Preparation and characterization of luminescent thin films doped with rare earth (Tb3+, Eu3+) complexes derived from a sol-gel process

Sol-gel derived luminescent thin films doped with rare earth (RE) complexes were prepared using an in-situ synthesis method with a two-step hydrolysis process and the luminescence spectra were measured. Fluorescence Lifetime and thermal stability were investigated. The results show that a broad excitation band indicates the formation of RE complexes in the solid thin films. RE ions, which are restrained in a silica matrix, present longer lifetime and higher thermal stability than that in DMF/PVB films containing the corresponding pure complexes. (C) 2000 Elsevier Science B.V. All rights reserved.

Sol-gel deposition of calcium silicate red-emitting luminescent films doped with Eu3+

Eu3+-activated calcium silicate (CaO-SiO2:Eu3+) luminescent films were prepared by the sol-gel method. The structural evolution of the film was studied by X-ray powder diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM), and the luminescence properties of the phosphor films were investigated as a function of heat treatment temperature. The XRD study indicates that a kilchoanite phase forms in the film sintered at 800 degreesC, which is different from that in gel powder treated under the same conditions. The SEM results show that the film thickness decreases and the particles in the film become smaller with increasing heat treatment temperature. The CaO-SiO2:Eu film shows the characteristic emission of Eu3+ under UV excitation, with the Eu3+ D-5(0)-->F-7(2) band (616 nm) being the most prominent. A large difference in the Eu3+ lifetime is observed between the film samples treated at 500 and 700 degreesC (or above). Concentration quenching occurs when the Eu3+ doping concentration is above 6 mol% of Ca2+ in the film.

Processible nanostructured materials with electrical conductivity and magnetic susceptibility: Preparation and properties of maghemite polyaniline nanocomposite films

We here present a versatile process for the preparation of maghemite/polyaniline (gamma-Fe2O3/ PAn) nanocomposite films with macroscopic processibility, electrical conductivity, and magnetic susceptibility. The gamma-Fe2O3 nanoparticles are coated and the PAn chains are doped by anionic surfactants of omega-methoxypoly(ethylene glycol) phosphate (PEOPA), 4-dodecylbenzenesulfonic acid (DBSA), and 10-camphorsulfonic acid (CSA). Both the coated gamma-Fe2O3 and the doped PAn are soluble in common organic solvents, and casting of the homogeneous solutions gives free-standing nanocomposite films with gamma-Fe2O3 contents up to similar to 50 wt %. The morphology of the gamma-Fe2O3 nanoparticles are characterized by transmission electron microscopy, UV-vis spectroscopy, and X-ray diffractometry. The gamma-Fe2O3/PAn films prepared from chloroform/m-cresol solutions of DBSA-coated gamma-Fe2O3 and CSA-doped PAn are conductive (sigma = 82-237 S/cm) and superpapamagnetic, exhibiting no hysteresis at room temperature. The zero-field-cooled magnetization experiment reveals that the nanocomposite containing 20.8 wt % gamma-Fe2O3 has a blocking temperature (T-b) in the temperature region of 63-83 K.

Luminescent properties of divalent samarium-doped strontium hexaborate

The valence change of samarium from trivalent to divalent in strontium hexaborate (SrB6O10) prepared in air is observed. The temperature dependence of the luminescence and vibronic transitions of Sm2+ are studied. The Sm2+ ions occupy three crystallographic sites. With increasing temperature, the D-5(0)-->F-7(0) transition line exhibits red shifts, and the half-width increases. At room temperature, due to the thermal population through the 4f(5)5d channel, the D-5(1)-->F-7(J) transitions are observed even though the vibrational energy is very close to the energy gap between the D-5(1) and D-5(0) levels in the host. A coupled phonon energy of about 108 cm(-1) is determined from the vibronic transitions of Sm2+ in the host.

Perovskite-type B-site Bi-doped ceramic membranes for oxygen separation

Novel mixed conducting oxides, B-site Bi-doped perovskites were exploited and synthesized. Cubic perovskite structures were formed for BaBi0.2COyFe0.8-yO3-delta (y less than or equal to 0.4) and BaBixCo0.2Fe0.8-xP3-delta (x=0.1-0.5) The materials exhibited considerable high oxygen permeability at high temperature. The oxygen permeation flux of BaBi0.2Co0.35Fe0.45O3-delta membrane reached about 0.77 x 10(-6) mol/cm(2) s under an air/helium oxygen partial pressure gradient at 900 degrees C, which was much higher than that of other bismuth-contained mixed conducting membranes. The permeation fluxes of the materials increased with the increase of cobalt content, but no apparent simple relationship was found with the bismuth content. The materials also demonstrated excellent reversibility of oxygen adsorption and desorption. Stable time-related oxygen permeation fluxes were found for BaBi0.2CO0.35Fe0.45O3-delta and BaBi0.3Co0.2Fe0.5O3-delta a membranes at 875 degrees C.

Post-grafting preparation of large-pore mesoporous materials with localized high content titanium doping

A new post-grafting process, consisting of two steps of substrate preparation and sol - gel post-grafting, has been developed to prepare titanium-doped mesoporous SBA-15 material with a double-layered structure and locally concentrated titanium content at the inner pore surface. With this novel technique, the single phased and originally ordered mesostructures can be well conserved; in the conventional direct synthesis they can be partially damaged when the frameworks are doped with high content heteroatoms. Titanium species exist in an isolated, tetrahedral structure and are localized at the pore surface; this is beneficial to both reactant access and product release. Characterization with XRD, N-2 adsorption/desorption isotherms, HREM/ EDS, ICP, UV - Vis, and the newly developed UV - Raman spectroscopy confirm these results. Preliminary catalytic tests with the selective epoxidation of cyclohexene show good catalytic activity. Among them, sample TiSBA-15-10 with a Si : Ti molar ratio of 10 shows a TON value of 75 and a highest product ( epoxide) yield of 55%.

Structure and impedance of ZrO2 doped with SC2O3 and CeO2

Scandia and ceria doped zirconia samples, with 10 mol% SC2O3 and different content of CeO2, were synthesized and characterized. The XRD results depict that the sintered samples have a cubic phase structure. However, Raman spectra show that besides the main cubic phase, a secondary phase is also present in the sintered samples. The addition of CeO2 can raise the content of the cubic phase, but the minor metastable tetragonal phase (t'-phase) exists even at the CeO2 content as high as 10 mol%. The near-UV Raman spectra indicate that the deformed tetragonal structure predominates at the grain boundary. The addition of CeO2 can reduce the impurity at grain boundary, and no impurity can be found by near-UV Raman spectroscopy at the grain boundary of the samples with high CeO2 content. The impedance measurements show that with the increase of CeO2 content, the impedance of grain boundary decreases and the bulk impedance increases. The low impedance of grain boundary can be attributed to the formation of a clean grain boundary upon CeO2 doping, and the increase of the bulk impedance is due to the blocking effect of the large Ce(IV) ions. (c) 2005 Elsevier B.V All rights reserved.