Synthesis, photoluminescence, thermoluminescence and dosimetry properties of novel phosphor KSr4(BO3)(3):Ce

Polycrystalline powder sample of KSr4(BO3)(3) was synthesized by high-temperature solid-state reaction. The influence of different rare earth dopants, i.e. Tb3+, TM3+ and Ce3+, on thermoluminescence (TL) of KSr4(BO3)(3) Phosphor was discussed. The TL, photoluminescence (PL) and some dosimetric properties of Ce3+-activated KSr4(BO3)(3) phosphor were studied. The effect of the concentration of Ce3+ on TL intensity was investigated and the result showed that the optimum Ce3+ concentration was 0.2 mol%. The TL kinetic parameters of KSr4(BO3)(3):0.002 Ce3+ phosphor were calculated by computer glow curve deconvolution (CGCD) method. Characteristic emission peaking at about 407 and 383 nm due to the 4f(0)5d(1) -> F-2((5/2),(7/2)) transitions of Ce3+ ion were observed both in PL and three-dimensional (3D) TL spectra. The dose-response of KSr4(BO3)(3):0.002 Ce3+ to gamma-ray was linear in the range from 1 to 1000 mGy. In addition, the decay of the TL intensity of KSr4(BO3)(3):0.002 Ce3+ was also investigated.

Microstructure, tensile properties, and creep behavior of high-pressure die-cast Mg-4Al-4RE-0.4Mn (RE = La, Ce) alloys

High-pressure die-cast (HPDC) Mg-4Al-4RE-0.4Mn (RE = La, Ce) magnesium alloys were prepared and their microstructures, tensile properties, and creep behavior have been investigated in detail. The results show that two binary Al-Ce phases, Al11Ce3 and Al2Ce, are formed mainly along grain boundaries in Mg-4Al-4Ce-0.4Mn alloy, while the phase composition of Mg-4Al-4La-0.4Mn alloy contains only alpha-Mg and Al11La3. The Al11La3 phase comprises large coverage of the grain boundary region and complicated morphologies. Compared with Al11Ce3 phase, the higher volume fraction and better thermal stability of Al11La3 have resulted in better-fortified grain boundaries of the Mg-4Al-4La-0.4Mn alloy. Thus higher tensile strength and creep resistance could be obtained in Mg-4Al-4La-0.4Mn alloy in comparison with that of Mg-4Al-4Ce-0.4Mn. Results of the theoretical calculation that the stability of Al11La3 is the highest among four Al-RE intermetallic compounds supports the experimental results further.

Influence of montmorillonite on syndiotactic polymerization behavior of styrene

The influence of montmorillonite (MMT) on the syndiotactic polymerization behavior of styrene was studied. To avoid the hydrophilic surface of the MMT coming into contact with the catalyst, which could poison it, SAN was introduced between the MMT and Cp*Ti (OCH3)(3). MMT was introduced into the catalytic system as a supporter for the Ti catalyst (supported catalytic system) or just dispersed in the polymerization solvent directly (in situ polymerization system). The polymerization results showed that surface modification of MMT dramatically affected the catalytic activity as well as the syndiotacticity of the polymers. This is mainly explained by the insulator SAN preventing the formation of the inactive/little active species Si-O-Ti and other atactic active species resulting from the reaction of the -OH on the MMT layer surface with Cp*Ti(OCH3)(3).

Study on the synthesis and performance of hydrogels with ionic monomers and montmorillonite

Two series of the nanocomposite hydrogels were synthesized by in-situ solution polymerization. One pre-gel solution was obtained by directly dispersing the montmorillonite (MMT) powder into aqueous monomer solution and the other pre-gel solution was obtained by mixing monomer aqueous solution and the dispersion of MMT. The structure and performance of two series of hydrogels in dry state were studied by XRD, Raman spectroscopy, TEM and Al-27 MAS NMR. Compressing test results showed that the gel strength of the hydrogels prepared by the latter method was much higher than that by the former method. When acryloyloxyethyl trimethyl ammonium chloride (DAC) was introduced into the system, hydrogels with excellent nanostructure could be synthesized. The result of Al-27 MAS NMR suggested that the chemical environment of aluminum in MMT was changed by the introduction of DAC due to the interaction between the groups of DAC and MMT layers. Thus, the combination of copolymerizing with strong polar monomers and using the dispersion of MMT were the effective ways to obtain tranocomposite hydrogel of MMT and ionic monomers. The nanostructure of the hydrogel improved the gel strength, while the swelling ratio of the hydrogel depended on synergic effects of multifunctional groups.

