Synthesis, structure and ionic conductivity of La2/3-xLi3xMoO4

A series of compounds, La2/3 - xLi3xMoO4, were first prepared. Their structures are tetragonal scheelites with the cationic defects. The cell parameters a, c and values of c/a decrease with the increasing of the substitution amount (3x) of lithium ion. Cationic vacancies are getting more as Li+ concentration is lower. The diffusion of lithium ion is predominant. The concentration of charge carriers increases with increasing the substitution amount (3x) of lithium ion, meanwhile, the concentration of cationic vacancies decreases. The conductivity approaches the best when the substitution amount (3x) of lithium ion is about 0.3. The conductivity of La0.567Li0.3MoO4 is 6.5 x 10(-6) S . cm(-1) at room temperature.

Unidirectional current flow of reversible redox couples on a MoO3 film-modified microelectrode

In this paper, we have investigated the reactivity of the molybdenum oxide film toward some standard redox systems (e.g., ferrocene (Fc) and its derivatives) and observed a few interesting phenomena. The results demonstrate that the electrochemical behaviour of Fc and its derivatives at the oxide-modified carbon fiber (CF) microelectrode differs from that at a bare CF microelectrode, The conductivity of the molybdenum oxide film is seriously affected by the range and the direction of the potential scan, which influences the electrochemical behaviour of these redox systems at the film electrode. If the cycling potential is more positive than the reduction potential of the molybdenum oxide film, the reduction and oxidation peak currents of Fc and its derivatives could not be observed. The result indicates that the molybdenum oxide film on a microelectrode surface cannot transfer electrons between the surface of the electrode and Fc or its derivatives due to the existence of a high resistance between the interface in these potential ranges. On the other hand, if the lower limit of the scan potential was extended to a potential more negative than the reduction peak potential of the film, the oxidation peak of Fc or its derivatives appeared at about the potential relative to E-0 of Fc or its derivatives on the bare electrode, and the peak current is proportional to the concentration of these couples in the electrolyte. To our surprise, the peak height on the modified electrode is much larger than that on the bare CF microelectrode under the same conditions in the range of low concentration of these couples, and the oxidation peak potential of these couples is more negative than that on the bare CF microelectrode. On the basis of the experimental observation, we propose that these redox couples may undergo an interaction with the reduction state of the molybdenum oxide film. The new phenomena that we observed have been explained by using this interaction. (C) 1997 Elsevier Science S.A.

Residual properties of an injection-molded poly(phenylene ether ketone) carbon composite during flexural fatigue

The present work investigates the effects of cyclic fatigue loading on the residual properties of an injection-molded composite, carbon-fiber-reinforced poly(phenylene ether ketone) (CF/PEK-C), and damage development in this material under fatigue lending. Test specimens, which had been conditioned to various preselected fatigue damage stages, were measured for their residual properties. The results indicated that cyclic fatigue loading alters the constitutive behavior of the injection-molded composite, especially in the non-linear portion of the stress/strain curve. The residual strength decreases with increase in the number of fatigue cycles as a consequence of the accumulation of fatigue damage, which is dominated by the growth of microcracks. While the residual modulus increases slightly with cyclic fatigue loading, this is probably due to the oriented hardening resulting from creep deformation which is induced during cyclic loading. (C) 1997 Elsevier Science Limited.

Synthesis of lanthanide-alkylaluminium bimetallic complexes and studies on their catalytic activities for polymerization of some polar monomers

Three new lanthanide (Ln)-alkylaluminium (Al) bimetallic complexes with the formula [(mu-CF3CO2)(2)Ln(mu-CF3CHO2)AIR(2) . 2THF](2) (Ln = Nd, Y, R=i-C4H9 (i-Bu); Ln=Eu, R=C2H5(Et); THF=tetrahydrofuran) were synthesized by the reaction of Ln(CF,CO,), (Ln=Nd, Y) with HAI (i-Bu)(2) and of Eu(CF3CO2)(3) with AlEt(3), respectively. Their crystal structures were determined by X-ray diffraction at 233 K. [(mu-CF3CO2)(2)Nd (mu-CF3CHO2)Al(i-Bu)(2) . 2THF](2) (Nd-Al) and [(mu-CF3CO2)(2)Y(mu-CF3CHO2)Al(i-Bu)(2) . 2THF](2) (Y-Al) are isomorphous and crystallize in space group with a=12.441(3) Angstrom [12.347(5) Angstrom for Y-Al], b=12.832(3) Angstrom [12.832(4) Angstrom], c=11.334(3) Angstrom [11.292(8) Angstrom], alpha=104.93 (2)degrees [104.45(4)degrees], beta=98.47(2)degrees [98.81(4)degrees], gamma=64.60(2)degrees [64.30(3)degrees], R=0.519 [0.113], R(w)=0.0532 [0.110], Z=1 and [(mu-CF3CO2)(2)Eu(CF3CHO2)AlEt(2) . 2THF](2)(Eu-Al) in space group P2(1)/n with a=11.913(6) Angstrom, b=14.051(9) Angstrom, c=17.920(9) Angstrom, alpha=101.88(11)degrees, beta=gamma=90 degrees, R=0.0509, R(w)=0.0471 and Z=2. The six CF3CO2- (including CF3CHO2-) of each complex, among which pairs are equivalent, coordinated to Ln and Al in three patterns: (A) the two oxygen atoms in one of the three CF3CO2- type coordinated to two different Ln; (B) the two oxygen atoms in the second of CF3CO2- type coordinated to Ln and Al, respectively; (C) one of the two oxygen atoms in the third CF3CO2- type bidentately coordinated to two Ln and another oxygen coordinated to Al and one of the two Ln, respectively. Unlike types A and B, in type C the carboxyl carbon with a hydrogen atom bonded to it was found to appear as an sp(3)-hybridized configuration rather than an sp(2)-one. 1D and 2D NMR results further confirmed the existence of such a disproportionated CF3CHO2- ligand. Methyl methacrylate (MMA) and epichlorohydrin (ECH) could be polymerized by Y-Al or Eu-Al as a single-component catalyst and highly syndiotactic poly(MMA) was obtained. THF could also be polymerized by Y-Al in the presence of a small amount of ECH.

Electrochemical preparation of microelectrodes modified with non-stoichiometric mixed-valent molybdenum oxides

A compact non-stoichiometric molybdenum (VI, V) oxide of blue film was grown on carbon fiber (CF) microelectrode surface be cycling the potential between + 0.2V and - 0.70V in a freshly prepared Na2MoO4 solution containing 5 x 10(-3) mol/L H2SO4. The quantity-of the oxide is controlled by the charge passing the electrode. The electrochemical pretreatment of CF microelectrode not only mises the deposition velocity of molybdenum oxide on CF surface, but also improves greatly the cyclic voltammetric behavior of the molybdenum oxide film prior to the electrodeposition. The cathodic processes are believed to yield the hydrogen molybdenum oxide bronzes HxMoO3(0 < x < 2), or substoichiometric lower molybdenum oxides with the formula MoO3-y(0 < y < 1). The anodic response results from the reversible oxidation of molybdenum bronze/Mo(V) centers [or perhaps Mo(IV) in more reduced coatings], to Mo(VI). Further information was gained about the chemical composition and valent state of Mo from XPS and SEM.