Toxin-screening and identification of bacteria isolated from highly toxic marine gastropod Nassarius semiplicatus

Bacteria isolated from a highly toxic sample of gastropod Nassarius semiplicatus in Lianyungang, Jiangsu Province in July 2007, were studied to probe into the relationship between bacteria and toxicity of nassariid gastropod. The toxicity of the gastropod sample was 2 x 10(2) mouse unit (MU) Per gram Of tissue (wet weight). High concentration of tetrodotoxin (TTX) and its analogues (TTXs) were found in the digestive gland and muscle of the gastropod, using high performance liquid chromatography coupled with mass chromatography (LC-MS). Bacterial strains isolated from the digestive gland were cultured and screened for TTX with a competitive ELISA method. Tetrodotoxin was detected in a proportion of bacterial strains, but the toxin content was low. Partial 16S ribosomal DNA (rDNA) of the TTX-producing strains was then sequenced and compared with those published in the GenBank to tentatively identify the toxic strains. It was found that most of the toxic strains were closely affiliated with genus Vibrio, and the others were related to genus Shewanella, Marinomonas, Tenacibaculum and Aeromonas. These findings suggest that tetrodotoxin-producing bacteria might play an important role in tetrodotoxin accumulation/production in N. semiplicatus. (C) 2008 Elsevier Ltd. All rights reserved.

Hydrogen permeation and corrosion behaviour of high strength steel 35CrMo under cyclic wet-dry conditions

Hydrogen permeation behaviours of high strength steel 35CrMo under different cyclic wet-dry conditions have been investigated by using Devanathan-Stachurski's technique. Four electrolytes were used: distilled water, seawater, seawater containing 1500 ppm H2S and seawater containing 0.03 mol L-1 SO2. The corrosion weight loss of 35CrMo in the wet-dry cycles was measured simultaneously. The experimental results show that hydrogen can be detected at the surface opposite to the corroding side of the specimen during wet-dry cycles and the permeation current density during a wet-dry cycle showed a maximum during the drying process. The hydrogen permeation was obviously promoted by Cl- ions, H2S and SO2. The hydrogen permeation in the real marine atmosphere has also been investigated. There is a clear correlation between the amount of hydrogen permeated and the corrosion weight losses. Results show the importance of hydrogen permeation that merits further investigation.

Hydrogen permeation behavior and corrosion monitoring atmospheric of steel in cyclic wet-dry environment

Hydrogen permeation of 16Mn steel under a cyclic wet-dry condition was investigated by Devanathan-Stachurski's electrolytic cell with a membrane covered on the exit side by a nickel layer and the weight loss was measured for each wet-dry cycle. The results show that hydrogen permeation current change with different atmospheric environment: distilled water, seawater, and seawater containing 100 ppm H2S. The results show that seawater can induce an increase in the hydrogen permeation current due to the hydrolyzation reaction. And after the increase, equilibrium is reached due to the equilibrium of hydrolyzation reaction effect and the block of the rust layer. On the other hand, H2S contamination also can induce an increase in the maximum hydrogen permeation current due to the hydrolyzation reaction. And H2S contamination delays the time that hydrogen permeation is detected because of the formation of the FeS(1-x) film. The FeS(1-x) film can block the absorption of hydrogen onto the specimen surface. The surface potential change and the pH change of the metal surface control the hydrogen permeation current. And a clear linear correlation exists between the quantities of hydrogen permeated through the 16Mn steel and the weight loss. Based on the linear correlation, we monitored the corrosion rate by monitoring the hydrogen permeation current by a sensor outside. Good coherences were shown between results in laboratory and outside.