CE with electrochemical detection for investigation of label-free recognition of amino acid amides by guanine-rich DNA aptamers

In this work, we report a simple and effective investigation into adaptive interactions between guanine-rich DNA aptamers and amino acid amides by CE with electrochemical (EC) detection. Argininamide (Arm) and tyrosinamide (Tym) were chosen as model molecules. On a copper electrode, Arm generated a good EC signal in 60 mM NaOH at 0.7 V (vs Ag/ AgCl), while Tym. was detected well on a platinum electrode at 1. 3 V in 20 mM phosphate of pH 7.0. Based on their EC properties, the ligands themselves were used as indicators for the adaptive interactions investigated by CE-EC, making any step of labeling and/or modification of aptamers with indicators exempted. Hydrophilic ionic liquid was used as an additive in running buffer of CE to improve the sensitivity of Arm detection, whereas the additive was not used for Tym. detection due to its negative effect. Two guanine-rich DNA aptamers were used for molecular recognition of Arm and Tym. When the aptamers were incubated with ligands, they bound the model molecules with high affinity and specificity, reflected by obvious decreases in the signals of ligands but no changes in those of the control molecules. However, the ligands were hardly affected by the control ssDNAs after incubation. The results revealed the specific recognition of Arm and Tym. by the aptamers.

Luminescent properties of RE3+-activated CaAl2B2O7 (RE = Tb, Ce) in VUV-visible region

RE3+-activated alpha- and beta-CaAl2B2O7 (RE = Tb, Ce) were synthesized with the method of high-temperature solid-state reaction. Their VUV excitation and VUV-excited emission spectra are measured and discussed in the present article. The charge transfer band of Tb3+ and Ce3+ is respectively calculated to be at 151 +/- 2 and 159 +/- 3 nm. All the samples show an activator-independent excitation peak at about 175 nm and an emission peak at 350-360 nm ascribed to the host absorption and emission band, respectively.

The luminescence of CaYBO4 : RE3+ (RE=Eu, Gd, Tb, Ce) in VUV-visible region

Phosphors CaYBO4:RE3+ (RE = Eu, Gd, Tb, Ce) were synthesized with the method of solid-state reaction at high temperature, and their vacuum ultraviolet (VUV)-visible luminescent properties in VUV-visible region were studied at 20 K. In CaYBO4, it is confirmed that there are two types of lattice sites that can be substituted by rare-earth ions. The host excitation and emission peaks of undoped CaYBO4 are very weak, which locate at about 175 and 350-360nm, respectively. The existence of Gd3+ can efficiently enhance the utilization of host absorption energy and result in a strong emission line at 314 nm. In CaYBO4, Eu3+ has typical red emission with the strongest peak at 610 nm; Tb3+ shows characteristic green emission, of which the maximum emission peak is located at 542 nm. The charge transfer band of CaYBO4:Eu3+ was observed at 228 nm; the co-doping of Gd3+ and Eu3+ can obviously sensitize the red emission of Eu3+. The fluorescent spectra of CaYBO4:Ce3+ is very weak due to photoionization; the co-addition of Ce3+-Tb3+ can obviously quench the luminescence of Tb3+.

Spectroscopic studies on charge transfer from Ce3+, to Yb3+ in KMgF3 : Ce, Yb nanocrystals

Nanocrystals of KMgF3 single-doped and codoped with Ce3+ or/and Yb3+ were synthesized separately by the microemulsion method. The X-ray diffraction(XRD) patterns were indexed to show that the KMgF, crystal system was unchanged. The fluorescent spectra of KMgF3:Ce, Yb polycrystal powders were studied and compared with those of the Ce, Yb doped KMgF3 crystals produced using the high-temperature solid phase method. The diffuse reflection spectra and infrared. emission of KMgF3:Ce, Yb were investigated. From the results, the authors could confirm that there were charge transfer processes from Ce3+ to Yb3+ in both KMgF3: Ce,Yb nanocrystals and polycrystal powders.

纳米KZnF_3∶Ce~(3+)的制备及其光谱特性

采用微乳液法合成了KZnF3∶Ce3+纳米颗粒.分析了样品的结构与形态,结果表明:所合成的样品为单相,颗粒粒度分布均匀.讨论了光谱特性,并与高温固相法合成的产物作了对比.研究发现KZnF3∶Ce3+纳米晶的发射光谱与体相多晶相比,最强谱峰位置红移约35 nm,谱带半高宽加宽约12 nm.

Microstructure and some dynamic performances of Ti0.17Zr0.08V0.34RE0.01Cr0.1Ni0.3 (RE = Ce, Dy) hydrogen storage electrode alloys

Microstructure and some dynamic performances of Ti0.17Zr0.08V0.34RE0.01Cr0.1Ni0.3 (RE=Ce, Dy) hydrogen storage electrode alloys have been investigated using XRD, FESEM-EDS, ICP-MS and EIS measurements. The alloy is composed of V-based solid solution phase with a dendritic shape and a continuous C14 Laves phase with a network shape surrounding the dendrite. Pressure-composition isotherm curves indicate that the alloy with Dy addition has a lower equilibrium hydrogen pressure and a wider plateau region. The alloy electrode with Dy addition has higher discharge capacity, while the alloy electrode with Ce addition has better activation and higher cycle stability. The alloy electrode with Ce addition has better electrochemical activity with higher exchange current density (127.5 mA g(-1)), lower charge transfer resistance (1.37 Omega) and lower apparent activation energy (30.5 kJ mol(-1)). The capacity degradation behavior for the alloy electrode is attributed to two main factors: one is the dissolutions of V and Zr element to KOH solution, and another is the larger charge transfer resistance which increases with increasing cycle number.

