambda = 1.03 mum). Analysis of the crystal absorption and luminescence spectra allows one to conclude that Yb3+-Cr4+ energy transfer is a mechanism responsible for the B-3(2)(T-3(2))-B-3(1)((3)A(2)) emission of Cr4+ ions. This crystal is promising as an efficient source of the near infrared emission. (C) 2004 Elsevier B.V. All rights reserved.

Infrared (1.2-1.6 mu m) luminescence in Cr4+: Yb3Al5O12 single crystal with 940 nm diode pumping

Infrared (1.2-1.6 mu m) luminescence in a ytterbium aluminium garnet (YbAG) crystal, doped with Cr (0.05 at.%) ions, was investigated under CW laser diode pumping (lambda = 940 nm). The Cr4+ emission band was observed with its peak at 1.34 mu m and measured to be about 1.3 times with respect to Yb3+ IR luminescence (lambda = 1.03 mu m). We demonstrate that for the excitation wavelength of 940 nm Yb3+ ions act as sensitizers of the B-3(2)(T-3(2))-B-3(1)((3)A(2)) emission of Cr4+ ions. This crystal is promising as a high-efficient system for tunable laser (1.2-1.6 mu m) output. (c) 2004 Elsevier B.V. All rights reserved.

Upconversion luminescence from E-2 state of Cr3+ in Al2O3 crystal by infrared femtosecond laser irradiation

Visible upconversion luminescence was observed in Cr3+: Al2O3 crystal under focused femtosecond laser irradiation. The luminescence spectra show that the upconversion luminescence originates from the E-2-(4)A(2) transition of Cr3+. The dependence of the fluorescence intensity of Cr3+ on the pump power reveals that a two-photon absorption process dominates in the conversion of infrared radiation to the visible emission. It is suggested that the simultaneous absorption of two infrared photons produces the population of upper excited states, which leads to the characteristic visible emission from E-2 state of Cr3+.

Direct writing computer-generated holograms on metal film by an infrared femtosecond laser

Writing computer-generated holograms has been achieved by using near infrared femtosecond laser selective ablation of metal film deposited on glass substrate. The diffraction features with data reconstruction of fabricated computer-generated holograms were evaluated. Both transmission and reflection holograms can be fabricated in a single process. The process required no mask, no pre- or post-treatment of the substrate. (C) 2005 Optical Society of America.

GeO2 : Bi, M (M = Ga, B) glasses with super-wide infrared luminescence

Broadband infrared luminescence covering the optical telecommunication wavelength region of 0, E and S bands was observed in GeO2: Bi, M (M = Ga, B) glasses prepared by conventional melting-quenching technique. The luminescence with a maximum at around 1320 nm possesses a full width at half maximum larger than 300 nm and mean fluorescent lifetime longer than 500 mus when excited by an 808 nm-laser. These glasses may have potential applications in widely tunable laser and super-broadband optical amplifier for the optical communications. (C) 2005 Elsevier B.V. All rights reserved.

Superbroadband 1310 nm emission from bismuth and tantalum codoped germanium oxide glasses

Near-infrared broadband emission from bismuth-tantalum-codoped germanium oxide glasses was observed at room temperature when the glasses were pumped by an 808 nm laser diode. The emission band covered the 0, E, S, C, and L bands (1260-1625 nm), with a maximum peak at similar to 1310 nm, a FWHM broader than 400 nm, and a lifetime longer than 200 lis. The observed broadband luminescence was attributed to bismuth clusters in the glasses. Bismuth-tantalum-codoped germanium oxide glass might be promising as amplification media for broadly tunable lasers and wideband amplifiers in optical communications. (c) 2005 Optical Society of America.

Blue upconversion luminescence generation in Ce3+: Gd2SiO5 crystals by infrared femtosecond laser irradiation

Blue frequency-upconversion fluorescence emission has been observed in Ce3+-doped Gd2SiO5 single crystals, pumped with 120-fs 800 nm IR laser pulses. The observed fluorescence emission peaks at about 440nm is due to 5d -> 4f transition of Ce3+ ions. The intensity dependence of the blue fluorescence emission on the IR excitation laser power obeys the cubic law, demonstrating three-photon absorption process. Analysis suggested that three-photon simultaneous absorption induced population inversion should be the predominant frequency upconversion mechanism. (c) 2006 Optical Society of America.

Broadband near-infrared emission from transparent Ni2+-doped sodium aluminosilicate glass ceramics

Broadband neat-infrared emission from transparent Ni2+-doped sodium aluminosilicate glass-cermaics is observed. The broad emission is centered at 1290 nm and covers the whole telecommunication wavelength region (1100-1700 nm) with full width at half maximum of about 340 nm. The observed infrared emission could be attributed to the T-3(2)(F) -> (3)A(2)(F) transition of octahedral Ni2+ ions that occupy high-field sites in nanocrystals. The product of the lifetime and the stimulated emission cross section is 2.15 x 10(-24) cm(2)s. It is suggested that Ni2+-doped sodium aluminosilicate glass ceramics have potential applications in tunable broadband light sources and broadband amplifiers.