Influence of exotic Mn on magnetic properties of YCo5.0-xMnxGa7.0 (0.05 <= x <= 3.0)

The YCo5.0-xMnxGa7.0 compounds crystallize with the ScFe6Ga6-type structure. The lattice of YCo5.0-xMnxGa7.0 expands with the increase of the Mn content for 0.05 <= x <= 2.5, but the lattice of YCo2.0Mn3.0Ga7.0 shrinks compared with YCo2.5Mn2.5Ga7.0. The shrinkage of the lattice is attributed to the magnetostriction of YCo2.0Mn3.0Ga7.0. The substitution of Mn for Co forms magnetic clusters in the antiferromagnetic matrix. The magnetic frustration results in the spin-glass-like behavior for 0.8 <= x <= 1.5 and the difference between zero-field-cooling (ZFC) and field-cooling (FC) magnetizations for x = 2.0, 2.5, and 3.0. A stable long-range magnetic ordering appears among the Mn-centered magnetic clusters with the ordering temperature 110 K for x = 2.0. The hump in the thermomagnetization of YCo3.0Mn2.0Ga7.0 can be attributed to the competitive effects between the thermal fluctuation and the enhanced magnetic interaction. Both the hump and the bifurcation between the ZFC and the FC magnetizations of YCo3.0Mn2.0Ga7.0 occur at lower temperatures as the applied field increases. On the two-step magnetization curve of YCo3.0Mn2.0Ga7.0, the inflection point at 4000 Oe is due to the coercive field, and the magnetic moments in the clusters are tilted to the applied field above 4000 Oe. The magnetic ordering temperature is further increased to 210 K for x = 2.5 and to 282 K for x = 3.0. The spontaneous magnetization of YCo2.0Mn3.0Ga7.0 is 0.575 mu B/f.u. at 5 K with a canted magnetic structure.

Fe-57 Mossbauer spectroscopic and magnetic studies of R3Fe29-xVx (R = Y, Ce, Nd, Sm, Gd, Tb, and Dy)

Mossbauer spectra for Fe atoms in the series of R3Fe29-xVx (R = Y, Ce, Nd, Sm, Gd, Tb, and Dy) compounds were collected at 4.2 K. The ratio of 14.5 T/mu(B) between the average hyperfine field B-hf and the average Fe magnetic moment mu(Fe)(MS), obtained from our data, in Y3Fe29-xVx is in agreement with that deduced from the RxTy alloys by Gubbens et al. The average Fe magnetic moments mu(Fe)(MS) in these compounds at 4.2 K, deduced from our Mossbauer spectroscopic studies, are in accord with the results of magnetization measurement. The average hyperfine field of the Fe sites for R3Fe29-xVx at 4.2 K increases with increasing values of the rare earth effective spin (g(J) - 1) J, which indicates that there exists a transferred spin polarization induced by the neighboring rare earth atom.

ELECTRONIC AND MAGNETIC-STRUCTURE OF THE TERNARY COMPOUND ND2FE17N

The electronic and the magnetic structure of the Nd2Fe17N1 phase in the family of Nd-Fe-N ternary compounds have been calculated using the first-principles, spin-polarized orthogonalized linear-combination-of-atomic-orbitals method. Results are presented in the form of site-decomposed and spin-projected partial density of states. The occupation sites of the three N atoms are determined by an average radial distribution of all possible N site configurations. Both cases of N occupying the 3b and the 18g sites are studied. The results indicate that the 6c Fe sites have the maximum and the 18h Fe sites have the minimum local moments. This is in good agreement with experiment. It is concluded that the influence on the local moment due to lattice expansion is less important compared to that due to interatomic interaction between the N atom and its neighbors. The results also show the important role of N atoms in raising the Curie temperature of this compound.

CALCULATED ELECTRONIC AND MAGNETIC-STRUCTURES OF THE NEW TERNARY RARE-EARTH IRON NITRIDE ND2FE17N3

The electronic and magnetic structures of Nd2Fe17 and Nd2Fe17N3 have been calculated using the first-principle, spin-polarized orthogonalized linear combination of atomic orbitals method. Comparative studies of the two materials reveal important effects of the nitrogen atoms (at 9e site) on the electronic and magnetic structures. Results are presented for the total density of states, site-projected partial density of states and the spin magnetic moments on four nonequivalent Fe sites. The highest magnetic moments are found to be located on the 6c site for Nd2Fe17 and on the 9d site for Nd2Fe17N3, in agreement with the neutron and Mossbauer experiments. The variation trends of the magnetic moments on different Fe sites are discussed in terms of the separation between Fe and N atoms. Compared with Nd2Fe17, an increase in the exchange splitting of the Fe d band is found in Nd2Fe17N3, which accounts for its higher Curie temperature as observed in experiments. The calculated results show that the nitrogen atoms are charge acceptors in these compounds.

