Wear of hardfacing white cast irons by solid particle erosion

The response of three commercial weld-hardfacing alloys to erosive wear has been studied. These were high chromium white cast irons, deposited by an open-arc welding process, widely used in the mineral processing and steelmaking industries for wear protection. Erosion tests were carried out with quartz sand, silicon carbide grit and blast furnace sinter of two different sizes, at a velocity of 40 m s-1 and at impact angles in the range 20° to 90°. A monolithic white cast iron and mild steel were also tested for comparison. Little differences were found in the wear rates when silica sand or silicon carbide grit was used as the erodent. Significant differences were found, however, in the rankings of the materials. Susceptibility to fracture of the carbide particles in the white cast irons played an important role in the behaviour of the white cast irons. Sinter particles were unable to cause gross fracture of the carbides and so those materials with a high volume fraction of carbides showed the greatest resistance to erosive wear. Silica and silicon carbide were capable of causing fracture of the primary carbides. Concentration of plastic strain in the matrix then led to a high wear rate for the matrix. At normal impact with silica or silicon carbide erodents mild steel showed a greater resistance to erosive wear than these alloys. © 1995.

Friction and material transfer in micro-scale sliding contact between aluminium alloy and steel

A ball-on-flat reciprocating micro-tribometer has been used to measure the friction coefficient between aluminium alloy strip and a steel ball. A relatively small ball and correspondingly low contact load is used to give a contact width of the order of 100μm, closer to asperity contact widths than generally found for this type of test. The effects of load, initial strip surface roughness, lubricants and boundary additives are investigated. It is found that the friction coefficient is significantly reduced by the addition of a lubricant. Observations of the wear tracks and ball surface show that the material transfer from aluminium to the ball is reduced in the presence of the lubricant. The initial friction coefficient is further reduced by the addition of a boundary additive, but the friction coefficient after 8 cycles is unchanged. Copyright © 2004 by Springer Science+Business Media, Inc.

Solid particle erosion of boronized steels

Boronizing is a thermochemical diffusion-based process for producing iron boride layers in the surface of steel components. The boride layer is wear resistant and is very hard. Large residual stresses are found to exist in the surface layers, which are a function of substrate steel composition and heat treatment. By slow cooling from the boronizing temperature (900°C), a large compressive stress is developed in the boride layer. Hardening the steel by rapid cooling, either directly from the boronizing treatment or after subsequent austenitizing, develops tension in the coating which causes it to fracture. Tempering of the martensite produces compression in the coating, closing but not welding the cracks. The results of solid particle erosion experiments using silicon carbide, quartz, and glass bead erodents on boronized steels are presented.