La_2O_3∶Sm发光粉的合成与发光性质的研究

以La2O3和Sm2O3为原料,用碳酸盐沉淀法制备了La2O3:Sm3+发光粉,并分别用XRD,SEM和发光光谱及寿命进行了表征。La2O3晶相的形成温度为800℃,其发光强度随温度升高而增强。La2O3基质中Sm3+的最佳掺杂浓度为1.5%(摩尔分数)。

YAG∶Nd中Pr,Sm,Dy杂质对其光谱的影响

采用溶胶 -凝胶法合成了YAG∶Nd ,Re(Re =Pr,Sm ,Dy)系列化合物 ,研究了它们的光谱性质 .结果表明 :Pr3 + ,Sm3 + ,Dy3 + 对YAG基质中Nd3 + 的发光具有猝灭作用 ,属于有害杂质 ,在激光晶体原料中必须除去

Preparation, patterning and luminescence properties of rare earth-doped YVO4 nanocrystalline phosphor films via sol-gel soft lithography

In this presentation, nanocrystalline YVO4:A (A=Eu3+, Dy3+, SM3+, Er3+) phosphor films and their patterning were fabricated by a Pechini sol-gel process combined with a soft lithography (micro-molding in capillaries). XRD, FT-IR, AFM and optical microscope, absorption spectra, photoluminescence (PL) spectra as well as lifetimes were used to characterize the resulting films. The results of XRD indicated that the films began to crystallize at 400 degrees C and the crystallinity increased with the increase of annealing temperatures. Transparent nonpattemed phosphor films were uniform and crack free, which mainly consisted of grains with an average size of 90nm. Patterned crystalline phosphor film bands with different widths (5-30 mu m) were obtained. The doped rare earth ions (A) showed their characteristic emission in crystalline YVO4 phosphor films due to an efficient energy transfer from vanadate groups to them. The Sm3+ and Er3+ ions also showed upconversion luminescence in YVO4 film host. The optimum concentration for Eu3+ was determined to be 7 mol% and those for Dy3+, Sm3+, Er3+ were 2 Mol% of Y3+ in YVO4 films, respectively.

Novel trichromatic phosphor codoped with two rare earth ions in a single matrix

The luminescence properties of CaBPO5: Eu, Tb phosphor and the sensitization of Ce3+ were investigated. The CaBPO5: Eu, Tb phosphors were synthesized in the ambient air and the emission spectra of Eu3+, Tb3+ and Eu2+ were Observed in the phosphor. The result shows that there is electron transfer between conjugate rare earth ions. Sensitization of Ce3+ can improve the intensity of emission of Tb3+ and Eu2+. A novel trichromatic lamp phosphor codoped with Eu3+-Tb3+ in matrix CaBPO5 is then predicted.

TG-DTA properties of new nonlinear optical materials: K(2)Ln(NO3)(5)center dot 2H(2)O (Ln = La, Ce, Pr, Nd, Sm)

Single crystals of K(2)Ln(NO3)(5). 2H(2)O (KLnN) (Ln = La, Ce, Pr, Nd, Sm) were grown from aqueous solution. The thermogravimetric analysis and differential thermal analysis curves of KLnN demonstrate that the processes of dehydration, melting, irreversible phase transformation and decomposition of NO3- take place in sequence in the heating processes (except KCN). There are three stages in the decomposition of NO3- in KLnN (Ln = La, Nd, Sm) while two in KLnN (Ln = Ce, Pr). K(2)Ln(NO3)(5) is formed at about 225 degrees C by the reaction of KNO3 and Ln(NO3)(3). nH(2)O (Ln = La, Ce, Pr, Nd). (C) 2000 Elsevier Science Ltd. All rights reserved.

Preparation of borates doped with divalent rare earth ions (RE2+) in air and spectroscopy of divalent rare earth ions (RE2+ = Sm, Eu, Tm, Yb)

The spectroscopic feature of divalent Sm2+, Eu2+, Tm2+ and Yb2+ is discussed in this paper. Especially the spectroscopic properties of some berates containing tetrahedral BO4 group such as SrB4O7, SrB6O10 and BaB8O13 doped with these divalent ions are reported. When the divalent alkaline earth ion in these berates is replaced partially by the above trivalent rare earth ion, the charge carried in the produced defects can be used as reductant to reduce the doped rare earth ion into divalent state at high temperature even in air. Therefore, a convenient and safe method is provided to prepared phosphors doped with these divalent rare earths.

Theoretical studies of nonlinear optical properties of compounds K(4)Ln(2)(CO3)(3)F-4 (Ln=Pr, Nd, Sm, Eu, Gd)

K(4)Ln(2)(CO3)(3)F-4 (Ln=Pr, Nd, Sm, Eu, Gd) is a special type of frequency doubling compound, whose crystal structure exhibits a scarcity of fluorine ions. This leads to two different coordination polyhedrons in the general position of K(2) atoms: [K(2)O6F(1)(2)F(2)] and [K(21)O6F(1)(2)] in a 2/1 ratio. The chemical bonding structures of all constituent atoms of the compound K4Gd2(CO3)(3)F-4 (KGCOF) are comprehensively studied; moreover, the relationship between the chemical bonding structure and the nonlinear optical (NLO) properties is investigated from the chemical bond viewpoint. The theoretical prediction of the NLO tensor coefficient d(11) of KGCOF is in agreement with experimental observation. Theoretical analyses show that the nonlinearity of this crystal type mainly originates from K-O bonds. In addition, the correlation between the NLO tensor d(11) and the refractive index n(0) of KGCOF is discussed. (C) 2000 American Institute of Physics. [S0021-8979(00)07506-X].