Fe-57 Mossbauer spectroscopic and magnetic studies of R3Fe29-xVx (R = Y, Ce, Nd, Sm, Gd, Tb, and Dy)

Mossbauer spectra for Fe atoms in the series of R3Fe29-xVx (R = Y, Ce, Nd, Sm, Gd, Tb, and Dy) compounds were collected at 4.2 K. The ratio of 14.5 T/mu(B) between the average hyperfine field B-hf and the average Fe magnetic moment mu(Fe)(MS), obtained from our data, in Y3Fe29-xVx is in agreement with that deduced from the RxTy alloys by Gubbens et al. The average Fe magnetic moments mu(Fe)(MS) in these compounds at 4.2 K, deduced from our Mossbauer spectroscopic studies, are in accord with the results of magnetization measurement. The average hyperfine field of the Fe sites for R3Fe29-xVx at 4.2 K increases with increasing values of the rare earth effective spin (g(J) - 1) J, which indicates that there exists a transferred spin polarization induced by the neighboring rare earth atom.

Baryon magnetic moment and beta decay ratio in colored quark cluster model

Baryon magnetic moments of p, n, Sigma(+), Sigma(-), Xi(0), Xi(-) and the beta decay ratios (G(A)/G(V)) of n -> p, Sigma(-) -> n and Xi(0) -> Sigma(+) are calculated in a colored quark cluster model. With SU(3) breaking, the model gives a good fit to the experimental values of those baryon magnetic moments and the beta decay ratios. Our results show that the orbital motion has a significant contribution to the spin and magnetic moments of those baryons and the strange component. in nucleon is small.

Structure, electric and magnetic properties of new compounds CdYMWO7 (M = Cr and Mn)

Two new compounds with the formula of CdYMWO7 (M = Cr, Mn) were prepared by solid state reaction. They crystallized with orthorhombic structure with the cell parameters of a = 11.7200 Angstrom, b = 7.1779 Angstrom, c = 6.9805 Angstrom (CdYCrWO7), and a = 11.7960 Angstrom, b = 6.1737 Angstrom, c = 7.6530 Angstrom (CdYMnWO7). These compounds are insulators with high resistivities at room temperature. The temperature dependence of the magnetic susceptibility of CdYMWO7 (M = Cr and Mn) show Curie-Weiss Law's behaviors from 80 to 300 K. The magnetic moments at room temperature fit very well with those corresponding to Cr3+ and Mn3+ ions. This suggests that both Cr and Mn ions exist in + 3 oxidation state in CdYMWO7 compounds. (C) 1998 Elsevier Science Ltd. All rights reserved.

Microstructure and Magnetic Properties of Nd60Al10Fe20Co10 Glass-forming Alloy

The microstructural variations of the Nd60Al10Fe20CO10 melt-spun ribbons and the as-cast rod were studied by high resolution transmission electron microscopy (HRTEM), x-ray diffraction (XRD) and differential scanning calorimetry. Nano-clusters in glassy m

Domain structure of a Nd60Al10Fe20Co10 bulk metallic glass

Magnetic domain structure of Nd60Al10Fe20Co10 bulk metallic glass (BMG) has been studied by using magnetic-force microscopy. In the magnetic-force images it is shown that the exchange-interaction-type magnetic domains with a period of about 360 nm do exist in the BMG, which is believed to be associated with the appearance of hard-magnetic properties in this system. The existence of the large-scale domains demonstrates that the magnetic moments of a great deal of short-scale ordered atomic clusters in the BMG have been aligned by exchange coupling. Annealing at 715 K leads to partial crystallization of the BMG. However, the exchange coupling is stronger in the annealed sample, which is considered to arise from the increase of transition-metal concentration in the amorphous phase due to the precipitation of Nd crystalline phase.

Phase Evolution and its Effect on Magnetic Properties of Nd60Al10Fe20Co10 Bulk Metallic Glass

The thermal stability of nanocrystalline clusters, the phase evolution, and their effects on magnetic Propertieswere studied for as-cast Nd60Al10Fe20Co10 alloy using differential scanning calorimetry curves, x-ray diffraction patterns, scanning electron microscopy, and high-resolution transition electron microscopy. Thermomagnetic curves and hysteresis loops of the bulk metallic glass were measured during the annealing process. The high thermostability of the hardmagnetic properties of the samples observed is attributed to the stability of the nanocrystalline clusters upon annealing, while the slight enhancement in the magnetization is due to the precipitation of some Nd-rich metastable phases. The mechanism of thermostability of the nanocrystalline clusters and the formation of the metastable phases are discussed.

