超宽带光纤放大器用的新型掺铋发光材料

最近，一种新型的掺铋发光材料引起了人们的关注。这种发光材料有长的荧光寿命（τ＞200μs），在800nm激光激发下发射波长在1200～1600nm区间的超宽带荧光（荧光半高宽FWHM＞200nm），其发光性质与以往文献中报道的Bi^3＋或Bi^2＋掺杂的发光材料的性质截然不同；光发射截面（σem）是光掺铒光纤放大器玻璃（EDFAG）的2～3倍，其σem×FWHM值是EDFAG的10倍左右，σem×τ值是掺Ti^3＋蓝宝石的3倍左右。

Low-threshold and continuously tunable Yb : Gd2SiO5 laser

Yb:Gd2SiO5 (Yb:GSO) exhibits a large fundamental manifold splitting. Its long-wavelength emission band around 1088 nm, which has the largest emission cross section, encounters the lowest reabsorption losses caused by thermal population of the terminal laser level. As a result, low-threshold and tunable continuous-wave Yb:GSO lasers were demonstrated. A slope efficiency up to 86% and a pumping threshold as low as 127 mW were achieved for a continuous-wave Yb:GSO laser at 1092.5 nm under the pump of a high-brightness laser diode. A continuous tunability between 1000 and 1120 nm was realized with an SF14 prism as the intracavity tuning element. (c) 2006 American Institute of Physics.

Spectroscopic properties of Nd3+-doped high silica glass prepared by sintering porous glass

A new kind of Nd3+, -doped high silica glass (SiO2 > 96% (mass fraction)) was obtained by sintering porous glass impregnated with Nd3+, ions. The absorption and luminescence properties of high silica glass doped with different Nd3+, concentrations were studied. The intensity parameters Omega(t) (t = 2, 4, 6), spontaneous emission probability, fluorescence lifetime, radiative quantum efficiency, fluorescence branching ratio, and stimulated emission cross section were calculated using the Judd-Ofelt theory. The optimal Nd3+ concentration in high silica glass was 0.27% (mole fraction) because of its high quantum efficiency and emission intensity. By comparing the spectroscopic parameters with other Nd3+ doped oxide glasses and commercial silicate glasses, the Nd3+-doped high silica glasses are likely to be a promising material used for high power and high repetition rate lasers.

高浓度掺Er^3＋铌酸锂晶体的光谱参数计算

用提拉法成功地生长了6mol％的高浓度掺铒铌酸锂晶体。测量了晶体的两个非偏振方向（X和Z）以及两个偏振方向（π和δ）的吸收光谱。高浓度掺铒铌酸锂晶体的吸收系数高，有利于提高泵浦效率。根据所测的吸收光谱用Judd-Ofelt理论拟合出了Er^3＋离子的强度参数Ωλ。所得的均方差结果显示偏振拟合的误差要小于非偏振拟合。利用偏振吸收数据计算了各能级跃迁的自发辐射跃迁几率（AJJ’）、辐射寿命（τ）、荧光分支比（β）和积分发射截面（σp）等参数，对计算结果进行了讨论并与其他文献的报道结果进行了比较。

Investigation of the spectroscopic properties of Yb3+-doped yttrium lanthanum oxide transparent ceramic

Spectroscopic properties of (Y0.9-xLa0.1Ybx)(2)O-3 transparent ceramic were studied. Two main absorption peaks of the specimen are centered at 940 and 970 nm, which are suitable for InGaAs laser diode pumping. The main emission peaks were located at 1032 and 1075 nm with larger emission cross-section and longer fluorescence lifetime than those of Yb:Y2O3. These properties of (Y0.9-xLa0.1Ybx)(2)O-3 transparent ceramic are favorable to achieve high efficiency and high power laser output. (c) 2007 Elsevier B.V. All rights reserved.

Spectral characterization of transparent (Nd0.01Y0.94La0.05)(2)O-3 laser ceramics

The spectrum properties of transparent (Nd0.01Y0.94La0.05)(2)O-3 ceramics were investigated. It was found that all absorption bands of (Nd0.01Y0.94La0.05)(2)O-3 ceramics are broadened, of which the full width at half maximum of the peak centered at 804 nm is 8 nm and its absorption cross section is 1.02x10(-20) cm(2). The emission cross section of (Nd0.01Y0.94La0.05)(2)O-3 ceramics located at 1078 nm is 5.71x10(-20) cm(2) and its fluorescent lifetime is 0.214 ms, which are similar to those of 1.0 at. %Nd:Y2O3 ceramics. These indicate that (Nd0.01Y0.94La0.05)(2)O-3 transparent ceramics has excellent spectroscopic properties.