Pr~(3+)或Sm~(3+)掺杂YAG∶Ce的发光特性及其荧光寿命

研究了Pr3+,Sm3+掺杂对YAG∶Ce发射光谱及其荧光寿命的影响。观察到当掺杂Pr3+时,在609nm处出现Pr3+的发射峰,而掺杂Sm3+时,在616nm处呈现Sm3+的发射峰。掺杂Pr3+或Sm3+增加红光区的发射峰将有利于提高YAG∶Ce荧光粉的显色性。实验中测定了(Y0.95Sm0.01Ce0.04)3Al5O12、(Y0.95Pr0.01Ce0.04)3Al5O12、(Y0.96Ce0.04)3Al5O12的荧光寿命(τ),观察到在YAG∶Ce中掺入Pr3+或Sm3+使Ce3+的荧光寿命减小。实验结果表明,少量掺杂Pr3+或Sm3+并未引起基质的结构的变化。

An investigation on the dispersion of montmorillonite (MMT) primary particles in PP matrix

A novel path of preparing PP/o-MMT nanocomposites, which pay attention to the breaking up of MMT original agglomerates and dispersing of its primary particles, rather than the intercalation or exfoliation degree of o-MMT, was reported. The method of predispersing the o-MMT particles into a polar poly(vinyl alcohol) (PVA) matrix and then melt blending the pre-treated PVA/o-MMT hybrids with PP was studied. 3-isopropenyl-alpha,alpha-dimethylbenzene-isocyanate (TMI) was used as a modifier of PVA to improve the compatibility between PVA and PP matrix. Pre-disperse o-MMT with TMI modified PVA was proved to be an effective way to get a composite with fine o-MMT particles dispersion. But the method, which is pre-dispersing o-MMT with non modified PVA and then using TMI to modify such PVA/o-MMT hybrid, would largely reduce the reaction degree between TMI and PVA because of the relatively lower reaction temperature. Although the latter method also can obtain finer dispersion composites than that with using PP-g-MAH as compatibilizer, the relatively higher degradation degree of PP matrix in this method will limit the use of this nanocomposite.

Studies on syntheses and properties of novel CeO2/Polyimide nanocomposite films from Ce(Phen)(3) complex

A series of cerium dioxide (CeO2,)/polyimide (PI) nanocomposites were successfully prepared from Ce(Phen)(3) and polyamic acid (PAA) via the solution direct-dispersing method, followed by a step thermal imidization process. TGA and XPS studies showed that the cerium complex decomposed to form CeO2, during the thermal imidization process at 300 degrees C. SEM observation showed that the formed CeO2, as nalloparticles was well dispersed in polyimide matrix with a size of about 50-100 nm for samples with different contents of CeO2. Thermal analysis indicated that the introduction of CeO2, decreased the thermal stability of nanocomposite films due to the decomposition of Ce(Phen)(3) in the imidization process, while the glass transition temperature (T-g) increased obviously. especially nanocomposite films with high loading of CeO2 exhibited a trend of disappearance off, DMTA and static tensile measurements showed that the storage modulus of nanocomposite films increased, while the elongation at break decreased with increasing CeO2 content.

Biodegradable poly(L-lactide)/poly(epsilon-caprolactone)-modified montmorillonite nanocomposites: Preparation and characterization

New nanocomposites were prepared by melt blending poly(L-lactide) (PLLA), poly(epsilon-caprolactone) (PCL), and organically modified montmorillonite (OMMT). The obtained nanocomposites showed enhanced tensile strength, modulus and elongation at break than that of PLLA/PCL blends. The dynamic mechanical analysis showed the increasing mechanical properties with temperature dependence of nanocomposites. Wide-angle X-ray diffraction analysis and transmission electron microscopy indicated that the material formed the nanostructure. Adding OMMT improved the thermal stability and crystalline abilities of nanocomposites. The morphology was investigated by environmental scanning electron microscopy, which showed that increasing content of OMMT reduces the domain size of phase-separated particles. The specific interaction between each polymer and OMMT was characterized by the Flory-Huggins interaction parameter, B, which was determined by the equilibrium melting point depression of nanocomposites. The final values of B showed that PLLA was more compatible with OMMT than PCL.