Magnetic Properties of Mn-Implanted n-Type Ge

Mn+ ions were implanted into n-type Ge(111) single crystal at room temperature at an energy of 100 keV with a dose of 3 x 1016 cm-2. Subsequent annealing was performed on the samples at 400 °C and 600 °C in a flowing nitrogen atmosphere. The magnetic properties of the samples have been investigated by alternating gradient magnetometer at room temperature. The compositional properties of the annealed samples were studied by Auger electron spectroscopy and the structural properties were analyzed by X-ray diffraction measurements. Magnetization measurements reveal room-temperature ferromagnetism for the annealed samples. The magnetic analysis supported by compositional and structural properties indicates that forming the diluted magnetic semiconductor (DMS) MnxGe1-x after annealing may account for the ferromagnetic behavior in the annealed samples.

Structural and magnetic properties of insulating Zn1-xCoxO thin films

Cobalt-doped ZnO (Zn1-xCoxO) thin films were fabricated by reactive magnetron cosputtering. The processing conditions were carefully designed to avoid the occurrence of Co precipitations. The films are c-axis oriented, and the solubility limit of Co in ZnO is less than 17%, determined by x-ray diffraction. X-ray photoemission spectroscopy measurements show Co ions have a chemical valance of 2+. In this paper, hysteresis loops were clearly observed for Zn1-xCoxO films at room temperature. The coercive field, as well as saturation magnetization per Co atom, decreases with increasing Co content, within the range of 0.07of Physics.

Magnetic properties of sintered sm2fe17ny magnets

Sintered magnets of Sm2Fe17Ny nitrides, with a density of 6.0-7.4 g/cm3, have been prepared by using an explosion technique. Both crystalline structure and the magnetic properties of Sm2Fe17Ny nitrides were retained in the process. The sintered magnet had a remanence B(r)=0.83 T, an intrinsic coercivity mu(0i)H(c)=0.57 T and an energy product (BH)max=88 kJ/m3. The temperature dependence of coercivity and remanence were also measured. The temperature coefficients alpha of remanence and beta of coercivity are -0.076%/degrees-C and -0.51%/degrees-C, respectively.

Synthesis and magnetic properties of Ni-doped zinc oxide powders

Polycrystalline Zn1-xNixO diluted magnetic semiconductors have been successfully synthesized by an auto-combustion method. X-ray diffraction measurements indicated that the 5 at% Ni-cloped ZnO had the pure wurtzite structure. Refinements of cell parameters from powder diffraction data revealed that the cell parameters of Zn0.95Ni0.05O were a little bit larger than ZnO. Transmission electron microscopy observation showed that the as-synthesized powders were of the size similar to 60 nm. Magnetic investigations showed that the nanocystalline Zn0.95Ni0.05O possessed room temperature ferromagnetisin with the saturation magnetic moment of 0.1 emu/g (0.29 mu(B)/Ni2+). (c) 2005 Elsevier B.V. All rights reserved.

Structure and magnetic properties of CoNiP nanowire arrays embedded in AAO template

Ternary CoNiP nanowire (NW) arrays have been synthesized by electrochemical deposition inside the nanochannels of anodic aluminum oxide (AAO) template. The CoNiP NWs deposited at room temperature present soft magnetic properties, with both parallel and perpendicular coercivities less than 500 Oe. In contrast, as the electrolyte temperature (T-elc) increases from 323 to 343 K, the NWs exhibit hard magnetic properties with coercivities in the range of 1000-2500 Oe. This dramatic increase in coercivities can be attributed to the domain wall pinning that is related to the formation of Ni and Co nanocrystallites and the increase of P content. The parallel coercivity (i.e. the applied field perpendicular to the membrane surface) maximum as high as 2500 Oe with squareness ratio up to 0.8 is achieved at the electrolyte temperature of 328 K. It has been demonstrated that the parallel coercivity of CoNiP NWs can be tuned in a wide range of 200-2500 Oe by controlling the electrolyte temperature, providing an easy way to control magnetic properties and thereby for their integration with magnetic-micro-electromechanical systems (MEMS). (C) 2008 Elsevier B.V. All rights reserved.