Growth and spectral properties of Yb : FAP single crystal

In this paper, single crystal of ytterbium (Yb) doped Ca-5(PO4)(3)F (FAP) has been grown along the c-axis by using the Czochralski method. The segregation coefficients of Yb3+ in the Yb:FAP crystal has been determined by ICP-AES method. The absorption spectrum, fluorescence spectrum and fluorescence lifetime of the Yb:FAP crystal has been also measured at room temperature. In the absorption spectra, there are two absorption bands at 904 and 982 nm, respectively, which are suitable for InGaAs diode laser pumping. The absorption cross-section (sigma(abs)) is 5.117 x 10(-20) cm(2) with an FWHM of 4 nm at 982 nm. The emission cross-section is (sigma(em)) 3.678 x 10(-20) cm(2) at 1042 nm. Favorable values of the absorption cross-section at about 982 nm are promising candidates for laser diode (LD) pumping. (c) 2005 Elsevier B.V. All rights reserved.

Spectroscopic properties of Nd3+:(La,Sr)(Al,Ta)O-3 crystal

A new laser crystal Nd3+:(La, Sr)(Al, Ta)O-3 (abbreviated as Nd3+:LSAT) has been grown by the conventional Czochralski method. The absorption and luminescence spectra of trivalent neodymium in Nd3+:LSAT crystal were measured at room temperature. The value of absorption and emission cross-section was calculated. The Judd-Ofelt analysis was applied to the crystal to get the phenomenological parameters (Omega(i), i = 2,4,6), the line strengths, the radiative transition rates, the branching ratios and the radiative lifetime. (C) 2006 Elsevier B.V. All rights reserved.

Spectroscopic properties of Yb:YAP crystal

The 10at% Yb-YAP crystal has been grown by the Czochralski method. The absorption and emission spectra and fluorescence lifetime of Yb:YAP crystal at room temperature were studied. There is a strong absorption band centered at 959 nm and the absorption cross-section of 1.51 × 10^-20 cm². The emission cross-section at 1040 nm is 0.6 × 10^-20 cm² and the fluorescence lifetime is about 1.2 ms. The effects of O₂-annealing on the spectral properties were studied. The spectroscopic properties strongly depended on the axis direction and b axis was the best direction for laser output. The spectrum parameters of Yb:YAP and Yb:YAG crystal were compared.}

Er^3＋／Yb^3＋共掺的氧化镧钇透明陶瓷的光谱性能研究

采用传统无压烧结工艺制备了Er^3＋／Yb^3＋共掺的氧化镧钇透明陶瓷并对其光谱性能进行了研究．样品具有较大的吸收和发射截面．La2O3的添加使样品的荧光寿命（τs）与玻璃接近，当Yb^3＋和Er^3＋的掺杂量分别为5at％和0．5at％时，测得τs=9．65ms．这种荧光寿命长、发射截面大和线宽窄的特性有利于微型、可集成化和大功率激光输出的实现．

Fabrication and spectral properties of Nd3+-doped yttrium lanthanum oxide transparent ceramics

Transparent 1 at% Nd3+:Y1.9La0.1O3 ceramics were fabricated with nanopowders prepared by carbonate coprecipitation method. The powder compacts were sintered in H-2 atmosphere at 1550 degrees C for 30 h. The Nd3+:Y1.9La0.1O3 ceramics display uniform grains of about 50 mu m and high transparency. The highest transmittance of the ceramics reaches 67%. The strongest absorption peak is in the wavelength of 820 nm with absorption cross section of 2.48 x 10(-20) cm(2). The absorption is still high at LD wavelength 806 nm with absorption cross section of 1.78 x 10(-20) cm(2) and broad full width at half maximum (FWHM) of about 6.3 nm. The strongest emission peak was centered at 1078 nm with large stimulated emission cross section of 9.63 x 10(-20) cm(2) and broad FWHM of about 7.8 nm. The broad absorption and emission bandwidth of Nd3+:y(1.9)La(0.1)O(3) transparent ceramics are favorable to achieve the miniaturized LD pumping apparatus and ultrashort modelocked pulse laser output, respectively. (c) 2007 Elsevier B.V. All rights reserved.