在空气下制备掺二价稀土的硼酸盐及二价稀土离子(RE~(2+)=Sm,Eu,Tm,Yb)的光谱特征

本文讨论了Sm2 + 、Eu2 + 、Tm2 + 、Yb2 + 等二价稀土离子的光谱特征 ,特别是在一些含四面体硼酸根的硼酸盐如SrB4 O7、SrB6 O10 和BaB8O13中它们的光谱性质。当以三价稀土离子取代化合物中的二价碱土离子时 ,利用不等价取代而产生的缺陷所带的电荷 ,可在高温的空气下使上述的稀土离子还原成二价 ,不需加入化学还原剂 ,从而提出了一个简便、安全的制备含二价稀土离子发光材料的方法

Synthesis and characterization of polynuclear half-sandwich lanthanoid complexes [Na(THF)(6)](2)[(Cp6Sm6Se13)-Sm-t] and [Li(LHF4](2)[Cp6Nd6Se13]

The half-sandwich tert-butyl cyclopentadienyl lanthanoid complexes {[Cp ' Ln(THF)](2)(mu (2)-Cl)(2)(mu (3)-Cl)(3)Na(THF)}(n) [Cp ' = eta (5)-' BuC5H4; Ln = Nd (1a), Sm (1b), Gd (1c), Yb (1d)] are prepared by the reaction of anhydrous lanthanoid trichloride, LnCl(3), with NaCp ' in THF solution. Complex 1b reacts with Na2Se5 to give hexanuclear samarium polyselenide complexes [Na(THF)(6)](2)[Cp-6' SM6(mu (6)-Se)(mu -Se-2)(6)] (2). An analogous cyclopentadienyl neodymium polyselenide complex [Li(THF)(4)](2)[Cp6Nd6(mu (6)-Se)(mu -Se-2)(6)] (3) is synthesized by the reaction of [CpNdCl2. 2LiCl . 5THF] with Na2Se5 in THF solution. The molecular structures of 1a and 2 were determined by X-ray crystal structure analysis. Complex 2 contains an interstitial selenium atom which is coordinated with six samarium atoms. (C) 2001 Elsevier Science BN. All rights reserved.

Luminescent centers of EU2+ in BaMgAl10O17 phosphor

Two kinds of luminescent centers an observed in BaMgAl10O17:Eu2+ phosphor. Influence of flux on luminescence of Eu2+ in the phosphor is discussed in detail. There exists Eu2+ (F-) center (a luminescent center with 277 nm excitation band and 386 nm emission band) due to the substitution of F- ions for O2- ions, Effective energy transfer from Eu2+ (F-) to Eu2+ (O2-) (a luminescent center with 334 nm excitation band and 450 nm emission band) is observed. The quenching concentration of Eu2+ in BaMgAl10O17 is raised by 0.20 mole per mole host due to forming of new luminescent center Eu2+ (F-). (C) 2001 Elsevier Science Ltd. All rights reserved.

Synthesis and crystal structure of (1,3-(Bu2C5H3)-Bu-t)(2)Sm(mu-Cl)(2)Li(THF)(2)

Anhydrous SmCl3 reacts with two equal of Li(1-3-(Bu2C5H3)-Bu-t) to give a complex (1,3-(Bu2C5H3)-Bu-t)(2) Sm(mu -Cl)(2)Li(THF)(2) (C34H58Cl2LiO2Sm, M-r = 726.99), monoclinic, space group P2(1)/n, a = 10.615(2), b = 21.037(4), c = 17.166(3) Angstrom, beta = 93.60(3)degrees, V = 3825.7 (13) Angstrom (3), Z = 4, D-c = 1.262 Mg/m(3), mu = 1.699 mm(-1) and F(000) = 1508, final R = 0.0387 and wR = 0.0741 for 5320 observed[I greater than or equal to2 sigma (I)] reflections. The average Sm - C distance is 2.73 Angstrom. Sm - Cl1 and Sm - Cl2 distances are 2.719 (2) and 2. 697 (2) Angstrom, respectively. Two 1, 3-(Bu2C5H3)-Bu-t-ring centroids and two mu (2)-bridging chloride atoms around Sm atom form a distorted tetrahedron.

Luminescence of RE2+ (RE = Sm, Yb) in barium octoborate

The reduction process from trivalent to divalent state for Sm3+ and Yb3+ ions in barium berates (BaB8O13) prepared in air was observed. The luminescence properties of these divalent rare-earth ions were studied. Yb2+ shows an f-d broad emission band, due to the 4f(14) --> 4f(13)5d transition, while the Sm2+ ion shows an f --> f transition. From the spectra of Yb2+, and using the D-5(0) --> F-7(0) transition of Sm2+ as a structural probe, two crystallographic sites were found to be available for the cations in the host. Vibronic transitions of Sm2+ were observed at low temperature. BaB8O13 was found to be a good host for reducing the trivalent rare-earth ions to divalent state and to exhibit interesting spectroscopic properties,