Growth and spectral properties of Er:Gd2SiO5 crystal

Er3+ -doped Gd2SiO5 (Er:GSO) single crystal with dimensions of circle divide 35 x 40 mm(3) has been grown by the Czochralski method. The absorption and fluorescence spectra of the Er:GSO crystal were measured at room temperature. The spectral parameters were calculated based on Judd-Ofelt theory, and the intensity parameters Omega(2), Omega(4) and Omega 6 are obtained to be 6.168 x 10(-20), 1.878 x 10(-20), and 1.255 x 10(-20) cm(2), respectively. The emission cross-section has been calculated by Fuechtbauer-Ladenbury formula. (c) 2007 Elsevier B.V. All rights reserved.

Judd-Ofelt analysis of spectra and experimental evaluation of laser performance of Tm3+ doped Lu2SiO5 crystal

This paper reports that the TM3+:Lu2SiO5 (Tm:LSO) crystal is grown by Czochralski technique. The room-temperature absorption spectra of Tm:LSO crystal are measured on a b-cut sample with 4 at.% thulium. According to the obtained Judd-Ofelt intensity parameters Omega(2)=9.3155 x 10(-20) cm(2), Omega(4)=8.4103 x 10(-20) cm(2), Omega(6)=1.5908 x 10(-20) cm(2), the fluorescence lifetime is calculated to be 2.03 ms for F-3(4) -> H-3(6) transition, and the integrated emission cross section is 5.81 x 10(-18) cm(2). Room-temperature laser action near 2 mu m under diode pumping is experimentally evaluated in Tm:LSO. An optical-optical conversion efficiency of 9.1% and a slope efficiency of 16.2% are obtained with continuous-wave maximum output power of 0.67 W. The emission wavelengths of Tm:LSO laser are centred around 2.06 mu m with spectral bandwidth of similar to 13.6 nm.

利用窄得-奥菲特理论研究Tm:Lu_2SiO_5晶体的光谱特性

采用丘克拉斯基(Czochralski)技术生长了掺铥硅酸镥(Tm∶Lu2SiO5,Tm∶LSO)晶体;测量了LSO晶体在室温下的非偏振吸收光谱和非偏振荧光光谱;利用窄得-奥菲特(Judd-Ofelt)理论计算了Tm∶LSO晶体的窄得-奥菲特强度参数、振子强度、自发辐射概率、辐射寿命、积分吸收截面和积分发射截面.Tm∶LSO晶体的强度参数为Ω2=9.1355×10-20cm2,Ω4=8.4103×10-20cm2,Ω6=1.5908×10-20cm2;Tm∶LSO晶体在1.9μm附近有明显的发射峰(3F4→3H6跃迁),相应的辐射寿命为2.03 ms,积分发射截面为5.81×10-18cm2,半峰全宽(FWHM)为250 nm.用Tm∶LSO晶体在77 K温度下实现了激光运转.利用792 nm的激光二极管(LD)作为抽运源,获得中心波长为1960 nm的激光输出,抽运阈值为2.13 kW/cm2.

Judd-Oflet analysis of spectrum and laser performance of Ho:YAP crystal end-pumped by 1.91-mu m Tm:YLF laser

The Ho:YAP crystal is grown by the Czochralski technique. The room-temperature polarized absorption spectra of Ho:YAP crystal was measured on a c-cut sample with 1 at% holmium. According to the obtained Judd-Ofelt intensity parameters Omega(2) = 1.42 x 10(-20) cm(2), Omega(4) = 2.92 x 10(-20) cm(2), and Omega(6) = 1.71 x 10(-20) cm(2), this paper calculated the fluorescence lifetime to be 6 ms for I-5(7) -> I-5(8) transition, and the integrated emission cross section to be 2.24 x 10(-18) cm(2). It investigates the room-temperature Ho:YAP laser end-pumped by a 1.91-mu m Tm:YLF laser. The maximum output power was 4.1 W when the incident 1.91-mu m pump power was 14.4W. The slope efficiency is 40.8%, corresponding to an optical-to-optical conversion efficiency of 28.4%. The Ho:YAP output wavelength was centred at 2118 nm with full width at half maximum of about 0.8 nm.